Polyurethane composite color fixing agent and preparation method thereof
A technology of color-fixing agent and polyurethane, which is applied in the field of textile materials, can solve the problems of poor fastness to wet treatment and achieve good color-fixing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] A polyurethane composite color-fixing agent is prepared from the following components in parts by weight: 30 parts of polyethylene glycol, 10 parts of polytetrahydrofuran diol, 10 parts of polyoxypropylene glycol, 0.2 parts of aglycone tyrosol, and isophor 2 parts of ketone diisocyanate, 2 parts of trimethylhexamethylenediamine, 0.1 part of sodium citrate, 1 part of octamethylcyclotetrasiloxane, 3 parts of dibutyltin dilaurate, 2 parts of dibutyltin diacetate , 5 parts of trimethylolpropane, 10 parts of glycerol, and 20 parts of deionized water.
[0021] The preparation method of the above-mentioned polyurethane composite color-fixing agent is as follows: (1) put polyethylene glycol and polytetrahydrofuran diol in a vacuum drying oven and dry at a temperature of 40° C. for 8 hours; (2) add them to a three-necked flask, stirring slowly while Add isophorone diisocyanate and trimethylhexamethylenediamine, heat up to 50°C and stir for 60 minutes; (3) reduce to room temperat...
Embodiment 2
[0023] A polyurethane composite color-fixing agent is prepared by weight of the following components: 35 parts of polyethylene glycol, 12 parts of polytetrahydrofuran diol, 15 parts of polyoxypropylene glycol, 0.3 parts of aglycone tyrosol, and isophor 3 parts of ketone diisocyanate, 2.5 parts of trimethylhexamethylenediamine, 0.15 parts of sodium citrate, 1.3 parts of octamethylcyclotetrasiloxane, 4 parts of dibutyltin dilaurate, 2.5 parts of dibutyltin diacetate , 6 parts of trimethylolpropane, 12 parts of glycerol, and 25 parts of deionized water.
[0024] The preparation method of the above-mentioned polyurethane composite color-fixing agent is as follows: (1) put polyethylene glycol and polytetrahydrofuran diol in a vacuum drying oven and dry at a temperature of 45°C for 8.5 hours; (2) add them to a three-necked flask, and stir slowly while Add isophorone diisocyanate and trimethylhexamethylenediamine, heat up to 55°C and stir for 70 minutes; (3) reduce to room temperatur...
Embodiment 3
[0026] A polyurethane composite color-fixing agent is prepared from the following components in parts by weight: 40 parts of polyethylene glycol, 15 parts of polytetrahydrofuran diol, 20 parts of polyoxypropylene glycol, 0.35 parts of aglycone tyrosol, and isophor 3.5 parts of ketone diisocyanate, 3 parts of trimethylhexamethylenediamine, 0.2 parts of sodium citrate, 1.5 parts of octamethylcyclotetrasiloxane, 5 parts of dibutyltin dilaurate, 3 parts of dibutyltin diacetate , 7.5 parts of trimethylolpropane, 15 parts of glycerol, and 30 parts of deionized water.
[0027] The preparation method of the above-mentioned polyurethane composite color-fixing agent is as follows: (1) Put polyethylene glycol and polytetrahydrofuran diol in a vacuum drying oven and dry at a temperature of 45° C. for 9 hours; (2) Put them into a three-necked flask, and stir slowly while Add isophorone diisocyanate and trimethylhexamethylenediamine, heat up to 60°C and stir for 75 minutes; (3) reduce to ro...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap