A kind of high-strength polypropylene material and preparation method thereof

A polypropylene material, high-strength technology, applied in the field of polymer material processing, can solve the problems of difficulty in meeting the performance requirements of polypropylene materials such as transparency and safety, and achieve good industrial application prospects, easy implementation, and significant enhancement effects. Effect

Active Publication Date: 2018-06-29
SICHUAN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of the second component is difficult to meet the performance requirements of polypropylene materials such as transparency and safety in food packaging and biomedical fields.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength polypropylene material and preparation method thereof
  • A kind of high-strength polypropylene material and preparation method thereof
  • A kind of high-strength polypropylene material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Polypropylene (1005, Formosa Plastics, Taiwan) was selected as the experimental material, and its melt index was 0.5g / 10min (210°C, 2.16Kg). Vacuum dry in an oven at 80°C for 12h.

[0037] (2) Put the dried pellets into a multi-stage stretching device consisting of an extruder (1), a confluence (2), a force assembly unit (3), and a cooling roller (4) (see figure 1 ) in the extruder. After the continuous division-deformation-stacking action of the force assembly unit, it flows out from the discharge port and is cooled by a traction cooling roller to obtain a polypropylene material with a thickness of about 1.5mm. Then the samples were annealed in a vacuum environment at 145°C for 12h.

[0038] In this embodiment, the force assembly unit adopts three 1 divided into 2 force assembly units.

[0039] Such as figure 1 As shown in , the discharge port of the extruder in the multi-stage stretching device is connected with the feed port of the confluence, the discharge p...

Embodiment 2

[0042] (1) Polypropylene (1005, Formosa Plastics, Taiwan) was selected as the experimental material, and its melt index was 0.5g / 10min (210°C, 2.16Kg). Vacuum dry in an oven at 80°C for 12h.

[0043] (2) Put the dried pellets into a multi-stage stretching device consisting of an extruder (1), a confluence (2), a force assembly unit (3), and a cooling roller (4) (see figure 1 ) in the extruder. After the continuous division-deformation-stacking action of the force assembly unit, it flows out from the discharge port and is cooled by a traction cooling roller to obtain a polypropylene material with a thickness of about 1.5mm. Then the samples were annealed in a vacuum environment at 145°C for 12h. Among them, the temperatures of the feeding port, conveying section, melting section, and homogenizing section of the single-screw extruder (1) are respectively 155°C, 205°C, 215°C, and 215°C; °C, 210 °C.

[0044] In this embodiment, the force assembly unit adopts seven force assemb...

Embodiment 3

[0047] (1) Polypropylene (1005, Formosa Plastics, Taiwan) was selected as the experimental material, and its melt index was 0.5g / 10min (210°C, 2.16Kg). Vacuum dry in an oven at 80°C for 12h.

[0048] (2) Put the dried pellets into a multi-stage stretching device consisting of an extruder (1), a confluence (2), a force assembly unit (3), and a cooling roller (4) (see figure 1 ) in the extruder. After the continuous division-deformation-stacking action of the force assembly unit, it flows out from the discharge port and is cooled by a traction cooling roller to obtain a polypropylene material with a thickness of about 1.5mm. Then the samples were annealed in a vacuum environment at 145°C for 12h. Among them, the temperatures of the feeding port, conveying section, melting section, and homogenizing section of the single-screw extruder (1) are respectively 155°C, 205°C, 215°C, and 215°C; °C, 210 °C.

[0049] In this embodiment, the force assembly unit adopts 7 1 divided into 8...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a high-strength polypropylene material. The preparation method is characterized in that in the machining process, the crystal habit of polypropylene is regulated and controlled, and therefore the mechanical performance of polypropylene is improved. In the machining process, a certain shear and two-way stretch force field is applied to polypropylene melt by regulating the number and type of force assembling units, under the action of the force field, the crystal habit of polypropylene is developed into shish-kebab structures orientated in different directions, the stretch strength of the polypropylene material can be remarkably improved, and the difference of the mechanical strength, in the extrusion direction, of the polypropylene product and the mechanical strength in the direction perpendicular to the extrusion direction, of the polypropylene product is weakened. The force assembling units are added to existing traditional extrusion equipment, operation is easy, continuous production can be achieved, control is convenient, quality is stable, production efficiency is high, and good industrial and market prospects are achieved; and the method can be widely applied to preparing high-strength polypropylene plate, sheet and film materials.

Description

technical field [0001] The invention relates to a method for preparing a high-strength polypropylene material, and belongs to the technical field of polymer material processing. Background technique [0002] Polypropylene is non-toxic, odorless and tasteless, and has a low relative density, only 0.90~0.91g / m 3 , is one of the lightest varieties of all plastics. The chemical stability of polypropylene is very good, and polypropylene is also particularly stable to water, with a water absorption rate of only 0.01% in water. Good formability. Because of the excellent comprehensive properties of polypropylene, it is widely used in large and small areas of daily life such as automobiles, construction, home furnishing, home appliances, and packaging printing industry. In the field of general plastic applications, its production capacity and consumption are second only to polyethylene. second. From 2010 to now, in just five years, my country's polypropylene production capacity h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C47/00B29C47/08
CPCB29C48/00B29C48/267B29K2023/12
Inventor 吴宏王萃林郭少云夏立超王建峰
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com