A kind of preparation method of carbon-containing alumina carrier

A technology of alumina carrier and carbon alumina, applied in catalyst carrier, chemical instrument and method, metal/metal oxide/metal hydroxide catalyst, etc., can solve the problem of reducing pore volume and macropore content, and the interaction needs to be further Improvement, collapse, etc.

Active Publication Date: 2019-10-15
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the molding process of the alumina carrier, it is necessary to knead pseudo-boehmite dry rubber powder, extrusion aids, peptizers, etc. The macropores of the body itself partially collapse, so that the pore volume and macropore content of the final carrier are greatly reduced
In addition, the interaction between the alumina carrier and the active component prepared by the prior art needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of carbon-containing alumina carrier
  • A kind of preparation method of carbon-containing alumina carrier
  • A kind of preparation method of carbon-containing alumina carrier

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Weigh 200 g of pseudo-boehmite (produced by Shandong Aluminum Co., Ltd.) and place it in a beaker, add 400 mL of xylitol aqueous solution with a mass concentration of 25% to the beaker and soak for 4 hours. The impregnated material is filtered, and the filter cake is transferred to a high-pressure reactor for carbonization treatment at a temperature of 140°C and a treatment time of 10 hours. The treated pseudo-boehmite is fully mixed with 4g of scallop powder, and an appropriate amount of aqueous solution dissolved in 2g of acetic acid is added to the above materials, mixed evenly, and extruded into cylindrical strips. The molded wet material was dried at 110°C for 8 hours and calcined at 600°C for 8 hours to obtain an alumina carrier.

[0031] Weigh 100 grams of the above-mentioned γ-phase cylindrical strip-shaped alumina carrier and put it into the spray rolling pot, and in the rotating state, spray and impregnate 25 ml of xylitol aqueous solution with a mass concentr...

Embodiment 2

[0033] Same as Example 1, except that pseudo-boehmite was impregnated with a mixed aqueous solution of sorbitol and mannitol with a mass concentration of 40% and a mass ratio of 1:1 for 3 hours. The carbonization treatment temperature is 130°C, and the treatment time is 14 hours. The alumina carrier is in the shape of clover strips. For the first spray and impregnation, use 30ml of an aqueous solution of sorbitol with a mass concentration of 30%, and for the second spray and impregnation, use 50ml of an aqueous solution of sorbitol with a mass concentration of 10%. 20ml of sorbitol aqueous solution with a mass concentration of 5% was used for the first spraying and impregnation, the temperature during carbonization treatment was 200°C, and the carbonization time was 8 hours. The alumina carrier S2 of the present invention was obtained, and the properties of the carrier are shown in Table 1.

Embodiment 3

[0035] Same as Example 1, except that pseudoboehmite was impregnated for 5 hours with a mixed aqueous solution of glucose and ribose with a mass concentration of 30% and a mass ratio of 1:1. The carbonization treatment temperature is 120° C., and the carbonization treatment time is 16 hours. Adopt four times of spray impregnation, use 20ml mass concentration to be the aqueous solution of mannitol of 50% when spraying and impregnating for the first time, use 40ml mass concentration to be the aqueous solution of sorbitol of 30% when spraying and impregnating for the second time, the third time Use 20ml of an aqueous solution of sorbitol with a mass concentration of 20% for spray impregnation, and use 20ml of an aqueous solution of sorbitol with a mass concentration of 10% for the fourth spray and impregnation. During the carbonization treatment, the temperature was 240° C., and the carbonization time was 12 hours. The alumina carrier S3 of the present invention was obtained, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a carbon-containing alumina carrier, which includes the following contents: (1) Impregnating pseudo-boehmite dry glue powder with an aqueous solution containing polyols and / or sugar substances, and the impregnated material is subjected to hydrothermal treatment Carbonization treatment, the treated pseudo-boehmite is shaped, dried, and roasted to obtain an alumina carrier; (2) Prepare at least two polyol and / or monosaccharide aqueous solutions of different concentrations, in order of concentration from high to low Spray-impregnate the alumina carrier in step (1) so that the concentration of polyol and / or monosaccharide forms a gradient distribution from outside to in from low to high on the carrier; (3) Dip the alumina impregnated in step (2) The carrier is subjected to hydrothermal carbonization treatment in a sealed container and drying treatment to obtain the carbon-containing alumina carrier of the present invention. The alumina carrier prepared by this method has larger pore volume and pore diameter, and the carbon content is gradient distributed in the radial direction of the carrier. The carrier is suitable for the preparation of heavy and residual oil hydrogenation demetallization catalysts and other fields.

Description

technical field [0001] The invention relates to a preparation method of an alumina support, in particular to a preparation method of a carbon-containing alumina support. Background technique [0002] At present, in the production process of heavy oil hydrodemetallization, because the raw oil contains a certain amount of impurities such as vanadium, sulfur, arsenic, nickel, etc., it is easy to form deposits, thereby blocking the pores of the catalyst, resulting in a rapid decline in catalyst activity, and even Inactivation affects industrial applications. Catalysts with larger pore volume and larger pore diameter have strong metal and carbon storage capacity, which can slow down the deactivation of the catalyst and prolong the operation period of the catalyst. The pore structure of the catalyst is determined by the carrier that constitutes the catalyst. Therefore, the preparation of a carrier with a larger pore volume and larger pore diameter is an important step in the prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J32/00B01J21/18B01J21/04B01J23/883
CPCB01J21/04B01J21/18B01J23/002B01J23/883B01J2523/00B01J35/635B01J35/647B01J35/615B01J2523/31B01J2523/68B01J2523/847
Inventor 佟佳吕振辉
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com