Environment-friendly non-stick pan surface treatment process

Abstract

The invention discloses an environment-friendly non-stick pan surface treatment process. The treatment process comprises the following steps of 1), molding to form a microporous layer; 2), using a laser for scanning on the surface of a pan blank to form a plurality of microporous structures to obtain the microporous layer; 3), spraying a non-stick coating on the surface of the microporous layer, wherein the microporous structures are filled with the non-stick coating. The treatment process adopts a laser micro-porous forming technology for scanning the surface of the pan blank to form the dense and slender microporous structures to obtain the microporous layer, so that the superficial area of the pan blank is increased by folds, the microscopic roughness of the surface of the pan blank isimproved, when the non-stick coating is directly sprayed on the surface of the microporous layer, the microporous structures are filled with the coating to greatly increase the contact area between the non-stick coating and the microporous layer to improve the adhesion of the non-stick coating.

Description

Technical field [0001] The invention belongs to the technical field of cookware manufacturing, and particularly relates to an environmentally-friendly non-stick pan surface treatment process. Background technique [0002] At present, spraying pot blanks in the pot industry basically use surface sandblasting or shot blasting to increase the surface roughness of the pot blanks to improve the adhesion of the surface non-stick coating. [0003] Sandblasting and shot blasting both increase the surface roughness of the pot body by deforming the surface of the pot body. Figure 4 Is a partial cross-sectional schematic diagram of a non-stick pan after sandblasting (non-stick coating is not shown), Figure 5 The partial cross-sectional schematic diagram of the non-stick pan after shot blasting (non-stick coating is not shown), from Figure 4 with Figure 5 It can be seen that although the surface of the pot blank has obvious concave and convex parts under the action of deformation, if the non-...

AI Technical Summary

Problems solved by technology

[0003] Both sandblasting and shot blasting increase the roughness of the surface of the pan by deforming the surface of the pan. Figure 4 It is a partial cross-sectional schematic diagram of a non-stick pan after sandblasting (non-stick coating is not shown), Figure 5 It is a partial cross-sectional schematic diagram of a non-stick pan after shot blasting (non-stick coating is not shown), from Figure 4 and Figure 5 It can be seen from the figure that although the surface of the pan has obvious concave and convex parts under the action of deformation, if the

Images