A kind of cherry blossom glaze and its preparation process
A preparation process, cherry blossom technology, applied in the field of cherry blossom glaze and its preparation technology, to achieve the effects of reducing the expansion coefficient, enriching the color, and improving the success rate of sintering
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] A kind of cherry blossom glaze is prepared from the following raw materials in parts by weight:
[0028] Bottom glaze: 55 parts of potassium feldspar, 8 parts of iron oxide, 6 parts of silica, 10 parts of talc, 8 parts of calcium carbonate;
[0029] Surface glaze: 25 parts of albite, 10 parts of calcium carbonate, 2 parts of barium carbonate, 1 part of zinc oxide, 0.5 part of magnesium carbonate, 30 parts of kaolin, 2 parts of silica, 7 parts of talc.
[0030] The glaze bottom of the cherry blossom glaze porcelain prepared in this example shows a faint and elegant cyan color, and the white glaze is dotted with patches of peach color like an ink painting, just like blooming cherry blossoms, fresh and unique, elegant and beautiful, with a mellow charm.
Embodiment 2
[0032] A kind of cherry blossom glaze is prepared from the following raw materials in parts by weight:
[0033] Bottom glaze: 75 parts of potassium feldspar, 15 parts of iron oxide, 12 parts of silica, 18 parts of talc, 15 parts of calcium carbonate;
[0034] Surface glaze: 35 parts of albite, 18 parts of calcium carbonate, 8 parts of barium carbonate, 5 parts of zinc oxide, 2 parts of magnesium carbonate, 42 parts of kaolin, 8 parts of silica, and 15 parts of talc.
[0035] The glaze bottom of the cherry blossom glaze porcelain prepared in this example shows a faint and elegant cyan color, and the white glaze is dotted with patches of peach color like an ink painting, just like blooming cherry blossoms, fresh and unique, elegant and beautiful, with a mellow charm.
Embodiment 3
[0037] A kind of cherry blossom glaze is prepared from the following raw materials in parts by weight:
[0038] Bottom glaze: 60 parts of potassium feldspar, 10 parts of iron oxide, 8 parts of silica, 10 parts of talc, 8 parts of calcium carbonate;
[0039] Surface glaze: 25 parts of albite, 12 parts of calcium carbonate, 3 parts of barium carbonate, 1 part of zinc oxide, 1 part of magnesium carbonate, 32 parts of kaolin, 3 parts of silica, and 8 parts of talc.
[0040] The glaze bottom of the cherry blossom glaze porcelain prepared in this example shows a faint and elegant cyan color, and the white glaze is dotted with patches of peach color like an ink painting, just like blooming cherry blossoms, fresh and unique, elegant and beautiful, with a mellow charm.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap