PET compound for packaging bottle and manufacturing method thereof

A packaging bottle and composition technology, applied in chemical instruments and methods, natural dyes, azo dyes, etc., can solve problems such as poor radiation resistance, improve compatibility and bonding strength, reduce manufacturing costs, increase The effect of degradation performance

Inactive Publication Date: 2016-12-14
陆志强
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this invention has the same problem of poor radiation resistance as existing PET packaging bottle materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PET compound for packaging bottle and manufacturing method thereof
  • PET compound for packaging bottle and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The PET composition used for packaging bottles, its components in parts by weight are: 50 parts of PET resin, 1.1 parts of stearic acid, 9 parts of TDBPPE, 3.5 parts of EPDM, 0.7 parts of ethylene bis stearamide, 1.5 parts of nano ATO, basalt 5 parts of fiber, 2 parts of methyl phenyl dimethyl silicone, 3.2 parts of maleic anhydride grafted SMA, 5.1 parts of epoxy resin, 7.7 parts of composite melanin capsule, 2 parts of nylon.

[0029] Its manufacturing method is as follows:

[0030] (1) Wash the black grape skins and dry them, crush them to obtain black grape skin powder, add the black grape skin powder to petroleum ether at a material-to-liquid ratio of 1:30, adjust the pH value to 5, and place in a 65°C water bath Extracted from the black grape skin for 2 hours, centrifuged at a speed of 3000 rpm, and dried the obtained filtrate in an oven at 65°C to obtain the black grape skin extract;

[0031] (2) Add the black grape skin extract obtained in step (1) into a sodiu...

Embodiment 2

[0036] The PET composition used for packaging bottles, its components in parts by weight are: 52 parts of PET resin, 1 part of stearic acid, 7 parts of TDBPPE, 3.3 parts of EPDM, 0.5 parts of ethylene bisstearamide, 1.4 parts of nano-ATO, basalt 7 parts of fiber, 1.8 parts of methyl phenyl dimethyl silicone, 3 parts of maleic anhydride grafted SMA, 5 parts of epoxy resin, 7.6 parts of composite melanin capsule, 2 parts of nylon.

[0037] Its manufacture method is the same as embodiment 1.

Embodiment 3

[0039] The PET composition used for packaging bottles, its components in parts by weight are: 54 parts of PET resin, 0.9 part of stearic acid, 5 parts of TDBPPE, 4 parts of EPDM, 0.9 part of ethylene bis stearamide, 2 parts of nano ATO, basalt 9 parts of fiber, 1.6 parts of methyl phenyl dimethyl silicone, 3.6 parts of maleic anhydride grafted SMA, 5.5 parts of epoxy resin, 8 parts of composite melanin capsule, 2 parts of nylon.

[0040] Its manufacture method is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a PET compound for a packaging bottle. The PET compound comprises the following components by weight part: 50-60 parts of PET resins, 0.6-1.1 parts of lubricating agents, 5-10 parts of fire retardants, 3-4 parts of flexibilizer, 0.5-1 part of dispersing agent, 1-2 parts of antistatic agents, 5-10 parts of reinforcing agents, 1-2 parts of low temperature-resisting modifying agents, 3-4 parts of compatilizer, 5-6 parts of epoxy resins, 7-8 parts of compound melanin capsules and 2 parts of nylon. The invention also provides a manufacturing method for the PET compound for the packaging bottle. The PET compound has higher radiation resistance.

Description

technical field [0001] The invention relates to a PET composition, in particular to a PET composition used for packaging bottles and a manufacturing method thereof. Background technique [0002] The full name of PET is Polyethylene Terephthalate (polyethylene terephthalate), which is a polymer produced by combining terephthalic acid (Terephthalic acid) and ethylene glycol (Ethylene glycol), referred to as polyester. PET plastic has the characteristics of light weight, high transparency, impact resistance and not easy to break. It can also block carbon dioxide gas and keep soda water steamy. Therefore, PET plastic is suitable for packaging, especially for water and soft drinks. [0003] The general PET bottle production process is to inject the preform after hot-melting the PET polyester chip with color oil, store it in a certain humidity and temperature environment for a period of time, crystallize or not crystallize, and then blow it into a bottle. PET bottles are mainly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L63/00C08K13/06C08K9/10C08K5/09C08K5/20C08K7/10C09B61/00
CPCC08L67/02C08K2201/011C08L2201/06C08L2203/10C08L2205/035C09B61/00C08L63/00C08K13/06C08K9/10C08K5/09C08K5/20C08K7/10
Inventor 陆志强
Owner 陆志强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap