Preparation method of oil based dual curable resin monomer

A technology for curing resin and grease, applied in the field of dual-curing resin monomers, can solve problems such as difficult application, and achieve the effects of energy saving, simple process flow and wide source of raw materials

Active Publication Date: 2017-04-05
南京林科众越新材料科技开发有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Technical problem to be solved: The purpose of this invention is to use the dual curing technology combined with UV curing and moisture curing to solve the problem of single UV curing on opaque materials, complex-shaped substrates, ultra-thick coatings and colored coatings. Due to the difficult application problem, the application field of UV curing technology has been expanded, and a preparation method of oil-based dual-curing resin monomer has been designed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of oil based dual curable resin monomer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Add the dimerized fatty acid into the reactor, raise the temperature to 70°C, then add glycidyl methacrylate into the reaction vessel according to the molar ratio of dimerized fatty acid to glycidyl methacrylate 1:2, and then add the Add 0.5% dodecyltrimethoxyammonium chloride and 0.1% 2,5-di-tert-butylhydroquinone to the total mass of the mixture, raise the temperature to 120° C. and keep stirring for 2.5 hours to obtain intermediate product A. Then, the intermediate product A and propyltrimethoxysilane isocyanate were added into the reactor at a molar ratio of 1:2, and reacted at 25° C. for 4 hours to obtain a UV-moisture dual-curable resin monomer.

Embodiment 2

[0021] Add citronic acid dibasic acid to the reactor, heat up to 80°C, then add glycidyl methacrylate into the reaction vessel according to the molar ratio of citric acid dibasic acid to glycidyl methacrylate 1:2 , and then add 0.1% octadecyldimethylbenzyl ammonium chloride and 0.5% hydroquinone, which account for the total mass of the above reactants, and heat up to 115° C. and continue to stir for 1.5 h to obtain intermediate product A. Then, the intermediate product A and propyltriethoxysilane isocyanate were added into the reactor at a molar ratio of 1:4, and reacted at 60°C for 2 hours to obtain a UV-moisture dual-curable resin monomer.

Embodiment 3

[0023] Add tung oil maleic acid into the reactor, heat up to 75°C, then add glycidyl methacrylate into the reaction vessel according to the molar ratio of tung oil maleic acid to glycidyl methacrylate 1:3, and then Add 1.0% octadecyl dimethyl hydroxyethyl ammonium perchlorate and 0.3% 2,5-di-tert-butylhydroquinone, which account for the total mass of the above reactants, heat up to 120°C and continue to stir for 2.0 hours , to obtain the intermediate product A. Then, the intermediate product A and propyltrimethoxysilane isocyanate were added into the reactor at a molar ratio of 1:3, and reacted at 30°C for 3.5 hours to obtain a UV-moisture dual-curable resin monomer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an oil based dual curable resin monomer. The specific method includes: subjecting a certain amount of oil polyacid, glycidyl methacrylate, a catalyst and a polymerization inhibitor to heating reaction to obtain an ultraviolet curable intermediate A, and then reacting the obtained intermediate A with isocyanate containing siloxane group, thus obtaining the ultraviolet curable and moisture curable oil based dual curable resin monomer. The oil based dual curable resin monomer prepared by the method provided by the invention can be used for dual curing in a way combining ultraviolet curing and moisture curing, and solves the difficult application problem of single ultraviolet curing between non-transparent materials, on complicatedly shaped substrates, in super-thick coatings and colored coatings, etc. At the same time, ultraviolet and moisture dual curing obtained by combining ultraviolet curing and moisture curing is a relatively hot dual curing technology in current research and development, and has a promoting effect for application of the dual curable resin monomer in other fields, also the used raw materials are all from renewable resources.

Description

technical field [0001] The invention belongs to the field of dual-curing resin monomers, in particular to a preparation method of grease-based dual-curing resin monomers. Background technique [0002] UV curing relies on ultraviolet light to stimulate the photoinitiator in the system to generate cations or free radicals, and the generated free radicals or cations can initiate polymerization reactions between various functional groups such as unsaturated double bonds and epoxy groups to form cross-linked polymers. Combined solidified structure. This technology is a brand-new green and environment-friendly new technology developed in the 1970s, because the ultraviolet light technology has low VOC emissions, and at the same time has a fast curing speed, saves energy, has little pollution, and has good comprehensive performance of the cured film. Solid this kind of technology has been widely used in coatings, aerospace, electronic packaging, electronics industry and many other ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F7/18
CPCC07F7/1804C07F7/1892
Inventor 夏建陵毛伟李守海黄坤李梅许利娜杨小华张燕
Owner 南京林科众越新材料科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com