A low-temperature far-infrared integrated electric heating soft porcelain decoration material and its preparation method

A decorative material, far-infrared technology, applied in the field of architectural decorative materials, can solve the problems of not being able to adjust the ambient temperature, not being able to realize the decorative effect of soft porcelain, and limited temperature adjustment, and achieve improved electrothermal conversion rate, good air permeability, and improved heat transmission. The effect of thermal efficiency

Active Publication Date: 2019-02-05
WUHAN WEIJUN IMPORT & EXPORT TRADE CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese Patent Announcement No. CN104277317A, the announcement date is January 14, 2015, and the name is "a preparation method of a phase-change temperature-regulating soft porcelain material", which discloses the preparation of a soft porcelain material with good thermal insulation properties The method is to introduce phase change microcapsules into the soft porcelain raw materials, and through the phase change of the material, the soft porcelain material prepared has good thermal insulation performance, and the temperature adjustment through the phase change material is limited, and it cannot achieve adjustment The effect of ambient temperature
Chinese Patent Announcement No. CN202787857U, dated March 13, 2013, titled 'A New Type of Infrared Radiation Electric Heating Ceramic Tile', discloses a ceramic tile with infrared radiation and electric heating function, which is obtained through the traditional ceramic tile substrate and the outer glaze layer. A conductor layer composed of non-metallic infrared conductive materials is arranged in between, and this traditional ceramic tile cannot realize the decorative function and function of soft porcelain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-temperature far-infrared integrated electric heating soft porcelain decoration material and its preparation method
  • A low-temperature far-infrared integrated electric heating soft porcelain decoration material and its preparation method
  • A low-temperature far-infrared integrated electric heating soft porcelain decoration material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A method for preparing a low-temperature and far-infrared integrated electric heating soft porcelain decorative material, comprising the following steps:

[0037] 1) Preparation of the soft porcelain layer: First weigh 15 parts of 300-mesh medical stone powder, 60 parts of 70-mesh quartz sand, 25 parts of 325 Portland white cement, 2 parts of anatase nano-titanium dioxide, 5 parts of flame retardant melamine and 2 parts of silane coupling agent KH-550 were placed in a kneader to stir and mix evenly to obtain a mixed powder; weigh 10 parts of silicon acrylic emulsion, 0.8 parts of hydrophobic agent SEAL 80 and 25 parts of water, Place in a stirred tank and mix evenly to obtain a mixed emulsion; then add the mixed powder into the stirred tank and stir thoroughly to obtain a mixed slurry, pour the slurry into a mold, and dry it for 4 hours at a temperature of 40°C to obtain Soft porcelain layer with a thickness of 2mm;

[0038] 2) Preparation of heat-conducting waterproof...

Embodiment 2

[0042] A method for preparing a low-temperature and far-infrared integrated electric heating soft porcelain decorative material, comprising the following steps:

[0043] 1) Preparation of the soft porcelain layer: First weigh 20 parts of 250-mesh medical stone powder, 50 parts of 90-mesh quartz sand, 30 parts of 425 Portland white cement, 4 parts of rutile nano-titanium dioxide, flame retardant 10 parts of amine polyphosphate and 1.5 parts of silane coupling agent KH-560 were placed in a kneader to stir and mix evenly to obtain a mixed powder; weigh 15 parts of silicon acrylic emulsion, 0.6 parts of hydrophobic agent PHOBE H-1022 and 20 parts of water Place in a stirring tank and mix evenly to obtain a mixed emulsion; then add the mixed powder into the stirring tank and stir thoroughly to obtain a mixed slurry, pour the slurry into a mold, and dry it for 4 hours at a temperature of 50°C , to obtain a soft porcelain layer with a thickness of 2.5mm;

[0044] 2) Preparation of t...

Embodiment 3

[0048] A method for preparing a low-temperature and far-infrared integrated electric heating soft porcelain decorative material, comprising the following steps:

[0049] 1) Preparation of the soft porcelain layer: first weigh 25 parts of 200-mesh medical stone powder, 55 parts of 100-mesh quartz sand, 20 parts of Portland white cement with a label of 525, 3.5 parts of anatase nano-titanium dioxide, 8 parts of flame retardant melamine ammonium polyphosphate and 1 part of silane coupling agent KH-570 were placed in a kneader to stir and mix evenly to obtain a mixed powder; weigh 20 parts of silicon acrylic emulsion, 0.3 parts of hydrophobic agent SEAL 80 and water 15 parts, placed in a stirred tank and mixed evenly to obtain a mixed emulsion; then the mixed powder was added to the stirred tank and stirred thoroughly to obtain a mixed slurry, which was poured into a mold and dried at a temperature of 60°C 3h, to obtain a soft porcelain layer with a thickness of 3mm;

[0050] 2) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building inner wall decorative materials and relates to a low-temperature far-infrared integral electric heating tender porcelain decorative material and a preparation method thereof. The low-temperature far-infrared integral electric heating tender porcelain decorative material is composed of a soft porcelain layer, a heat conductive waterproof layer, an electric heating layer and a heat preservation layer in sequence. The preparation method of the integral electric heating tender porcelain decorative material comprises the following steps that a silicone-acrylate emulsion, medical stone powder and cement and the like are prepared into slurry, and the slurry is poured into a mould, and after drying is conduced, the soft porcelain layer is obtained; then the surface of the soft porcelain layer is coated with waterborne polyurethane heat conductive insulating glue and conductive resin, and after drying is conducted in sequence, the heat conductive waterproof layer and the electric heating layer are obtained; and finally, a glass fabric is sufficiently immersed through waterborne polyurethane glue and covered on the electric heating layer, and after drying is conducted, the electric heating tender porcelain decorative material is obtained. The obtained electric heating tender porcelain decorative material has decorative and electric heating functions, has the properties of sterilization and bacteriostasis, releasing beneficial far infrared rays and being excellent in water and pollution resistance, and can work for a long time at the temperature ranging from minus 20 DEGC to 35 DEGC.

Description

technical field [0001] The invention belongs to the field of building decoration materials, and relates to a low-temperature and far-infrared integrated electric heating soft porcelain decoration material and a preparation method thereof. Background technique [0002] Soft porcelain is a new type of flexible surface decoration material, which is obtained by forming and processing water-based polymer emulsion and inorganic substances such as cement, soil, quartz sand or mineral powder. It is an ecological and environmentally friendly building material. The appearance of soft porcelain is similar to ceramics, but it lacks the cold, heavy and fragile texture of traditional ceramic materials. Low cost and convenient construction, it is suitable for architectural decoration such as exterior walls, interior walls and floors, which greatly enriches and beautifies people's living and working environments. [0003] With the development of technology, people have successively develop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/075E04F13/074B32B9/00B32B9/04B32B17/06B32B37/02B32B17/02C09D175/04C09D7/61C04B28/00C08L75/04C08K13/04C08K7/14
CPCB32B9/005B32B9/047B32B17/06B32B37/02B32B2037/243B32B2255/00B32B2255/26B32B2255/28B32B2260/021B32B2260/046B32B2262/101B32B2307/302B32B2307/7145B32B2307/758B32B2607/02C04B28/00C08K3/04C08K3/28C08K3/32C08K7/14C08K13/04C08K2003/282C08K2003/323C09D7/61C09D7/63C09D175/04E04F13/0875E04F13/142E04F2290/023E04F2290/04E04F2290/047C04B24/42C04B14/04C04B14/06C04B14/305C04B2103/63C04B2103/65C08L75/04
Inventor 王臻
Owner WUHAN WEIJUN IMPORT & EXPORT TRADE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com