Highly-flame-retardant scratch-resistant frosting TPE sheathing material

A scratch-resistant, highly flame-retardant technology, used in plastic/resin/wax insulators, organic insulators, electrical components, etc., to achieve the effect of maintaining appearance quality, high oil resistance, and good appearance quality

Inactive Publication Date: 2017-02-15
中广核高新核材集团(东莞)祈富新材料有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing optical cable sheathing materials are difficult to meet these requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1: The high flame-retardant, scratch-resistant and frosted TPE sheathing material provided in this example includes the following components by weight percentage: 15% of styrenic block copolymer, 6% of modified polyphenylene ether, thermoplastic Dynamic vulcanized rubber 15%, polyolefin 13%, filler oil 13%, plasticizer 10%, flame retardant 25%, lubricant 2.5%, UV light stabilizer 0.5%; its preparation method adopts conventional extrusion molding process, double The screw extrusion condition is a temperature of 200°C. Among them, the thermoplastic dynamically vulcanized rubber includes the following components in parts by weight: 60 parts of nitrile rubber, 20 parts of thermoplastic polyester elastomer, 25 parts of polylactic acid, 2 parts of phenolic resin vulcanization system, 20 parts of naphthenic oil softener, 1 part of oxygen agent 1010, 8 parts of inorganic filler, 3 parts of silane coupling agent KH570. The preparation method of this thermoplastic dynami...

Embodiment 2

[0024] Example 2: The high flame-retardant, scratch-resistant and frosted TPE sheathing material provided in this example is basically the same as Example 1, except that:

[0025] A high flame-retardant, scratch-resistant and abrasive-feeling TPE sheathing material, comprising the following components by weight percentage: 35% styrene-based block copolymer, 10% modified polyphenylene ether, 7% thermoplastic dynamic vulcanized rubber, polyolefin 5%, extender oil 15%, plasticizer 7%, flame retardant 20%, lubricant 0.8%, UV light stabilizer 0.2%; Polyolefin is ethylene-octene copolymer, and flame retardant consists of Phosphorus-based flame retardant 11%, organosilicon-based flame retardant 9%.

[0026] Among them, the thermoplastic dynamically vulcanized rubber includes the following components in parts by weight: 70 parts of nitrile rubber, 10 parts of thermoplastic polyester elastomer, 30 parts of polylactic acid, 1 part of phenolic resin vulcanization system, 30 parts of naph...

Embodiment 3

[0028] Example 3: The high flame-retardant, scratch-resistant and frosted TPE sheathing material provided in this example is basically the same as Example 1, except that:

[0029] A high flame-retardant, scratch-resistant and abrasive-feeling TPE sheathing material, comprising the following components by weight percentage: 20% styrene block copolymer, 15% modified polyphenylene ether, 10% thermoplastic dynamic vulcanized rubber, polyolefin 7%, extender oil 8%, plasticizer 3%, flame retardant 35%, lubricant 1.7%, UV light stabilizer 0.3%; Polyolefin is ethylene-octene copolymer; Flame retardant consists of Composition of 20% phosphorus-based flame retardant and 15% silicone-based flame retardant.

[0030] Among them, the thermoplastic dynamically vulcanized rubber includes the following components in parts by weight: 66 parts of nitrile rubber, 11 parts of thermoplastic polyester elastomer, 27 parts of polylactic acid, 1.5 parts of phenolic resin vulcanization system, 26 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a highly-flame-retardant scratch-resistant frosting TPE sheathing material. The highly-flame-retardant scratch-resistant frosting TPE sheathing material comprises the following components in percentage by weight: 15 to 35 percent of styrene block copolymer, 6 to 15 percent of modified polyphenyl ether, 7 to 15 percent of thermoplastic dynamic vulcanized rubber, 5 to 18 percent of polyolefin, 8 to 15 percent of extending oil, 3 to 10 percent of plasticizer, 20 to 35 percent of flame retardant, 0.8 to 3 percent of lubricant and 0.2 to 0.5 percent of UV stabilizer. As compared with the prior art, reasonable proportions of components are obtained through elaborate design and repetitive tests, finally the highly-flame-retardant scratch-resistant frosting TPE sheathing material is obtained, the surface of the outer sheath produced by using the material disclosed by the invention is wear-resistant, the scratch resistance is excellent, scratches are not easily produced on the surface, the maximum oxygen index can reach to 40, the flame-retardant effect is very good, and the material further has the advantages of good frosting hand feeling, high oil resistance, low surface gloss, high tensile strength, good impact resistance and low temperature resistance, good processing performance and the like.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a TPE sheathing material with a high flame-retardant, scratch-resistant and frosted feel. Background technique [0002] The cable sheath is an indispensable intermediate structural part of the cable, which plays the role of protecting the cable, ensuring the safety of the cable, and isolating the copper wire from water, air and other media to avoid leakage. Cables are susceptible to scratches during laying and moving. Especially the special optical cables used in 3G communication projects and fiber-to-the-home projects are mostly used in mobile communication base stations or indoors, and the materials used for the sheath of optical cables are required to be environmentally friendly, flame-retardant, low-smoke and non-toxic; The optical cable is used indoors, the space is small, the movement is frequent, and it is easy to be scratched. It is required that the surface of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L9/02C08L67/00C08L67/04C08L61/06C08L23/08C08L71/12C08L91/00H01B3/44
CPCC08L53/025C08L2201/02C08L2201/08C08L2203/202C08L2205/02C08L2205/025C08L2205/035C08L2207/04H01B3/442C08L9/02C08L67/00C08L67/04C08L61/06C08L23/0815C08L71/126C08L91/00
Inventor 伍春平
Owner 中广核高新核材集团(东莞)祈富新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap