A technology of absorbent cotton and high water absorption, applied in the field of medical devices, can solve the problems of unable to provide a moist environment for wounds, limited water absorption capacity of fibers, and unfavorable wound healing, etc., to achieve good overall easy removal, excellent biocompatibility, and promote wound healing. healing effect

Inactive Publication Date: 2017-10-17
TAICANG DONGNENG ENVIRONMENTAL PROTECTION EQUIP
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fibers in the existing medical absorbent cotton gauze generally have limited water absorption capacity and cannot provide a moist environment for t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of superabsorbent medical degreasing cotton gauze described in this embodiment is formed by blending seaweed fiber as warp yarn and cotton fiber as weft yarn, and the number of warp yarns per 100mm is 80 and the number of weft yarns per 100mm is 100. The seaweed fiber The weight ratio with cotton fiber is 0.4:1.

[0020] The preparation method of the super absorbent medical absorbent cotton gauze described in this embodiment:

[0021] 1) Preparation of seaweed fiber: Add sodium alginate to deionized water, stir at room temperature until completely dissolved, and obtain a sodium alginate solution with a mass percentage of 2.5, add nano-silver particles to the sodium alginate solution, stir evenly, and prepare Mix the spinning solution, the mass ratio of sodium alginate solution and nano-silver particles is 1:0.3; then use wet spinning technology to prepare seaweed fiber, stretch and wind after coagulation bath, the temperature of coagulation bath is 35 ℃, and let ...

Embodiment 2

[0027] A kind of superabsorbent medical absorbent cotton gauze described in this embodiment is formed by blending seaweed fiber and cotton fiber, and the number of warp yarns per 100mm is 80 and weft yarn is 100, and the weight ratio of the seaweed fiber and cotton fiber is It is 0.8:1.

[0028] The preparation method of the super absorbent medical absorbent cotton gauze described in this embodiment:

[0029] 1) Preparation of seaweed fiber: add sodium alginate to deionized water, stir at room temperature until it is completely dissolved to obtain a sodium alginate solution with a mass percentage of 3.5, add nano-silver particles to the sodium alginate solution, and stir evenly to prepare Mix the spinning solution, the mass ratio of sodium alginate solution and nano-silver particles is 1: 0.5; then use wet spinning technology to prepare seaweed fibers, stretch and wind after the coagulation bath, the temperature of the coagulation bath is 45 ℃, and let it dry naturally dry to...

Embodiment 3

[0035] A kind of superabsorbent medical degreasing cotton gauze described in this embodiment is formed by blending seaweed fiber and cotton fiber, and the number of warp yarns per 100mm is 72 and the number of weft yarns per 100mm is 120. The number of seaweed fibers and cotton fibers The weight ratio is 0.6:1.

[0036] The preparation method of the super absorbent medical absorbent cotton gauze described in this embodiment:

[0037] 1) Preparation of seaweed fiber: Add sodium alginate to deionized water, stir at room temperature until it is completely dissolved, and obtain a sodium alginate solution with a mass percentage of 3, add nano-silver particles to the sodium alginate solution, and stir evenly to prepare Mix the spinning solution, the mass ratio of sodium alginate solution to nano-silver particles is 1:0.4; then use wet spinning technology to prepare seaweed fibers, stretch and wind after coagulation bath, the temperature of coagulation bath is 40 ℃, and let it dry na...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of medical devices, in particular to a superabsorbent medical absorbent cotton gauze and a preparation method thereof. The highly water-absorbing medical absorbent cotton gauze of the present invention is formed by blending seaweed fibers and cotton fibers. The seaweed fibers have good softness, high comfort in use, good antibacterial effect, high hygroscopicity and gelation, and good overall ease of removal. , high oxygen permeability, excellent biocompatibility, and excellent biodegradation and absorption; after the seaweed fiber contacts with wound exudate or blood, it can exchange Na+/Ca2+ ions with the exudate, release Ca2+, and accelerate the coagulation process. Form a layer of stable mesh gel on the surface of the wound, create a microenvironment (slightly acidic, anaerobic or hypoxic, and moderately humid) for the wound that is conducive to tissue growth, and then promote wound healing; the preparation method is simple in process and mild in condition , low production cost, no pollution to the environment, and environmentally friendly.

Description

technical field [0001] The invention belongs to the technical field of medical devices, in particular to a superabsorbent medical absorbent cotton gauze and a preparation method thereof. Background technique [0002] Medical absorbent gauze and medical absorbent cotton are the main hygienic materials used in the medical industry for wound dressing, protection, and cleaning of patients. The gauze can promote wound healing of patients, and the gauze has soft texture, low price, wide sources, simple production and processing process, and can be repeated and practical. The fibers in the existing medical absorbent cotton gauze generally have limited water absorption capacity, which cannot provide a moist environment for the wound, which is not conducive to wound healing, and it is easy to cause secondary adhesion of the wound, and in severe cases, it will cause infection. Contents of the invention [0003] Purpose of the invention: In order to overcome the above problems, one ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D9/00D03D15/00D03D13/00D06B21/00D06M13/00D06M101/06D06M101/04
CPCD03D9/00D03D13/008D03D15/00D06B21/00D06M13/00D06M16/00D06M2101/04D06M2101/06D10B2101/00D10B2201/02D10B2509/026
Inventor 和晓刚
Owner TAICANG DONGNENG ENVIRONMENTAL PROTECTION EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap