Anti-aging paint for car storage box and preparing method thereof
A technology of anti-aging paint and storage box, which is applied in the field of paint and achieves the effects of good gloss retention, simple preparation method and convenient transportation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] An aging-resistant coating for automobile storage boxes, characterized in that it is made of the following raw materials in parts by weight: 15 parts of hydroxyl acrylic resin, 5 parts of silicon acrylic emulsion, 5 parts of alkyd resin, 2 parts of epoxy resin, isocyanate 1 part, 0.2 part of dispersant, 1 part of catalyst, 0.2 part of thickener, 1 part of calcium carbonate, 1 part of iron titanium powder, 0.2 part of propylene glycol methyl ether, 0.3 part of cyclohexane, 20 parts of deionized water, 2 parts of pentaerythritol ;
[0020] Its preparation method comprises the following steps in turn:
[0021] (1) Put hydroxyl acrylic resin, silicone acrylic emulsion, alkyd resin, epoxy resin, isocyanate and deionized water into a reaction vessel, control the temperature at 50-60°C, and stir for 15 minutes to disperse the mixture evenly;
[0022] (2) Add calcium carbonate, iron-titanium powder, propylene glycol methyl ether and cyclohexane into the reaction vessel, stir c...
Embodiment 2
[0029] An anti-aging coating for automobile storage boxes, characterized in that it is made of the following raw materials in parts by weight: 35 parts of hydroxyl acrylic resin, 20 parts of silicon acrylic emulsion, 20 parts of alkyd resin, 10 parts of epoxy resin, isocyanate 5 parts, 1 part of dispersant, 5 parts of catalyst, 1.5 parts of thickener, 5 parts of calcium carbonate, 5 parts of iron titanium powder, 1 part of propylene glycol methyl ether, 2 parts of cyclohexane, 50 parts of deionized water, 10 parts of pentaerythritol ;
[0030] Its preparation method comprises the following steps in turn:
[0031] (1) Put hydroxyl acrylic resin, silicone acrylic emulsion, alkyd resin, epoxy resin, isocyanate and deionized water into the reaction vessel, control the temperature at 50-60°C, and stir for 30 minutes to disperse the mixture evenly;
[0032] (2) Add calcium carbonate, iron-titanium powder, propylene glycol methyl ether and cyclohexane into the reaction vessel, stir ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com