An optical glass and glass technology, applied in the field of glass preforms and optical components, can solve the problems of reduced devitrification resistance and rising liquidus temperature of glass, and achieves low liquidus temperature, high devitrification resistance, and excellent transmission. rate effect

Inactive Publication Date: 2017-03-01
CDGM OPTICAL GLASS
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the glass also contains a lot of ZnO, which leads to a decrease in the devitrification resistance of the glass and an increase in the liquidus temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical glass
  • Optical glass
  • Optical glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0084] The present invention is explained using the following examples, but the present invention should not be limited to these examples.

[0085] [Optical glass example]

[0086] First, in order to obtain glasses No. 1-35 having the compositions shown in Table 1-Table 4, carbonates, nitrates, sulfates, hydroxides, oxides, boric acid, etc. were used as raw materials to prepare optical glass components Corresponding raw materials Weigh each raw material in proportion, mix them thoroughly to become a blended raw material, put the blended raw material into a platinum crucible, heat to 1380-1450°C, clarify and stir for 3-5 hours, and then become a uniform melting Glass, then pour the molten glass into a preheated mold and keep it at 650-700° C. for 2-4 hours, then slowly cool it to obtain the optical glasses of Glass No. 1-35.

[0087] Moreover, the characteristic of each glass was measured by the method shown below, and the measurement result is shown in Table 1-Table 4.

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
transition temperatureaaaaaaaaaa
densityaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to view more

Abstract

The invention provides optical glass with high refraction power and low chromatic dispersion. The optical glass comprises, by weight, 1 to 30% of B2O3, 0 to 20% of SiO2, 25 to 55% of La2O3, 5 to 40% of Gd2O3, 0 to 25% of Y2O3, 0 to 10% of Yb2O3, 0 to 10% of Ta2O5, 1 to 30% of Nb2O5, 0 to 10% of TiO2, 0.5 to 20% of ZrO2, 0 to 10% of WO3, 0 to 10% of Al2O3, 0 to 10% of GeO2 and 0 to 10% of Bi2O3. The optical glass does not contain ZnO and has a refractive index of 1.80 to 1.95 and an Abbe number of 33 to 45. The optical glass with excellent transmittance, high refraction power and low chromatic dispersion is obtained by reducing the content of Ta2O5 in the composition of the glass, introducing a proper amount of rare earth oxides with high refraction power and low chromatic dispersion and optimizing the ratio of the components.

Description

technical field [0001] The invention relates to an optical glass with high refractive index and low dispersion characteristics, as well as a glass preform and an optical element formed from the optical glass. Background technique [0002] Combining lenses made of high refractive index and low dispersion optical glass with lenses made of high refractive index and high dispersion optical glass can correct chromatic aberration and miniaturize the optical system, especially when the refractive index nd is 1.86-1.92 and the Abbe number νd is 36-42 high refractive index low dispersion optical glass, the market demand is increasing day by day. [0003] Japanese Patent Application No. 2001-348244, Patent Application No. 2007-269584, and Chinese CN101386469A all disclose this type of high-refraction and low-dispersion optical glass. In the examples of the description, optical glass components with a refractive index of 1.86 or more contain a large amount of Ta 2 o 5 , while Ta 2 o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/068C03C4/00
Inventor 孙伟
Owner CDGM OPTICAL GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap