A kind of Jingdezhen Yingqing reinforced porcelain and its preparation method

A technology for strengthening porcelain and porcelain stone, which is applied in the field of Jingdezhen shadow celadon and its preparation, can solve the problems of easy breakage of manufacturing molding, low production qualification rate, poor impact resistance, etc., and achieves good molding performance, low production cost, and reduced expansion. The effect of coefficients

Active Publication Date: 2018-04-17
景德镇邑山瓷业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, shadow celadon has the disadvantages of poor impact resistance, low glaze hardness and low thermal shock resistance. Low, with a flexural strength of 48-62 MPa, it is easy to cause damage due to collision during transportation and loading and unloading, especially when hotels and hotels adopt mechanical washing, which is not only easy to be broken, but also has serious scratches on the glaze surface, which affects the beauty of the product. Limit the application of shadow celadon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of Jingdezhen Yingqing reinforced porcelain and its preparation method
  • A kind of Jingdezhen Yingqing reinforced porcelain and its preparation method
  • A kind of Jingdezhen Yingqing reinforced porcelain and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The material composition of Jingdezhen Yingqing Celadon strengthened porcelain in the embodiment of the present invention is shown in Table 1.

[0025] Table 1 Material composition of Jingdezhen shadow celadon strengthened porcelain in the embodiment of the present invention

[0026]

[0027]

[0028] Note: *The amount of green body additives is relative to the green body base material.

[0029] **The amount of glaze additives is relative to the glaze base.

[0030] The solid content of the organic silicon nano-liquid is 40%, and the solid content of the nano aluminum sol is 25%.

[0031] The method for preparing Jingdezhen shadow celadon strengthened porcelain in the embodiment of the present invention includes the following steps:

[0032] (1) The body base material and the glaze base material are respectively ball-milled and mixed, and then the body additives and the glaze additives are added to the body and the glaze additives respectively and mixed uniformly to obtain the bla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Jingdezhen misty blue durable china which comprises a blank and a glaze. The blank is composed of a billet base material and billet additives; and the billet base material is composed of 45-60 wt% of sericite porcelain stone, 20-30 wt% of washed sludge, 15-25 wt% of Guiqi kaolin, 4-10 wt% of water milled quartz, 1-2 wt% of spodumene, 0-2 wt% of calcined talcum and 0-3 wt% of rare-earth tailing. The glaze is composed of a glaze base material and glaze additives; and the glaze base material is composed of 45-65 wt% of Yaoli Youguo, 10-18 wt% of Guiqi kaolin, 5-15 wt% of quartz, 5-12 wt% of glaze ash, 5-10 wt% of potash feldspar, 5-10 wt% of dolomite, 3-5 wt% of castorite, 1-3 wt% of barium carbonate and 1-4 wt% of calcined talcum. Besides, the invention also discloses a preparation method of the Jingdezhen misty blue durable china. The misty blue durable china product has the advantages of high strength, high jade sensation and low cost, can well satisfy the use safety and appearance decoration requirements of the consumers, and is beneficial to promoting the technical progress and application development of the misty blue china industry.

Description

Technical field [0001] The invention relates to the technical field of traditional ceramic materials, in particular to a Jingdezhen shadow celadon and a preparation method thereof. Background technique [0002] Jingdezhen shadow celadon is also called Ying celadon. Its predecessor is blue and white porcelain. The shadow celadon called "white white and blue" was originally created by Jingdezhen in the middle of the Northern Song Dynasty. Its glaze is blue and white and elegant, the glaze is clear and clean, and the fetal texture is firm and white. The color is as gentle as jade, and it is a treasure in the traditional porcelain-making craftsmanship of the Han nationality. [0003] With the development of economy and the continuous improvement of people’s living standards, people’s requirements for daily-use ceramics are getting higher and higher. They must have practical value as well as artistic value. Among them, shadow celadon is a porcelain with historical and cultural value. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/02C04B33/13C04B33/16C04B33/132C04B33/24C04B33/34C03C8/16
CPCC03C8/16C04B33/02C04B33/1305C04B33/131C04B33/1321C04B33/1324C04B33/16C04B33/24C04B33/34C04B2235/3427C04B2235/3472Y02P40/60
Inventor 包启富何芹李新青董伟霞
Owner 景德镇邑山瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products