Ultralow-hydrogen and high-tenacity metal powder core type seamless flux-cored welding wire for all-position welding
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A seamless flux-cored welding wire, ultra-low hydrogen technology, applied in the direction of welding medium, welding equipment, metal processing equipment, etc., can solve the problems of protection, welding wire can not use mixed gas, etc., to achieve good welding processability, stable mechanical properties, The effect of low diffusible hydrogen
Active Publication Date: 2017-06-27
725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
View PDF7 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The purpose of the present invention is to solve the problem that the existing welding wire cannot be protected by mixed g
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] Example 1: The drug core powder consists of 10% low-carbon ferromanganese, 20% atomized ferrosilicon, 3% rutile, 1% cryolite, 3% atomized nickel powder, 1% quartz, 2% feldspar, and the balance is iron pink. The filling rate is 16%, and the wire diameter is 1.2mm.
Embodiment 2
[0019] Example 2: The drug core powder consists of 15% low-carbon ferromanganese, 18% atomized ferrosilicon, 5% rutile, 1.5% cryolite, 2% atomized nickel powder, 1.5% quartz, 0.5% feldspar, and the balance is iron pink. The filling rate is 14%, and the wire diameter is 1.0mm.
Embodiment 3
[0020] Example 3: The drug core powder consists of 12% low-carbon ferromanganese, 15% atomized ferrosilicon, 2% rutile, 5% cryolite, 1% atomized nickel powder, 2% quartz, 1.5% feldspar, and the balance is iron pink. The filling rate is 17%, and the wire diameter is 1.6mm.
[0021] The preparation method of the metal powder-cored seamless flux-cored wire of the present invention is as follows: the sheath is made of ordinary low-carbon steel strip, and the chemical composition and properties are shown in Table 2 and Table 3. The chemical composition and mechanical properties of the welding wire deposited metal are shown in Table 4 and Table 5. The diffusible hydrogen content of deposited metal is shown in Table 6.
[0022] Table 1 The chemical composition (% by weight) of the metal powder cored seamless flux cored wire flux core powder of the embodiment of the present invention
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides an ultralow-hydrogen and high-tenacity metal powder core type seamless flux-cored welding wire for all-position welding. The seamless flux-cored welding wire comprises outer skin and flux core powder, wherein the inner part of the outer skin is filled with the flux core powder, and the outer skin is a low-carbon steel band. The seamless flux-cored welding wire is characterized in that the flux core powder comprises the following components in a percent by weight: 10-15% of low-carbon ferromanganese, 15-20% of atomized ferrosilicon, 2-5% of rutile, 1-5% of cryolite, 1-3% of atomized nickel powder, 1-2% of quartz, 0.5-2% of feldspar and the balance of iron powder. The seamless flux-cored welding wire is suitable for the all-position welding of carbon steel and low-alloy steel which are welded under the protection of mixed gas containing 75-85% of Ar and 15-25% of CO2. The seamless flux-cored welding wire is great in welding machinability, stable in mechanical properties, great in crack resistance, low in hydrogen dispersion and high in moisture absorbability and can be used for all-position welding.
Description
technical field [0001] The invention relates to the field of welding materials, in particular to an ultra-low-hydrogen high-toughness metal powder-cored seamless flux-cored welding wire for all-position welding. Background technique [0002] Metal powder flux-cored welding wire is a new trend in international development in recent years. At present, Japan and the United States have taken the less-slag-type metal powder flux-cored welding wire as one of the focuses of research and development. Metal powder type flux cored wire is relative to slag type flux cored wire, most of its flux core is metal powder (iron powder, deoxidizer), only a small amount of arc stabilizer and slagging agent. The reason why it is evaluated as "a welding material that replaces solid wire" is that it combines the advantages of a solid wire with less slag content with the advantages of a high deposition rate, excellent weld bead formation, and a low-spatter type flux-cored wire. , and the hydrogen ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): B23K35/12B23K35/368
CPCB23K35/0266B23K35/368
Inventor 郭纯李猛张学杰
Owner 725TH RES INST OF CHINA SHIPBUILDING INDAL CORP