Porcelain containing rare earth elements and production process thereof

A rare earth element and porcelain technology, which is applied in the field of rare earth element-containing porcelain and its preparation, and achieves the effects of improving aesthetics, simple process and easy realization.

Inactive Publication Date: 2017-09-26
苏州瓷气时代净化设备有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But traditional porcelain can no longer meet people's needs, so a new type of porcelain is needed to replace it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of porcelain containing rare earth elements, the porcelain includes the following raw materials in parts by weight: rare earth mixture: 0.5 parts; clay: 28 parts; calcined kaolin: 10 parts; Suzhou soil: 15 parts; sepiolite: 1 part; wheat rice Stone: 3 parts; Manganese dioxide: 2 parts; Quartz sand: 3 parts.

Embodiment 2

[0020] A kind of porcelain containing rare earth elements, the porcelain includes the following raw materials in parts by weight: rare earth mixture: 1 part; clay: 30 parts; calcined kaolin: 12 parts; Suzhou soil: 11 parts; sepiolite: 1 part; wheat rice Stone: 3 parts; Manganese dioxide: 7 parts; Quartz sand: 6 parts.

Embodiment 3

[0022] A kind of porcelain containing rare earth elements, the porcelain includes the following raw materials in parts by weight: rare earth mixture: 1.5 parts; clay: 38 parts; calcined kaolin: 13 parts; Suzhou soil: 12 parts; sepiolite: 1.8 parts; Stone: 1.2 parts; Manganese dioxide: 5 parts; Quartz sand: 5.5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides porcelain containing rare earth elements. The porcelain is characterized by being produced by the following raw materials in parts by weight: 0.5-2.5 parts of a rare earth mixture, 28-40 parts of clay, 10-18 parts of calcined kaolin, 8-15 parts of Suzhou clay, 1-3 parts of sepiolite, 1-3 parts of medical stone, 1-7 parts of manganese dioxide and 3-8 parts of quartz sand. The rare earth mixture is added into the porcelain containing rare earth elements, so that the surface of the fired porcelain is more delicate and thorough; the overall appearance of the porcelain is improved; the process is simple and is easy to implement.

Description

technical field [0001] The invention relates to a rare earth element-containing porcelain and a preparation process thereof. Background technique [0002] Porcelain is a unique creation of the Chinese people and represents China's long-standing civilization with its unique national cultural characteristics. Nowadays, porcelain has penetrated into people's lives as a craft and daily necessities with high artistic value. But traditional porcelain can no longer meet people's needs, so a new type of porcelain is needed to replace it. Contents of the invention [0003] In order to solve the above-mentioned problems, the object of the present invention is to provide a kind of porcelain containing rare earth elements. The rare earth element-containing porcelain is added with a rare earth mixture, so that the surface of the fired porcelain is more delicate and transparent, and the overall aesthetics of the porcelain is improved, and the process is simple and easy to realize. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/34C04B41/86
CPCC04B33/13C04B33/34C04B41/009C04B41/5022C04B41/86C04B2235/3224C04B2235/3225C04B2235/3227C04B2235/3267C04B2235/3418C04B2235/3427C04B2235/5418C04B2235/6567
Inventor 闵海龙
Owner 苏州瓷气时代净化设备有限公司