Polishing solution for stainless steel processing

A technology of polishing liquid and stainless steel, which is applied in the field of polishing liquid, can solve problems affecting the quality and efficiency of processing, low processing efficiency, and affecting stainless steel processing, etc., to achieve good promotion and use value, high processing quality, and enhanced quality Effect

Active Publication Date: 2017-05-31
ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of processing stainless steel, the polishing process is one of the necessary processes, and the polishing liquid is one of the necessary substances in the polishing process, and its quality greatly affects the quality and efficiency of the processing. At present...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A polishing solution for stainless steel processing, made of the following materials in parts by weight:

[0020] 90 parts of deionized water, 5 parts of diamond, 3 parts of boron carbide, 2 parts of silicon carbide, 2 parts of zirconia, 1 part of lanthanum oxide, 1 part of scandium oxide, 1 part of hydrotalcite, 2 parts of diethanolamine, 1 part of pentaerythritol, 1 Parts 1,2-diethoxyethane, 1 part urotropine, 2 parts polyoxyethylene polyoxypropylene pentaerythritol ether, 1 part sodium dodecylbenzenesulfonate, 1 part cetyl sodium sulfate, 1.5 parts glycerin.

[0021] A preparation method of polishing liquid for stainless steel processing, comprising the steps of:

[0022] (1) First mix diamond, boron carbide and silicon carbide together to obtain mixture A for later use;

[0023] (2) Take 92% of the total mass of mixture A obtained in step (1), grind and pulverize it until the particle size is 1-3 μm, and make mixture B for later use;

[0024] (3) Mix the remainin...

Embodiment 2

[0031] A polishing solution for stainless steel processing, made of the following materials in parts by weight:

[0032] 95 parts of deionized water, 6 parts of diamond, 4 parts of boron carbide, 3 parts of silicon carbide, 3 parts of zirconia, 2 parts of lanthanum oxide, 1.5 parts of scandium oxide, 1.5 parts of hydrotalcite, 2.5 parts of diethanolamine, 1.5 parts of pentaerythritol, 1.5 parts Parts of 1,2-diethoxyethane, 2 parts of urotropine, 2.5 parts of polyoxyethylene polyoxypropylene pentaerythritol ether, 1.5 parts of sodium dodecylbenzenesulfonate, 1.5 parts of sodium cetyl sulfate, 2 parts glycerin. All the other method steps are the same as in Example 1.

Embodiment 3

[0034] A polishing solution for stainless steel processing, made of the following materials in parts by weight:

[0035] 100 parts of deionized water, 7 parts of diamond, 5 parts of boron carbide, 4 parts of silicon carbide, 4 parts of zirconia, 3 parts of lanthanum oxide, 2 parts of scandium oxide, 2 parts of hydrotalcite, 3 parts of diethanolamine, 2 parts of pentaerythritol, 2 parts Parts 1,2-diethoxyethane, 3 parts urotropine, 3 parts polyoxyethylene polyoxypropylene pentaerythritol ether, 2 parts sodium dodecylbenzenesulfonate, 2 parts sodium cetyl sulfate, 2.5 parts glycerin. All the other method steps are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polishing solution for stainless steel processing, and relates to a polishing solution. The polishing solution for stainless steel processing is specifically prepared from deionized water, diamond, boron carbide, silicon carbide, zirconium oxide, lanthanum oxide, scandium oxide, hydrotalcite, diethanol amine, pentaerythritol, 1,2-diethoxyethane, urotropin, polyoxyethylene poly-oxypropylene pentaerythrilol ether, sodium dodecyl benzene sulfonate, cetyl sodium sulfate and glycerol. The finally prepared polishing solution can complete polishing of stainless steel rapidly and efficiently, the processing quality is high and stable, the defective rate is decreased, and the polishing solution has good application and promotion value.

Description

technical field [0001] The invention relates to a polishing liquid, in particular to a polishing liquid for stainless steel processing. Background technique [0002] Stainless steel is one of the essential materials in modern people's life. It is widely used in indoor and outdoor decoration. For example, various mirror plates, embossed plates, and brushed plates are mostly made of stainless steel. In the process of processing stainless steel, the polishing process is one of the necessary processes, and the polishing liquid is one of the necessary substances in the polishing process, and its quality greatly affects the quality and efficiency of the processing. At present, most polishing liquids The unreasonable combination of ingredients in the stainless steel will cause irregular scratches in the polishing, and the phenomenon of waste products. At the same time, the processing efficiency is not high, which affects the overall processing of stainless steel. Contents of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F3/06
CPCC23F3/06
Inventor 洪功正潘永刚蔡永波
Owner ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap