High-magnetic-conductivity wave-absorbing sheet and tape-casting slurry and preparation method therefor

A technology of casting slurry and high magnetic permeability, which is applied in the direction of shielding materials, magnetic field/electric field shielding, electrical components, etc. No high problems, to achieve the effect of improving quality and flexibility, resistivity, good wettability, high quality and magnetic permeability

Active Publication Date: 2016-06-15
SHENZHEN PENGHUI FUNCTIONAL MATERIAL CO LTD
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the above-mentioned deficiencies of the prior art, to provide a high-permeability wave-absorbing sheet, its preparation method and its casting slurry, so as to solve the technical problem that the magnetic permeability of the existing wave-abs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-magnetic-conductivity wave-absorbing sheet and tape-casting slurry and preparation method therefor
  • High-magnetic-conductivity wave-absorbing sheet and tape-casting slurry and preparation method therefor
  • High-magnetic-conductivity wave-absorbing sheet and tape-casting slurry and preparation method therefor

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] In another aspect, the embodiment of the present invention also provides a method for preparing the high permeability absorber of the embodiment of the present invention described above. In an embodiment, the process of the preparation method of the high permeability absorber of the present invention is as follows: figure 2 As shown, it includes the following steps:

[0038] Step S01. Obtain the raw material of the casting slurry of the high permeability absorber: Weigh the components contained in the casting slurry of the high permeability absorber as described above, including soft magnetic alloy powder Component raw materials for organic insulating elastomers, hard-to-volatile organic solvents, plasticizers, and dispersants;

[0039] Step S02. Prepare a mixed solution containing organic insulating elastomer, hardly volatile organic solvent, plasticizer, and dispersant: heat the organic insulating elastomer, hardly volatile organic solvent, plasticizer, and dispersant we...

Example Embodiment

[0052] Example 1

[0053] This embodiment provides a high magnetic permeability wave absorbing plate and its casting slurry and a preparation method thereof. The casting slurry of the high magnetic permeability wave absorbing plate of this embodiment includes the following components by weight:

[0054]

[0055] The preparation method of the high permeability wave absorbing plate of this embodiment is as follows:

[0056] Step S11. According to the present Example 1, the components contained in the casting slurry of the high permeability absorber were weighed, including soft magnetic alloy powder, organic insulating elastomer, hard-to-volatile organic solvent, plasticizer, and dispersion. Ingredient raw materials;

[0057] Step S12. The organic insulating elastomer, hardly volatile organic solvent, plasticizer, and dispersant weighed in step S11 are heated and stirred at 80° C. to obtain a mixed solution;

[0058] Step S13. The soft magnetic alloy powder weighed in step S11 is ball-mi...

Example Embodiment

[0060] Example 2

[0061] This embodiment provides a high magnetic permeability wave absorbing plate and its casting slurry and a preparation method thereof. The casting slurry of the high magnetic permeability wave absorbing plate of this embodiment includes the following components by weight:

[0062]

[0063] The preparation method of the high permeability wave absorbing plate of this embodiment is as follows:

[0064] Step S21. According to the present embodiment 2, the components contained in the casting slurry of the high permeability absorber are respectively weighed, including soft magnetic alloy powder, organic insulating elastomer, hard-to-volatile organic solvent, plasticizer, dispersion Ingredient raw materials;

[0065] Step S22. The organic insulating elastomer, hard-to-volatile organic solvent, plasticizer, and dispersant weighed in step S21 are heated and stirred at 70°C to obtain a mixed solution;

[0066] Step S23. The soft magnetic alloy powder weighed in step S21 i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-magnetic-conductivity wave-absorbing sheet and tape-casting slurry and a preparation method therefor. The tape-casting slurry for the high-magnetic-conductivity wave-absorbing sheet comprises the following ingredients in parts by weight: 80-85 parts of soft magnetic alloy powder, 8-12 parts of organic insulating elastic body, 3-5 parts of nonvolatile organic solvent, 2-3 parts of plasticizer and 1-3 parts of dispersing agent. The high-magnetic-conductivity wave-absorbing sheet is molded from the tape-casting slurry through a tape-casting process. The tape-casting slurry for the high-magnetic-conductivity wave-absorbing sheet has high wettability for the soft magnetic alloy powder; the prepared wave-absorbing sheet has high magnetic-conductivity, high resistivity and high flexibility; in addition, the preparation method is easy to control; and the prepared wave-absorbing sheet is high in yield and stable in performance.

Description

technical field [0001] The invention belongs to the technical field of electronic component materials, and in particular relates to a high-permeability wave-absorbing sheet slurry, a high-magnetic-permeability wave-absorbing sheet and a preparation method thereof. Background technique [0002] Near Field Communication technology (NearFieldCommunication, NFC) is initiated by Philips and jointly launched by famous manufacturers such as Nokia and Sony. It uses mobile phones as the carrier and combines non-contact IC card applications in mobile phones. Cards, readers, point-to-point Three application modes, realizing mobile payment, data transmission, point exchange, electronic ticketing, identification, anti-counterfeiting, advertising and other technical services for various applications. [0003] The specific application of NFC technology can be divided into the following three types: NFC mobile phone terminal can be simulated as an ordinary contactless card, which is mainly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H05K9/00
CPCH05K9/0075
Inventor 李立星
Owner SHENZHEN PENGHUI FUNCTIONAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap