Colored continuous-phase silicone-acrylic emulsion reactable with protective glue and preparation method thereof

A silicone-acrylic emulsion and protective glue technology, applied in the direction of coating, can solve the problems of water resistance white difference, water bubbling resistance, etc., and achieve the effect of saving cost, ensuring stability and excellent transparency

Active Publication Date: 2017-05-10
中山市巴德富化工科技有限公司
View PDF1 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This patented new type material for paints used in construction works solves problems associated with traditional materials like plaster boards due to their high volatile contents (VOC) released during manufacturing processes. Instead, this new material combines certain technical feates: 1), controllable pigment size without adding any extra ingredients, reducing waste and improving durability while maintaining good appearance properties, 2). Using an aqueous solution instead of conventional solutions containing harmful chemical substances, resulting in reduced pollution levels and improved safety standards compared to previous methods. 3） By combining different types of resin components together, these materials have better hiding power and wettabilty when applied over coatings made from various substrates.

Problems solved by technology

The technical issue addressed by this patented technology relates to developing an effective chemical solution used during coating processes where colored paints can form strong adhesion between different materials like glasses and plasterboards due to their unique properties such as high hydrophobicity and resistance against moisture penetration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment 1 A kind of colorful continuous phase silicon acrylic emulsion that reacts with protective colloid

[0038] The colorful continuous-phase silicon-acrylic emulsion is prepared from the following raw materials in parts by weight: 160 parts of water, 55 parts of methyl methacrylate, 60 parts of isooctyl acrylate, 10 parts of butyl acrylate, 1 part of acrylic acid, vinyltrimethylmethacrylate 1 part of oxysilane, 2 parts of methacryloxypropyltrimethoxysilane, 0.3 part of sodium dodecylsulfonate, 0.25 part of ammonium persulfate, 0.05 part of hydrogen peroxide, 0.05 part of sodium bisulfite

[0039] The preparation steps are as follows:

[0040] a1: Monomer mixing: under normal temperature and pressure, water, methyl methacrylate, isooctyl acrylate, butyl acrylate, acrylic acid, vinyltrimethoxysilane, methacryloxypropyltrimethoxysilane , sodium dodecylsulfonate, and ammonium persulfate are weighed in turn in an emulsification tank and stirred evenly to obtain a mi...

Embodiment 2

[0050] Embodiment 2 A kind of colorful continuous phase silicone acrylic emulsion reacted with protective colloid

[0051] The colorful continuous phase silicon-acrylic emulsion is prepared from the following raw materials in parts by weight: 130 parts of water, 90 parts of methyl methacrylate, 90 parts of isooctyl acrylate, 20 parts of butyl acrylate, 9 parts of methacrylic acid, ethylene 2 parts of trimethoxysilane, 5 parts of methacryloxypropyl trimethoxysilane, 2.5 parts of sodium dodecylbenzenesulfonate, 2 parts of sodium persulfate, 0.25 parts of hydrogen peroxide, sodium bisulfite 0.25 parts

[0052] The preparation steps are as follows:

[0053] a1: Monomer mixing: under normal temperature and pressure, water, methyl methacrylate, isooctyl acrylate, butyl acrylate, methacrylic acid, vinyltrimethoxysilane, methacryloxypropyltrimethoxy Base silane, sodium dodecylbenzenesulfonate, and sodium persulfate were weighed in turn into an emulsification tank and stirred evenly ...

Embodiment 3

[0063] Embodiment 3 A kind of colorful continuous phase silicon acrylic emulsion that reacts with protective colloid

[0064] The colorful continuous phase silicon-acrylic emulsion is prepared from the following raw materials in parts by weight: 180 parts of water, 70 parts of methyl methacrylate, 75 parts of isooctyl acrylate, 15 parts of butyl acrylate, 4 parts of itaconic acid, ethylene 2 parts of methyl trimethoxysilane, 3 parts of methacryloxypropyl trimethoxysilane, 1.0 parts of sodium lauryl sulfate, 1.0 parts of potassium persulfate, 0.1 parts of tert-butyl hydroperoxide, hanging white block 0.1 part

[0065] The preparation steps are as follows:

[0066] a1: Monomer mixing: under normal temperature and pressure, water, methyl methacrylate, isooctyl acrylate, butyl acrylate, itaconic acid, vinyl trimethoxysilane, methacryloxypropyl trimethoxy Base silane, sodium lauryl sulfate, and potassium persulfate were weighed in turn into an emulsification tank and stirred even...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Rotational viscosityaaaaaaaaaa
Rotational viscosityaaaaaaaaaa
Rotational viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses colored continuous-phase silicone-acrylic emulsion reactable with protective glue, prepared from, by weight, 130-180 parts of water, 50-90 parts of methyl methacrylate, 60-90 parts of 2-ethylhexyl acrylate, 10-20 parts of butyl acrylate, 0.5-9 parts of hydrophilic unsaturated organic acid, 3-7 parts of a functional monomer, 0.3-2.5 parts of an anionic emulsifier, 0.2-2 parts of an initiator, 0.05-0.25 part of an oxidant, and 0.05-0.25 part of a reducing agent; the prepared colored continuous-phase silicone-acrylic emulsion reactable with protective glue has excellent transparency, weatherability and paint formulating stability, can engage in directional crosslinking reaction with protective glue, and has excellent water resistance and water white resistance as no thickeners are added to the colored continuous phase.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner 中山市巴德富化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap