Modified polyurethane acrylic resin and preparation method thereof
A polyurethane acrylic and acrylic technology, applied in the direction of adhesive additives, non-polymer adhesive additives, etc., can solve the problems of water resistance, poor impact resistance, poor weather resistance, yellowing resistance, poor durability, etc., to achieve weather resistance. The effect of improved performance, good impact resistance and high water resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0055] Example 1:
[0056] A method for preparing modified polyurethane acrylic resin, comprising the following steps:
[0057] 1) 13.3 grams of isophorone diisocyanate, 0.08 grams of hydroquinone and 0.04 grams of stannous octoate were added to the reactor, heated to 60°C and stirred evenly;
[0058] 2) Add 8 grams of 4,4'-(1-methylene)-bicyclohexanol, heat to 70°C and stir evenly until the isocyanate mass percentage is 11.9±0.05%;
[0059] 3) Add 0.05 gram of antioxidant 1135, .02 gram of Tinuvin517 and 6.7 gram of acrylic acid-β-hydroxypropyl ester in turn, and heat to 80° C. to stir and react completely;
[0060] 4) Add 33.3 grams of polyester diol with hydroxyl value of 56 (model is Daicel Placcel 220), continue to react for 4 hours at a temperature of 80 ° C, until the NCO group content in the sample tracking test system is taken out, when it is When the mass percentage is less than 0.05%, the reaction reaches the end point;
[0061] 5) Add 27.1 grams of tetrahydrofuran...
Example Embodiment
[0062] Example 2:
[0063] 1) 9 grams of hexamethylene diisocyanate, 0.1 grams of p-hydroxyanisole and 0.04 grams of 0.08 grams of dibutyltin dilaurate were added to the reactor, heated to 60°C and stirred evenly;
[0064] 2) Add 8 grams of 4,4'-(1-methylethylene)-bicyclohexanol, heat to 70°C and stir evenly, until the detected isocyanate mass percentage is 13.5±0.05%;
[0065] 3) Add 0.05 gram of Irganox5057, 0.03 gram of Tinuvin328 and 4 gram of methacrylic acid-β-hydroxyethyl ester successively, and heat to 80° C. to stir and react completely;
[0066] 4) Add 26 grams of polyester diol with a hydroxyl value of 56 (the model is Daicel Placcel CD220PL), and continue to react for 4 hours at a temperature of 80 ° C until the sample is taken out to track the NCO group content in the test system. When the mass percentage is less than 0.05%, the reaction reaches the end point;
[0067] 5) Add 17.7 grams of isobornyl acrylate and 21.2 grams of isodecyl acrylate to reduce viscosit...
Example Embodiment
[0068] Example 3:
[0069] 1) 15.3 grams of isophorone diisocyanate, 0.07 grams of p-tert-butylcatechol and 0.06 grams of dibutyltin dilaurate were added to the reactor, heated to 68°C and stirred evenly;
[0070] 2) Add 8 grams of 4,4'-(1-methylene)-bicyclohexanol, heat to 70°C and stir evenly until the isocyanate mass percentage is 12.2±0.05% and the reaction is complete;
[0071] 3) Add 0.05 g of 2,6-di-tert-butyl-p-cresol, 0.02 g of Tinuvin 213 and 6 g of acrylic acid-β-hydroxypropyl ester in turn, heat to 70° C. to stir and react for 3 hours;
[0072] 4) Add 20 grams of polyester diol with a hydroxyl value of 112 (the model is Daicel Placcel 210), and continue the reaction at a temperature of 80 ° C until the sample is taken out to track the NCO group content in the test system. When the fractional content is less than 0.05%, the reaction reaches the end point;
[0073] 5) Add 20.4 grams of isodecyl acrylate and 16.3 grams of neopentyl glycol diacrylate to reduce viscos...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap