Preparation method of deodorant faint-scent non-latex high-elasticity bandage
A fragrance type, bandage technology, applied in bandages, medical science, absorbent pads, etc., can solve problems such as bad smell, poor elasticity, and affecting the effect of use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] A kind of preparation method of deodorizing delicate fragrance type non-latex high elastic bandage that the present invention proposes, comprises the steps:
[0020] S1, preparation of bandages: the weft yarn is selected to be 100% cotton yarn, and the warp thread is made of bare spandex yarn with a denier of 420D, skin color polyester low elastic yarn with a denier of 150D and natural white spandex with a denier of 150D as the fabric base cloth. The fabric base fabric uses 94°C high-temperature water in the liquid flow dyeing machine and the warp and weft yarns of the fabric base fabric are in a relaxed state during processing to obtain elasticity. Replace the weft density gear, start the production of the bandage into the shaping machine, after a high temperature of 180 ℃, the speed is 1100r / min, and the elasticity after shaping is 310%;
[0021] S2. Soaking: Put the bandage prepared in S1 into the soaking solution for soaking treatment. The temperature of the soaking...
Embodiment 2
[0025] A kind of preparation method of deodorizing delicate fragrance type non-latex high elastic bandage that the present invention proposes, comprises the steps:
[0026] S1, preparation of bandages: the weft yarn is selected to be 100% cotton yarn, and the warp thread is made of bare spandex yarn with a denier of 420D, skin color polyester low elastic yarn with a denier of 150D and natural white spandex with a denier of 150D as the fabric base cloth. The fabric base fabric uses 90°C high-temperature water in the liquid flow dyeing machine and the warp and weft yarns of the fabric base fabric are in a relaxed state during processing to obtain elasticity. Replace the weft density gear, start the production of the bandage into the shaping machine, after a high temperature of 200 ℃, the speed is 1000r / min, and the elasticity after shaping is 320%;
[0027] S2. Soaking: Put the bandage prepared in S1 into the soaking solution for soaking treatment. The temperature of the soaking...
Embodiment 3
[0031] A kind of preparation method of deodorizing delicate fragrance type non-latex high elastic bandage that the present invention proposes, comprises the steps:
[0032] S1, preparation of bandages: the weft yarn is selected to be 100% cotton yarn, and the warp thread is made of bare spandex yarn with a denier of 420D, skin color polyester low elastic yarn with a denier of 150D and natural white spandex with a denier of 150D as the fabric base cloth. The fabric base fabric uses 98°C high-temperature water in the liquid flow dyeing machine and the warp and weft yarns of the fabric base fabric are in a relaxed state during processing to obtain elasticity. Replace the weft density gear, start the production of the bandage into the shaping machine, after a high temperature of 160 ℃, the speed is 1200r / min, and the elasticity after shaping is 330%;
[0033] S2. Soaking: Put the bandage prepared in S1 into the soaking solution for soaking treatment. The temperature of the soaking...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com