Nanometer combined solution capable of generating negative oxygen ions, ceramic, and preparation method of nanometer combined solution

A technology of negative oxygen ions and combined liquid, applied in the field of architectural ceramics, can solve the problems of long production cycle, large environmental pollution and high cost, and achieve the effects of improving utilization rate, reducing energy consumption and stable quality

Inactive Publication Date: 2018-07-06
王贵锋 +1
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this technology is that the production cycle is long; the second is high energy consumption, high loss, and hig

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nanometer combined solution capable of generating negative oxygen ions, ceramic, and preparation method of nanometer combined solution
  • Nanometer combined solution capable of generating negative oxygen ions, ceramic, and preparation method of nanometer combined solution
  • Nanometer combined solution capable of generating negative oxygen ions, ceramic, and preparation method of nanometer combined solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Table 1

[0050]

[0051] ① The balance of the combined components of the nanocomposite liquid in Table 1 is water.

[0052] The nano-combination liquid in the above table is prepared according to the following preparation method:

[0053] a. Weigh 500 g of silicon powder and grind it into a powder with a particle size of 10-20 μm, then add enough water to prepare a 25% aqueous solution, add 5.8 g of suspending agent, and stir at high speed to make the silicon powder The powder is evenly suspended in water to form a milky white translucent glue, that is, to form a penetrating fluid. After testing, the pH value is 9-10, the specific gravity is 1.17, the Baume degree is 21, and the appearance is milky white translucent glue. This formula should be stored indoors at a temperature of 0-40°C, and it will be stable for one year.

[0054]b. Grind 500g of tourmaline into 2000-4000mesh fine powder with air, add it into water at room temperature, the dispersion mass ratio i...

Embodiment 2

[0057] Table 2

[0058]

[0059] a. Weigh 500 g of silicon powder and grind it into a powder with a particle size of 1-10 μm, then add enough water to prepare a 25% aqueous solution, add 5.8 g of suspending agent, and stir at high speed to make the silicon powder The powder is evenly suspended in water to form a milky white translucent glue, that is, to form a penetrating fluid. After testing, the pH value is 9-10, the specific gravity is 1.17, the Baume degree is 21, and the appearance is milky white translucent glue. This formula should be stored indoors at a temperature of 0-40°C, and it will be stable for one year.

[0060] b. Grind 500g of tourmaline into 4000-6000 mesh micropowder by jet mill, add it into water at normal temperature, the dispersion mass ratio is 15%, add 6.5g of sodium carboxymethyl cellulose with a content of 0.2%, and grind to 13g of thorium-containing compound activator micropowder with a particle size of 2000-4000 was stirred in a high-speed mix...

Embodiment 3

[0063] table 3

[0064]

[0065] a. Weigh 500 g of silicon powder and grind it into a powder with a particle size of 30-50 μm, then add enough water to prepare a 25% aqueous solution, add 5.8 g of suspending agent, and stir at high speed to make the silicon powder The powder is evenly suspended in water to form a milky white translucent glue, that is, to form a penetrating fluid. After testing, the pH value is 9-10, the specific gravity is 1.17, the Baume degree is 21, and the appearance is milky white translucent glue. This formula should be stored indoors at a temperature of 0-40°C, and it will be stable for one year.

[0066] b. Grind 500g of tourmaline into 6000-10000 mesh micropowder by jet mill, add it into water at normal temperature, the dispersion mass ratio is 15%, add 6.5g of sodium carboxymethyl cellulose with a content of 0.2%, and grind to 13g of thorium-containing compound activator micropowder with a particle size of 2000-4000 was stirred in a high-speed m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nanometer combined solution capable of generating negative oxygen ions. The nanometer combined solution capable of generating negative oxygen ions comprises a penetrating fluid, a negative ion liquid, and a sealing liquid which are prepared independently, wherein the penetrating fluid is prepared from, by mass 10 to 50% of nanometer silica, 2 to 10% of a suspending agent,and the balance water, the negative ion liquid is prepared from, by mass, 5 to 50% of tourmalinite, 0.1 to 1% of sodium carboxymethylcellulose, 0.1 to 3% of an activator, and the balance water; and the sealing liquid is prepared from, by mass, 1 to 30% of organic silicone oil, and the balance water. Compared with conventional products, the nanometer combined solution possesses following advantages: the penetrating fluid of relatively large particles are capable of penetrating relatively pores on ceramic surface, in dispersion of the negative ion liquid, the penetrating liquid can be taken asa carrier of the negative ion liquid, the contact area of tourmalinite surface with the air is enlarged effectively, and more negative oxygen ions are generated.

Description

technical field [0001] The invention relates to the field of architectural ceramics, in particular to a nano-composite liquid for generating negative oxygen ions, ceramics and a preparation method thereof. Background technique [0002] With the development of science, human beings are increasingly enjoying the benefits brought by science and technology, and people are more inclined to human-friendly home life. Under the premise that people's health requirements are increasing day by day, the building ceramics industry, which is closely related to people's livelihood, has made adjustments and started more research on embedding "healthy elements" in materials. [0003] Tourmaline is a general term for various tourmaline minerals, and it is a ring-shaped silicate mineral with complex composition, characterized by boron. Tourmaline is a crystal with piezoelectric effect and pyroelectric effect. In recent years, research has found that tourmaline can not only be used as a prospe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/89
CPCC04B41/52C04B41/89C04B41/5035C04B41/4539C04B41/5007C04B41/4535C04B41/4961
Inventor 王贵锋周国庆
Owner 王贵锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com