Preparation method of organic silicon modified high-molecular cement grinding aid
A technology of cement grinding aids and polymers, which is applied in the field of preparation of organosilicon-modified polymer cement grinding aids, which can solve the problems of ineffective grinding aids, reduce water interfacial tension, promote lubrication, and accelerate cracks extended effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] Take 100g of sodium lignosulfonate, add 200mL of deionized water, stir at 300r / min for 20min, then add 120g of diethanolamine, disperse by 200W ultrasonic for 20min, and heat to 70℃, then add 270g mass fraction dropwise at 3g / min It is a 37% formaldehyde solution. After 2 hours of incubation and reaction, it is transferred to a rotary evaporator for distillation under reduced pressure for 3 hours, and then 500 mL of absolute ethanol is added. After standing for 20 minutes, the filter residue is filtered and the filter residue is placed in a drying box for 6 hours to obtain modified wood. Sodium sulfonate, take 150g allyl glycidyl ether, 120g end hydrogen-containing silicone oil, stir at 300r / min for 20min, then add 5g 0.1% chloroplatinic acid isopropanol solution dropwise at 0.1g / min, and Heat to 80℃, continue to stir and react for 4h to obtain the reaction solution, take 150g of modified sodium lignosulfonate and 80g glacial acetic acid into the reactio...
Example Embodiment
[0023] Example 2
[0024] Take 150g of sodium lignosulfonate, add 300mL of deionized water, stir at 350r / min for 25min, then add 180g of diethanolamine, disperse with 200W ultrasonic for 25min, and heat to 75℃, then add 400g mass fraction dropwise at 4g / min It is a 37% formaldehyde solution. After the reaction is kept for 3 hours, it is transferred to a rotary evaporator for distillation under reduced pressure for 4 hours, and then 650 mL of absolute ethanol is added. After standing for 25 minutes, the filter residue is filtered and the filter residue is placed in a drying box for 7 hours to obtain modified wood. Sodium sulfonate, take 165g allyl glycidyl ether, 135g end hydrogen-containing silicone oil, stir at 350r / min for 25min, and then add dropwise 7g 0.1% chloroplatinic acid isopropanol solution at 0.2g / min, and Heat to 85°C, continue to stir and react for 4h to obtain the reaction solution. Take 195g of modified sodium lignosulfonate and 90g glacial acetic acid into the re...
Example Embodiment
[0025] Example 3
[0026] Take 200g of sodium lignosulfonate, add 400mL of deionized water, stir at 400r / min for 30min, then add 240g of diethanolamine, disperse by 200W ultrasonic for 30min, and heat to 80℃, then add 540g mass fraction dropwise at 5g / min It is a 37% formaldehyde solution. After the reaction is kept for 3 hours, it is transferred to the rotary evaporator for vacuum distillation for 5 hours, then 800 mL of absolute ethanol is added, and the filter residue is filtered after standing for 30 minutes. The filter residue is placed in a drying box for 8 hours to obtain modified wood Sodium sulfonate, take 180g allyl glycidyl ether, 150g end hydrogen-containing silicone oil, stir at 400r / min for 30min, then add 8g 0.1% chloroplatinic acid isopropanol solution dropwise at 0.3g / min, and Heat to 90℃, continue to stir and react for 5h to obtain the reaction solution. Take 240g of modified sodium lignosulfonate and 100g of glacial acetic acid into the reaction solution, stir ...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap