Female breast simulated polyethylene composite material

A composite material and polyethylene technology, which is applied in the field of composite material processing, can solve the problems affecting the appearance and transparency of the pacifier, the large difference in the texture of the mother's breast, and the difficulty in adjusting the formula of the compound rubber, etc., to achieve broad market promotion potential and excellent mechanics Improvement of performance and impact strength

Inactive Publication Date: 2017-02-22
佛山慧创正元新材料科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nipples made of high-temperature heat-vulcanized silicone rubber compound also have some problems: the formula of the compound is difficult to adjust, and it is prone to yellowing, which affects the appearance and transparency of the nipple; the product needs secondary vulcanization to eliminate residual vulcanizing agent Odor from pyrolysis
However, in order to ensure that the tear resistance, stretch resistance and resilience of the pacifier meet the actual use, the hardness of the pacifier products is mostly (Shore A) 40-50 degrees, which is quite different from the texture of the mother's breast.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Female breast simulated polyethylene composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A breast milk simulation polyethylene composite material is composed of the following components in parts by weight:

[0036] 100 parts of linear low density polyethylene, 12 parts of isotactic polypropylene, 8 parts of guar gum, 7 parts of ferric chloride aqueous solution (20% in mass concentration), 0.6 parts of 3,3'-oxindole, 2,4- 0.1 parts of difluorobenzoic acid.

[0037] Its preparation method comprises the following steps:

[0038] Step 1: Weigh raw materials according to the number of parts by mass;

[0039] Step 2: Put polyethylene, polypropylene, and guar gum in graphite molds, put them in a high-temperature furnace, and evacuate to 1×10 - 2 Pa, heated up to 1800°C at a heating rate of 30°C / min, filled with argon, and pressurized to 1×10 7 Pa;

[0040] Step 3: Place 3'-oxindole and 2,4-difluorobenzoic acid in a graphite mold with a filler rod, stir evenly, and keep warm for 12 minutes;

[0041] Step 4: Pour ferric chloride aqueous solution onto the surfa...

Embodiment 2

[0043] A breast milk simulation polyethylene composite material is composed of the following components in parts by weight:

[0044] 150 parts of low-density polyethylene, 17 parts of isotactic polypropylene, 15 parts of guar gum, 10 parts of ferric chloride aqueous solution (22% in mass concentration), 1.2 parts of 3,3'-oxindole, 2,4-di 0.4 parts of fluorobenzoic acid.

[0045] Its preparation method comprises the following steps:

[0046] Step 1: Weigh raw materials according to the number of parts by mass;

[0047] Step 2: Put polyethylene, polypropylene, and guar gum in graphite molds, put them in a high-temperature furnace, and evacuate to 1×10 - 4 Pa, heated up to 2300°C at a heating rate of 50°C / min, filled with argon, and pressurized to 3×10 7 Pa;

[0048] Step 3: Place 3'-oxindole and 2,4-difluorobenzoic acid in a graphite mold with a filler rod, stir evenly, and keep warm for 15 minutes;

[0049] Step 4: Pour ferric chloride aqueous solution onto the surface of...

Embodiment 3

[0050] A breast milk simulation polyethylene composite material is composed of the following components in parts by weight:

[0051]110 parts of linear low density polyethylene, 13 parts of isotactic polypropylene, 9 parts of guar gum, 7 parts of ferric chloride aqueous solution (20% in mass concentration), 0.8 parts of 3,3'-oxindole, 2,4- 0.2 parts of difluorobenzoic acid.

[0052] Its preparation method comprises the following steps:

[0053] Step 1: Weigh raw materials according to the number of parts by mass;

[0054] Step 2: Put polyethylene, polypropylene, and guar gum in graphite molds, put them in a high-temperature furnace, and evacuate to 1×10 - 2 Pa, heated up to 2300°C at a heating rate of 30°C / min, filled with argon, and pressurized to 3×10 7 Pa;

[0055] Step 3: Place 3'-oxindole and 2,4-difluorobenzoic acid in a graphite mold with a filler rod, stir evenly, and keep warm for 12 minutes;

[0056] Step 4: Pour ferric chloride aqueous solution onto the surfac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a female breast simulated polyethylene composite material. The material is prepared from, by weight, 100-150 parts of polyethylene, 12-17 parts of polypropylene, 8-15 parts of guar gum, 7-10 parts of ferric chloride aqueous solution, 0.6-1.2 parts of 3,3'-oxoindole and 0.1-0.4 part of 2,4-difluorobenzoic acid. The invention further discloses a method for preparing the female breast simulated polyethylene composite material and application of the female breast simulated polyethylene composite material to materials of infantile pacifiers or teats. The composite material is high in female breast texture simulation degree, excellent in tear resistance, stretch resistance and rebound resilience and appropriate in softness and is a great substitute for silicon rubber or rubber and high in market promotion potential.

Description

[0001] Technical field: [0002] The invention relates to the field of composite material processing, in particular to a breast milk simulated polyethylene composite material. [0003] Background technique: [0004] The material used to make baby pacifiers has historically been natural latex. Natural latex is a very elastic and soft material with very good elasticity, easy to return to its original shape, and it is not harmful to the environment. However, the disadvantage of natural latex baby pacifiers is that they are easy to age and have a short service life. Then there were silicone rubber nipples that included high-temperature heat-vulcanized silicone rubber compounds and addition-type liquid silicone rubber. Silicone rubber nipples have the characteristics of high temperature resistance, can be boiled repeatedly, are not easy to age, and have a longer service life. Nipples made of high-temperature heat-vulcanized silicone rubber compound also have some problems: the fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L23/12C08L5/00C08K3/16C08K5/3417C08K5/095
CPCC08L23/0815C08K2201/017C08L23/06C08L2205/03C08L2207/066C08L2207/10C08L2312/00
Inventor 叶青
Owner 佛山慧创正元新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap