Lightweight silicon brick
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A silica brick, lightweight technology, applied in the field of refractory materials, can solve the problems of short service life, poor thermal shock resistance, erosion, etc., and achieve the effects of low production raw material cost, strong thermal shock stability, and simple production process
Inactive Publication Date: 2016-12-07
青岛燕园海洋生物科技有限公司
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Silica brick is a siliceous product containing more than 93% of silicon oxide. The raw materials used are silica, waste silica brick, etc. It has strong resistance to acid slag erosion, high softening temperature under load, and does not shrink in volume after repeated calcination, and even slightly expands; However, it is easily corroded by alkaline slag and has poor thermal shock resistance
With the development of science and technology and industry, the requirements for lightweight refractory materials are getting higher and higher. The current lightweight silicon carbide bricks have poor corrosion resistance, short service life, heavy weight, and poor thermal shock resistance. Industrial production
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] A lightweight silica brick comprising the following components in parts by weight:
[0016] 100 parts of silica particles, 120 parts of fine silica powder, 50 parts of silicon dioxide material, 20 parts of silicon carbide, 10 parts of limestone, 5 parts of silica gel liquid, 15 parts of graphite powder, 1 part of foaming agent, and 1 part of sodium tripolyphosphate.
[0017] Silica material is a mixture of silica stone material and waste silica brick pulverized material.
Embodiment 2
[0019] A lightweight silica brick comprising the following components in parts by weight:
[0020] 150 parts of silica particles, 200 parts of silica fine powder, 80 parts of silicon dioxide material, 25 parts of silicon carbide, 20 parts of lime, 7.5 parts of silica gel liquid, 20 parts of graphite powder, 4.5 parts of foaming agent, 1.5 parts of sodium tripolyphosphate.
[0021] Silica material is a mixture of silica stone material and waste silica brick pulverized material.
Embodiment 3
[0023] A lightweight silica brick comprising the following components in parts by weight:
[0024] 200 parts of silica particles, 240 parts of silica fine powder, 100 parts of silicon dioxide material, 30 parts of silicon carbide, 30 parts of limestone, 10 parts of silica gel solution, 25 parts of graphite powder, 5 parts of foaming agent, and 3 parts of sodium tripolyphosphate.
[0025] Silica material is a mixture of silica stone material and waste silica brick pulverized material.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to the technical field of refractory materials, in particular to a lightweight silicon brick. The lightweight silicon brick is prepared from, by weight, 100-200 parts of silica particles, 120-240 parts of silica fine powder, 50-100 parts of silicon dioxide materials, 20-30 parts of silicon carbide, 10-30 parts of limestone, 5-10 parts of silica gel, 15-25 parts of graphite powder, 1-5 parts of a foaming agent and 1-3 parts of sodium tripolyphosphate. The lightweight silicon brick has advantages of light weight, corrosion resistance, high thermal shock resistance, crack resistance, long service life, low cost of production materials, technical simplicity in production, suitableness for industrial production and worthiness of popularization and application.
Description
technical field [0001] The invention relates to the technical field of refractory materials, in particular to a lightweight silica brick. Background technique [0002] Acidic refractory materials are mainly composed of silica, and commonly used are silica bricks and clay bricks. Silica brick is a siliceous product containing more than 93% of silicon oxide. The raw materials used are silica, waste silica brick, etc. It has strong resistance to acid slag erosion, high softening temperature under load, and does not shrink in volume after repeated calcination, and even slightly expands; However, it is easily corroded by alkaline slag and has poor thermal shock resistance. With the development of science and technology and industry, the requirements for lightweight refractory materials are getting higher and higher. The current lightweight silicon carbide bricks have poor corrosion resistance, short service life, heavy weight, and poor thermal shock resistance. Industrial produ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).