A kind of graphene-based water-based conductive electromagnetic shielding architectural coating and production method thereof
An electromagnetic shielding and architectural coating technology, applied in conductive coatings, coatings, etc., can solve the problems of poor electromagnetic wave shielding performance, poor resistance to cold and heat cycles, and poor substrate adhesion, and achieve good adhesion and excellent electromagnetic properties. Shielding performance, good effect of cold and heat cycle resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031]A water-based conductive electromagnetic shielding architectural coating based on graphene, comprising the following raw materials in parts by weight: 1 part of propylene glycol, 0.1 part of 2-amino-2-methyl-1-propanol, 0.1 part of polyoxyethylene alkyl ether , 0.1 part of polymer block copolymer, 0.1 part of silicone defoamer, 1 part of graphene, 35 parts of calcium carbonate, 0.05 part of 1,2-benzisothiazolin-3-one (BIT), 2-methanol 0.05 parts of methyl-5-chloro-4-isothiamidazol-3-one (CMIT), 0.05 parts of 2-methyl-4-isothiamidazol-3-one (MIT), iodopropynyl carbamate 0.1 part, 1 part of lauryl alcohol ester, 1 part of hydroxyethyl cellulose, 15 parts of acrylate-styrene copolymer emulsion, 45.4 parts of deionized. The solid content of the acrylate-styrene copolymer emulsion is 48%, the pH is 8.0, the particle size of the copolymer emulsion is 0.15 microns, the product viscosity is 1500mPa·s, the minimum film-forming temperature of the product is 22°C, and the product i...
Embodiment 2
[0039] A water-based conductive electromagnetic shielding architectural coating based on graphene, comprising the following raw materials in parts by weight: 3 parts in propylene glycol ethers, 0.2 parts in dimethylethanolamine, 0.3 parts in polyoxyethylene polyol ethers , 1 part of polyphosphate, 0.5 parts of aliphatic hydrocarbon emulsion, 5 parts of graphene, 50 parts of calcium carbonate, 0.1 part of 1,2-benzisothiazolin-3-one (BIT), 2-methyl- 0.1 part of 5-chloro-4-isothiamidazol-3-one, 0.1 part of 2-methyl-4-isothiamidazol-3-one (CMIT / MIT), 0.3 part of methyl benzimidazole carbamate, 12 3 parts of alcohol ester, 2 parts of polyurethane thickener, 25 parts of acrylate-styrene copolymer emulsion, 9.4 parts of deionized water. The solid content of the acrylate-styrene copolymer emulsion is 48%, the pH is 8.0, the particle size of the copolymer emulsion is 0.15 microns, the product viscosity is 1500mPa·s, the minimum film-forming temperature of the product is 22°C, and the p...
Embodiment 3
[0047] A water-based conductive electromagnetic shielding architectural coating based on graphene, comprising the following raw materials in parts by weight: each raw material comprising the following parts by weight: 1 part of propylene glycol, 1 part of propylene glycol ether, 0.1 part of potassium hydroxide, fatty acid polyethylene glycol 0.2 parts of esters, 0.5 parts of polycarboxylates, 0.3 parts of non-silicone organic ester hydrocarbons, 3 parts of graphene, 42 parts of calcium carbonate, 0.1 parts of 1,2-benzisothiazolin-3-one (BIT) , 0.05 part of 2-methyl-5-chloro-4-isothiamidazol-3-one and 0.05 part of 2-methyl-4-isothiamidazol-3-one (CMIT / MIT), iodopropynylamino 0.2 parts of formate, 2 parts of lauryl alcohol ester, 1.5 parts of modified polyurea thickener, 20 parts of acrylate-styrene copolymer emulsion, and 28 parts of deionized water. The solid content of the acrylate-styrene copolymer emulsion is 48%, the pH is 8.0, the particle size of the copolymer emulsion i...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
temperature | aaaaa | aaaaa |
glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap