Polyester resin for high filling mark covering powder paint and preparation method thereof
A polyester resin and powder coating technology, applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of increased equipment loss, prolonged process, increased maintenance requirements, etc., to prevent oxidation side reactions and achieve excellent surface performance. , the effect of increasing the conversion rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example 1:
[0040] A polyester resin for high filling and shading powder coatings is made with the following parts by weight:
[0041]
[0042] Among them, the branching agent is trimethylolpropane. The esterification catalyst is a mixture of dibutyltin oxide and monobutyltin oxide, and the mass ratio of the two is 1:1.5. The curing accelerator is a mixture of tetrabutylammonium chloride and ethyltriphenylphosphonium bromide, and the mass ratio of the two is 1:1. The antioxidant is a mixture of antioxidant 3114 and antioxidant 168, and the mass ratio of the two is 2:1.
[0043] The preparation method of the above-mentioned polyester resin for high filling and shading powder coatings, the specific steps are as follows:
[0044] (1) Add neopentyl glycol, pentaerythritol, 1,4-cyclohexanedicarboxylic acid, branching agent and esterification catalyst to the reactor containing the water-containing agent in sequence, continue to pass nitrogen, and heat to 240°C. Stir the reaction ...
Example Embodiment
[0052] Example 2:
[0053] A polyester resin for high filling and shading powder coatings is made with the following parts by weight:
[0054]
[0055] Among them, the branching agent is trimethylolethane. The esterification catalyst is a mixture of dibutyltin oxide and monobutyltin oxide, and the mass ratio of the two is 1:1.5. The curing accelerator is a mixture of tetrabutylammonium chloride and ethyltriphenylphosphonium bromide, and the mass ratio of the two is 1:1. The antioxidant is a mixture of antioxidant 3114 and antioxidant 168, and the mass ratio of the two is 2:1.
[0056] The preparation method of the above-mentioned polyester resin for high filling and shading powder coatings, the specific steps are as follows:
[0057] (1) Add neopentyl glycol, pentaerythritol, 1,4-cyclohexanedicarboxylic acid, branching agent and esterification catalyst to the reactor containing the water-containing agent in sequence, continue to pass nitrogen, and heat to 250°C. Stir the reaction u...
Example Embodiment
[0065] Example 3:
[0066] A polyester resin for high filling and shading powder coatings is made with the following parts by weight:
[0067]
[0068] Among them, the branching agent is pentaerythritol. The esterification catalyst is a mixture of dibutyltin oxide and monobutyltin oxide, and the mass ratio of the two is 1:1.5. The curing accelerator is a mixture of tetrabutylammonium chloride and ethyltriphenylphosphonium bromide, and the mass ratio of the two is 1:1. The antioxidant is a mixture of antioxidant 3114 and antioxidant 168, and the mass ratio of the two is 2:1.
[0069] The preparation method of the above-mentioned polyester resin for high filling and shading powder coatings, the specific steps are as follows:
[0070] (1) Add neopentyl glycol, pentaerythritol, 1,4-cyclohexanedicarboxylic acid, branching agent, and esterification catalyst to the reactor containing the water agent in sequence, continue to pass nitrogen, and heat to 250°C. Stir the reaction until the rea...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap