Combined In3+ and Sn4+ donor doped ZnO varistor ceramic and preparation method thereof

A technology of donor doping and varistor ceramics, which is applied in varistors, overvoltage protection resistors, etc., can solve the problem of ZnO varistor aging life, the decline of pulse current tolerance performance indicators, and the inability to meet industrial applications. ZnO crystal To avoid problems such as lattice distortion, to achieve the effect of enhancing aging life, suppressing the decline of nonlinear coefficient, and suppressing the increase of leakage current

Active Publication Date: 2017-06-27
贵阳高新益舸电子有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the ion radius of Al is only 0.0535nm, and the ion radius of Zn is 0.074nm, the difference between the ion radii of the two is relatively large, and the formation of donor doping will lead to serious distortion of the ZnO lattice, which will inevitably lead to the aging life of ZnO varistors, pulse Performance indicators such as current tolerance have dropped significantly, which can no longer meet the needs of industrial applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined In3+ and Sn4+ donor doped ZnO varistor ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: a kind of In 3+ , Sn 4+ The ZnO varistor ceramic prepared by compound donor doping includes a base material and a dopant, and the base material includes ZnO: 90.5 parts, Bi 2 o 3 : 3.0 parts, MnO 2 : 0.5 parts, Sb 2 o 3 : 2.5 parts, Co 2 o 3 : 1 part, Cr 2 o 3 : 0.5 part, 2 parts of seed crystal dopant material, the mass fraction ratio of described seed crystal dopant material is ZnO:Sn(NO 3 ) 4 :In(NO 3 ) 3 =94:3:3.

Embodiment 2

[0027] Embodiment 2: a kind of In 3+ , Sn 4+ The ZnO varistor ceramic prepared by compound donor doping includes a base material and a dopant, and the base material includes ZnO: 87 parts, Bi 2 o 3 : 2.0 parts, MnO 2 : 0.4 parts, Sb 2 o 3 : 1.5 parts, Co 2 o 3 : 0.5 parts, Cr 2 o 3 : 0.2 parts, seed dopant: 1 part; the seed dopant is ZnO, SnO 2 and In 2 o 3 , whose mass fraction ratio is ZnO:SnO 2 :In 2 o 3 =90:0.1:0.1.

Embodiment 3

[0028] Embodiment 3: a kind of In 3+ , Sn 4+ The ZnO varistor ceramic prepared by compound donor doping includes a base material and a dopant material, and the base material includes ZnO: 95 parts, Bi 2 o 3 : 4.0 parts, MnO 2 : 0.7 parts, Sb 2 o 3 : 3.5 parts, Co 2 o 3 : 1.5 parts, Cr 2 o 3 : 1.0 parts, seed dopant: 5 parts; the seed dopant is ZnO, SnO 2 and In 2 o 3 , whose mass fraction ratio is ZnO:SnO 2 :In 2 o 3 =95:5:5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses combined In3+ and Sn4+ donor doped ZnO varistor ceramic and a preparation method thereof; the combined In3+ and Sn4+ donor doped ZnO varistor ceramic comprises a base material and a doping material, wherein the base material comprises, by weight, 87-95 parts of ZnO, 2.0-4.0 parts of Bi2O3, 0.4-0.7 part of MnO2, 1.5-3.5 parts of Sb2O3, 0.5-1.5 parts of Co2O3, 0.1-1.0 part of Cr2O3, and 1-5 parts of seed crystal doping material; the seed crystal doping material comprises ZnO, SnO2 and In2O3 having a mass ratio of (90-95):(0.1-5):(0.1-5). The combined In3+ and Sn4+ donor doped ZnO varistor ceramic has the advantages that ZnO grain resistivity can be decreased and ZnO lattice distortion can also be controlled, and also has the advantages of low final ZnO varistor residue, long ageing life and high pulse current tolerance.

Description

technical field [0001] The invention relates to a ZnO varistor ceramic and a preparation method thereof, in particular to an Al-free 3+ Doped In 3+ , Sn 4+ Composite donor-doped ZnO varistor ceramics and a preparation method thereof. Background technique [0002] ZnO varistor is made of ZnO as the main raw material, adding a small amount of Bi 2 o 3 、Co 3 o 4 , MnO 2 , Sb 2 o 3 、Cr 2 o 3 And other raw materials, prepared by ceramic sintering process. The varistor has the advantages of good nonlinearity and large flow capacity, and it has been widely used as a lightning surge protection component in electronic circuits and power systems. With the rapid development of microelectronic information technology, the requirements for miniaturization, integration and modularization of components are becoming more and more urgent. Miniaturized electronic components have high sensitivity and low overvoltage resistance level, which increases the demand for lightning protect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/453C04B35/626C04B35/634C04B35/638H01C7/12
CPCC04B35/453C04B35/62605C04B35/63416C04B35/638C04B2235/3241C04B2235/3267C04B2235/3275C04B2235/3284C04B2235/3286C04B2235/3293C04B2235/3294C04B2235/3298C04B2235/6567H01C7/12
Inventor 庞驰张宁方超周芳
Owner 贵阳高新益舸电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap