Method for measuring elastic modulus of pipe coating

An elastic modulus, measuring tube technology, which is used in the preparation of test samples, and the application of stable tension/pressure to test the strength of materials, etc. Coating elastic modulus, complex testing process, etc.

Active Publication Date: 2017-01-04
CHINA TEST & CERTIFICATION INT GRP CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the process of solving the above problems, the inventors of this case proposed a method for measuring the elastic modulus of ring or tubular brittle materials, but this method can only characterize the elastic modulus of the uniform pipe as a whole, and cannot be used to test the elastic modulus of the pipe surface. Elastic modulus of the coating
At present, the method usually used to measure the elastic modulus of the pipe coating is: use the same substrate, coating material and preparation proce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for measuring elastic modulus of pipe coating
  • Method for measuring elastic modulus of pipe coating
  • Method for measuring elastic modulus of pipe coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0090] Embodiment 1: Measurement of elastic modulus of outer coating

[0091] On the basis of obtaining the elastic modulus of the matrix above, the following steps are also included:

[0092] 1) Remove the inner surface of C-SiC and the upper and lower ends of the coating by grinding to obtain the outer coating of the C-SiC pipe coating sample, and then use a diamond blade to cut a gap with a width of about 2 mm to form a gap ring sample;

[0093] 2) Use a micrometer to measure the outer diameter R of the notched ring sample c = 15.10mm, inner diameter r = 11.95mm, width b = 7.16mm; using a digital microscope to measure the coating thickness h = 36μm; then the outer diameter of the substrate R = Rc-h = 15.064mm;

[0094] 3) Place the notched ring sample with the outer coating on the support table of the universal testing machine, and keep the notch at 1 / 2 of its height, and compress the sample at a loading rate of 0.1mm / min, The compression displacement variation of the no...

Embodiment 2

[0096] Embodiment 2: Measurement of elastic modulus of inner coating

[0097] 1) Remove the outer surface of C-SiC and the coating at the upper and lower ends by cutting to obtain a C-SiC pipe coating sample with an inner coating. Use a polishing machine to polish the surface, and then use a diamond blade to cut out a A notch with a width of about 2 mm to form a notched ring sample;

[0098] 2) Use a micrometer to measure the outer diameter of the notch ring sample R = 15.10mm, inner diameter rc = 11.95mm, width b = 7.14mm; use a digital microscope to measure the coating thickness h = 83μm; then the inner diameter of the substrate r = r c +h=12.033mm;

[0099] 3) Place the notched ring sample with the outer coating on the support table of the universal testing machine, and keep the notch at 1 / 2 of its height, and compress the sample at a loading rate of 0.1mm / min, The compression displacement variation of the notched ring sample between 4N and 10N (△P=6N) was measured by a h...

Embodiment 3

[0101] Embodiment 3: the measurement of elastic modulus of double-sided coating

[0102] 1) Remove the upper and lower coatings of C-SiC by grinding to obtain a double-sided coated C-SiC pipe coating sample, and then use a diamond blade to cut a gap with a width of about 2 mm to form a gap ring sample ;

[0103] 2) Use a micrometer to measure the outer diameter R of the notched ring sample c = 15.10mm, inner diameter r c = 11.95mm, width b = 7.14mm; using a digital microscope to measure the outer coating thickness h1 = 28μm, the inner coating thickness h 2=36μm; then the outer diameter of the substrate R=R c -h1=15.072mm, base inner diameter r=r c + h 2 =11.986mm;

[0104] 3) Place the notched ring sample with the outer coating on the support table of the universal testing machine, and keep the notch at 1 / 2 of its height, and compress the sample at a loading rate of 0.1mm / min, The compression displacement variation of the notched ring sample between 4N and 10N (△P=6N) w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Coating thicknessaaaaaaaaaa
Outer diameteraaaaaaaaaa
The inside diameter ofaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for measuring elastic modulus of a pipe coating. The method comprises the following steps that the elastic modulus Es of matrix of a composite sample to be measured is measured by a gap-ring method; the composite sample to be measured is processed to a gap-ring sample, the gap is formed in the middle of the sample height, and the gap-ring sample of the composite sample is compressed and loaded, the increasing amount of the load delta P and the variable quantity of the compression displacement delta Delta within the online elastic range are recorded; the derived analytic expression of Es, delta P, delta Delta and alpha is used to calculate the ratio alpha of the coating elastic modulus Ec and the matrix elastic modulus Es, and then the coating elastic modulus Ec is obtained according to the equation Ec=alpha*Es. The method is simple in operation, convenient and efficient, and has great practical value and broad application prospect in the engineering field of pipe coating surface technology.

Description

technical field [0001] The invention relates to the technical field of coating mechanical property measurement, in particular to a method for measuring the elastic modulus of a pipe coating. Background technique [0002] In recent years, due to special requirements, a large number of pipes need to serve in various extreme environmental conditions, such as oxidation, corrosion, wear, high temperature and high pressure. Especially in corrosive environments, pipes are required to be resistant to corrosive industrial gases, industrial solutions, high-temperature molten salts, etc. under service conditions, so corrosion-resistant coatings are widely used in such pipes. And some pipes must meet certain functional requirements during service. For example, the selective absorption coating in the vacuum heat collecting tube must meet the requirement of high absorption rate of solar radiation in order to improve the heat collection efficiency of the vacuum heat collecting tube. In or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N3/08G01N1/28
CPCG01N1/28G01N3/08
Inventor 包亦望聂光临万德田刘小根刘钊
Owner CHINA TEST & CERTIFICATION INT GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap