A kind of synthetic method of polyimide

A technology of polyimide and synthesis method, applied in the field of synthesis of polyimide, can solve problems such as poor transparency of polyimide, and achieve the effect of improving transparency and high transparency

Active Publication Date: 2018-02-13
HUBEI DINGLONG CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problem of poor transparency of polyimide in the prior art, the embodiment of the present invention provides a synthesis method of polyimide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of synthetic method of polyimide
  • A kind of synthetic method of polyimide
  • A kind of synthetic method of polyimide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Introduce nitrogen into a 250mL three-neck flask equipped with a mechanical stirring device, first add 2.9112g (0.0091mol) 2,2'-bis(trifluoromethyl)diaminobiphenyl and 0.2422g (0.0009mol) 1,1' - Mixed diamines of bis(4-aminophenyl)cyclohexane, followed by 62.56 g of ionic liquid 1,3-bis(2-methoxy-2-oxoethyl)imidazole tetrafluoroborate, 1 , The structural formula of 3-bis(2-methoxy-2-oxyethyl)imidazolium tetrafluoroborate is:

[0035]

[0036] Turn on the mechanical stirring and heat to make it dissolve. At this time, the temperature of the mixed solution in the three-neck flask is not higher than 50°C. After the mixed diamine is completely dissolved, add 3.1021g (0.01mol) 3,3',4,4'-diphenyl ether tetracarboxylic dianhydride into the three-necked flask, stir for 10min, squeeze the nitrogen bag to make the three-necked flask Remove as much air as possible. The mixture in the three-necked flask was slowly heated up to 180° C., stirred at a constant temperature of 180°...

Embodiment 2

[0041] Argon was passed into a 250mL three-neck flask equipped with a mechanical stirring device, and 1.6012g (0.005mol) of 2,2'-bis(trifluoromethyl)diaminobiphenyl and 1.3319g (0.005mol) of 1,1 The mixed diamine of '-bis(4-aminophenyl) cyclohexane, then add 14.75g ionic liquid 1,3-bis(2-methoxy-2-oxoethyl) imidazole tetrafluoroborate, And turn on the mechanical stirring, heat to make it dissolve, and the temperature of the mixed solution in the three-necked flask is not higher than 50°C at this time. After the mixed diamine is completely dissolved, add 4.4424g (0.01mol) 4,4'-hexafluoroisopropyl phthalic anhydride to the three-necked flask, and after stirring for 10min, squeeze the argon bag to make the air in the three-necked flask Eliminate as much as possible. The mixed solution in the three-neck flask was slowly heated up to 150° C., stirred at a constant temperature of 150° C. for 10 h, and then cooled down to room temperature naturally to obtain a pale yellow polyimide ...

Embodiment 3

[0045] Nitrogen was passed into a 250mL three-neck flask equipped with a mechanical stirring device, and 2.6579g (0.0083mol) of 2,2'-bis(trifluoromethyl)diaminobiphenyl and 0.4528g (0.0017mol) of 1,1' - Mixed diamines of bis(4-aminophenyl)cyclohexane, and then add 17.21g of ionic liquid chloride 1,3-bis(2-methoxy-2-oxyethyl)imidazole chloride, chloride 1, The structural formula of 3-bis(2-methoxyl-2-oxyethyl)imidazole is:

[0046]

[0047] Turn on the mechanical stirring and heat to make it dissolve. At this time, the temperature of the mixed solution in the three-neck flask is not higher than 50°C. After the mixed diamine is completely dissolved, add 1.5511g (0.005mol) of 3,3',4,4'-diphenyl ether tetracarboxylic dianhydride and 2.2212g (0.005mol) of 4,4'-hexafluoroiso Propyl phthalic anhydride, after stirring for 10 minutes, squeeze the nitrogen bag to remove the air in the system as much as possible. The mixed solution in the three-necked flask was slowly heated up to 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a synthesis method of polyimide, which belongs to the field of polymer materials. The method comprises: polymerizing dianhydride and diamine in an ionic liquid; mixing the polyimide prepolymer solution with methanol or deionized water to obtain a precipitate, and filtering and drying the precipitate to obtain Polyimide prepolymer powder; the polyimide prepolymer powder is dissolved in a polar solution to obtain a polyimide prepolymer glue; the polyimide prepolymer glue is It was applied on a flat plate to solidify, cooled to room temperature, and peeled off to obtain a film-like polyimide. The embodiment of the present invention provides a method for synthesizing polyimide. The ionic liquid provided by the embodiment of the present invention can enable the polyimide prepolymer generated to undergo a complete imidization reaction at low temperature, so that the preparation The polyimide is colorless and has high transparency.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a synthesis method of polyimide. Background technique [0002] Polyimide is a high-performance polymer material with excellent chemical stability, thermal stability and high mechanical strength, and has been widely used in aerospace, microelectronics and chemical industries. [0003] The existing conventional method of synthesizing polyimide is to form soluble polyimide by dianhydride and diamine in aprotic strong polar solvent at high temperature, wherein, aprotic strong polar solvent can be N, N-Dimethylformamide, N,N-Dimethylacetamide or N-methylpyrrolidone. [0004] In the process of realizing the present invention, the inventor finds that there are at least the following problems in the prior art: [0005] The color of the polyimide synthesized by the above method is generally light yellow or brownish yellow, which makes the polyimide poor in transparency, thereby limiting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G73/10C08J5/18
Inventor 尤庆亮刘继延陈妤红张玲于洁阮敏胡思泉付华刘学清谭时友曹元成徐亨陈灵瑄
Owner HUBEI DINGLONG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com