Multifunctional Coatings for Polyethylene Candy Wrap Films

A packaging film and polyethylene technology, applied in the field of coatings, can solve the problems of incomplete holographic effects, limited development, low production efficiency, etc., and achieve outstanding coating anti-counterfeiting effects, good coating adhesion fastness, and wide molding adaptability Effect

Active Publication Date: 2019-04-05
SHANGHAI WEIKAI CHEM +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Existing multi-functional coatings for polyethylene candy packaging materials are mainly oily two-component coatings. After coating by the coating machine, the coating film must be baked for a long time in the drying tunnel before the two components can fully react and dry. solidification, resulting in low overall production efficiency; at the same time, there are also relatively large defects in the subsequent molding process, and it is very easy for the coating layer to adhere to the nickel plate, thereby blocking the grating and causing incomplete holographic effects and other problems, so serious Limit its development in the field of polyethylene candy packaging materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional Coatings for Polyethylene Candy Wrap Films
  • Multifunctional Coatings for Polyethylene Candy Wrap Films
  • Multifunctional Coatings for Polyethylene Candy Wrap Films

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The multifunctional coating composition used for polyethylene candy packaging film of the present embodiment is prepared using the raw materials of the components and contents shown in Table 1; the specific preparation includes the following process steps:

[0031] (1) 40 kilograms of ethyl acetate and 20 kilograms of n-butyl acetate are dropped into the reactor, and the temperature is raised to 60° C.;

[0032] (2) 30 kilograms of non-reactive polyamide resins, 2.5 kilograms of glycidyl ether epoxy resins, 2.5 kilograms of glycidyl ester epoxy resins, and 4.9 kilograms of low-viscosity polyvinyl butyral resins are dropped into the reactor, Stir at high speed for 4.0 hours until fully dissolved;

[0033] (3) Add 0.1 kg of curing agent into the reaction kettle and stir until it is evenly dispersed.

[0034] The paint is directly coated on the coating machine, the leveling is good, the coating surface is flat, the molding temperature is 80-95 ℃, the molding effect is goo...

Embodiment 2

[0036] The multifunctional coating composition used for polyethylene candy packaging film of the present embodiment is prepared using the raw materials of the components and contents shown in Table 1; the specific preparation includes the following process steps:

[0037] (1) 20 kilograms of cyclohexanone, 40 kilograms of n-propyl acetate, and 10 kilograms of n-butanol are dropped into the reactor, and the temperature is raised to 55° C.;

[0038] (2) 6.0 kg of non-reactive polyamide resin, 4.0 kg of reactive polyamide resin, 2.0 kg of glycidyl ether epoxy resin, 4.0 kg of glycidyl ester epoxy resin, 2.0 kg of glycidyl amine epoxy resin , 9.0 kilograms of medium-viscosity polyvinyl butyral resin, 2.5 kilograms of low-viscosity polyvinyl butyral resin are put into the reaction kettle, stirred at high speed for 2.5 hours, until fully dissolved;

[0039] (3) Add 0.2 kg of leveling agent and 0.3 kg of curing agent into the reaction kettle in turn, and stir well until the dispersio...

Embodiment 3

[0042] The multifunctional coating composition used for polyethylene candy packaging film of the present embodiment is prepared using the raw materials of the components and contents shown in Table 1; the specific preparation includes the following process steps:

[0043] (1) 10 kilograms of cyclohexanone, 20 kilograms of ethyl acetate, 25 kilograms of n-propyl acetate, and 10 kilograms of n-butyl acetate are dropped into the reactor, and the temperature is raised to 60° C.;

[0044] (2) 8.2 kg of non-reactive polyamide resin, 8.2 kg of reactive polyamide resin, 3.2 kg of glycidyl ether epoxy resin, 1.6 kg of glycidyl ester epoxy resin, 1.6 kg of glycidyl amine epoxy resin , 8.0 kilograms of medium-viscosity polyvinyl butyral resin, 4.0 kilograms of low-viscosity polyvinyl butyral resin are put into the reaction kettle, stirred at high speed for 3.0 hours, until fully dissolved;

[0045] (3) Add 0.1 kg of smoothing agent and 0.1 kg of curing agent into the reaction kettle in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a multifunctional coating for a polyethylene candy packaging film. The multifunctional coating for the polyethylene candy packaging film is prepared from the following components in percentage by weight: 10 to 30 percent of polyamide resin, 5 to 8 percent of epoxy resin, 4 to 12 percent of polyvinyl butyral resin, 0.1 to 0.5 percent of accessory ingredient, and 60 to 70 percent of solvent. Compared with the prior art, the multifunctional coating for the polyethylene candy packaging film provided by the invention has the following beneficial effects that the coating is convenient to prepare, and is excellent in coating and levelling; the adhesion of a coating is good; the mould pressing adaptability is wide; an anti-fake effect of the coating is outstanding.

Description

technical field [0001] The invention relates to a coating, in particular to a multifunctional coating for polyethylene candy packaging film. Background technique [0002] With the continuous progress of society, packaging has developed from its birth to today. As a part of the commodity itself, its importance is obvious. Candy packaging plays a vital role in the storage, transportation, sales, and safety guarantee of candies. First of all, the barrier properties of the packaging can prevent the erosion of sunlight and air vapor, prevent the deliquescence and oxidation of the candy, and at the same time maintain the luster, flavor, shape, etc. that the candy should have; secondly, the advertising effect of the candy packaging plays an important role in the candy sales process. The role that cannot be underestimated, novel and unique packaging can attract the attention of consumers, stimulate the purchase desire of the target consumer group, and improve the sensory value of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D177/00C09D163/00C09D129/14C08J7/04C08L23/06
CPCC08J7/0427C08J2323/06C08J2429/14C08J2477/00C08L2205/025C08L2205/035C09D129/14C09D177/00C08L63/00C08L29/14C08L77/00
Inventor 虞明东韩莲
Owner SHANGHAI WEIKAI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com