Corrosion-resistant cement clinker warehouse top conveyor

A clinker silo and top conveying technology, which is applied in the field of conveyors, can solve the problems of the mechanical strength of the cement clinker silo top conveyor plummeting, corrosion, and the collapse of the cement clinker silo top conveyor.

Inactive Publication Date: 2016-07-20
WUHU ADER CONVEYOR MACHINERY
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the strong corrosiveness of cement clinker, the top conveyor of the cement clinker silo will corrode after a long period of use, which will lead to a sh...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1) Mix high manganese steel, zinc oxide, chromium oxide, nickel sulfate, graphite, asbestos, chalcocite, stibnite and cassiterite according to the weight of 100:28:10:49:6:16:18:65:38 After mixing, the raw materials were heated from 25°C to 1445°C over 25 minutes and kept for 2.5 hours, then cooled to 1400°C over 20 minutes and kept for 2.5 hours, and finally raised to 1425°C over 45 minutes and kept for 1.2 hours to obtain a melt;

[0031] 2) Mix the melt, silicon carbide, magnesium borate whiskers (4um in diameter, 100um in length) and graphene at a weight ratio of 100:35:9:11 and reheat at 1590°C for 4h, then heat at 1280°C Water quenching at ℃ for 4 min to prepare the steel material A1 in the top conveyor of the corrosion-resistant cement clinker silo.

Embodiment 2

[0033] 1) Mix high manganese steel, zinc oxide, chromium oxide, nickel sulfate, graphite, asbestos, chalcocite, stibnite and cassiterite according to the weight of 100:25:7:45:4:12:15:60:34 After mixing, the raw material is heated from 15°C to 1440°C for 20 minutes and kept for 2 hours, then cooled to 1390°C for 15 minutes and kept for 2 hours, and finally raised to 1420°C for 40 minutes and kept for 1 hour to obtain a melt;

[0034] 2) Mix the melt, silicon carbide, magnesium borate whiskers (1um in diameter, 30um in length) and graphene at a weight ratio of 100:30:8:9 and heat for a second time at 1550°C for 3h, then heat at 1240°C ℃ water quenching for 3 minutes to prepare the steel material A2 in the top conveyor of the corrosion-resistant cement clinker silo.

Embodiment 3

[0036] 1) Mix high manganese steel, zinc oxide, chromium oxide, nickel sulfate, graphite, asbestos, chalcocite, stibnite and cassiterite according to the weight of 100:31:14:52:8:18:22:71:52 After mixing, the raw materials were heated from 30°C to 1450°C for 30 minutes and kept for 3 hours, then cooled to 1410°C for 25 minutes and kept for 3 hours, and finally raised to 1430°C for 50 minutes and kept for 1.5 hours to obtain a melt;

[0037] 2) Mix the melt, silicon carbide, magnesium borate whiskers (8um in diameter, 200um in length) and graphene at a weight ratio of 100:44:10:13 and reheat at 1620°C for 5h, then heat at 1310°C °C for 5 min in water to prepare steel A3 for the corrosion-resistant cement clinker silo top conveyor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a corrosion-resistant cement clinker warehouse top conveyor. A processing method for steel in the corrosion-resistant cement clinker warehouse top conveyor comprises the steps that (1) high-manganese steel, zinc oxide, chromic oxide, nickel sulfate, graphite, asbestos, chalcocite, stibnite and cassiterite are molten at the temperature of 1390-1450 DEG C so as to obtain molten mixture; and (2) silicon carbide, magnesium borate whiskers, graphene and the molten mixture are reheated at the temperature of 1550-1620 DEG C, and then water quenching is conducted at the temperature of 1240-1310 DEG C so as to obtain the steel in the corrosion-resistant cement clinker warehouse top conveyor. The corrosion-resistant cement clinker warehouse top conveyor has excellent mechanical strength and corrosion resistance.

Description

technical field [0001] The invention relates to a conveyor, in particular to a corrosion-resistant cement clinker roof conveyor. Background technique [0002] Conveyors have a long history. The ancient Chinese high-drum carts and water-lifting dump trucks are the prototypes of modern bucket elevators and scraper conveyors. A conveyor is a material handling machine that continuously conveys materials on a certain route, also known as a continuous conveyor. The conveyor can carry out horizontal and inclined conveying, and can also form a space conveying line, and the conveying line is generally fixed. The conveyor has a large conveying capacity, a long transportation distance, and can complete several process operations at the same time during the conveying process, so it is widely used. Among them, the cement clinker warehouse top conveyor is a conveyor specially used for conveying cement clinker. [0003] Due to the strong corrosiveness of cement clinker, the top conveyor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/04C22C38/18C22C38/08C22C38/16C22C38/60C22C38/02C22C33/06C21D1/18
CPCC22C38/04C21D1/18C22C33/006C22C33/06C22C38/002C22C38/008C22C38/02C22C38/08C22C38/16C22C38/18C22C38/60
Inventor 贾真李开领周勇
Owner WUHU ADER CONVEYOR MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap