Epoxy resin anticorrosive coating and preparation method thereof

An anti-corrosion coating and epoxy resin technology, applied in the field of coatings, can solve problems such as personal safety hazards, accidents and personal injuries, and achieve effective anti-corrosion protection, prolong service life, and good shielding protection

Inactive Publication Date: 2018-08-03
DONGGUAN JIAQIAN NEW MATERIAL TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal corrosion not only brings huge economic losses to people, but also indirectly causes many accidents and personal injuries, and is also a hidden danger to people's personal safety.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin anticorrosive coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of epoxy resin anticorrosion coating, by weight, comprises following component:

[0024] 100 parts of water-based epoxy resin emulsion, nano CeO 2 20 parts, 12 parts of zinc phosphate, 15 parts of cellulose acetate butyrate, 4 parts of sodium polyacrylate, 3 parts of sodium silicate, 1 part of silane coupling agent, 3 parts of triethylenetetramine, 2 parts of polyethylene wax, phthalate 1 part of dioctyl diformate, 6 parts of amine antifouling agent, 7 parts of montmorillonite, 1 part of SD-202, 12 parts of phenolic resin, 30 parts of water.

[0025] A preparation method for epoxy resin anticorrosion paint, comprising the following steps:

[0026] (1) Dissolve sodium polyacrylate, sodium silicate, and silane coupling agent in water, stir and mix evenly, heat to 50°C, add nano-CeO 2 After ultrasonic dispersion for 3 hours, add water-based epoxy resin emulsion, stir and disperse at a speed of 700rpm for 1 hour to obtain a mixed solution;

[0027] (2) Add trieth...

Embodiment 2

[0029] A kind of epoxy resin anticorrosion coating, by weight, comprises following component:

[0030] 100 parts of water-based epoxy resin emulsion, nano CeO 2 30 parts, 19 parts of zinc phosphate, 18 parts of cellulose acetate butyrate, 8 parts of sodium polyacrylate, 5 parts of sodium silicate, 2 parts of silane coupling agent, 6 parts of triethylenetetramine, 5 parts of polyethylene wax, phthalate 2 parts of dioctyl diformate, 8 parts of amine antifouling agent, 9 parts of montmorillonite, 3 parts of SD-202, 25 parts of phenolic resin, 40 parts of water.

[0031] A preparation method for epoxy resin anticorrosion paint, comprising the following steps:

[0032] (1) Dissolve sodium polyacrylate, sodium silicate, and silane coupling agent in water, stir and mix evenly, heat to 70°C, add nano-CeO 2 After ultrasonic dispersion for 4 hours, add water-based epoxy resin emulsion, stir and disperse at a speed of 900rpm for 2 hours to obtain a mixed solution;

[0033] (2) Add tr...

Embodiment 3

[0035] A kind of epoxy resin anticorrosion coating, by weight, comprises following component:

[0036] 100 parts of water-based epoxy resin emulsion, nano CeO 2 20 parts, 19 parts of zinc phosphate, 15 parts of cellulose acetate butyrate, 8 parts of sodium polyacrylate, 3 parts of sodium silicate, 2 parts of silane coupling agent, 3 parts of triethylenetetramine, 5 parts of polyethylene wax, phthalate 1 part of dioctyl diformate, 8 parts of amine antifouling agent, 7 parts of montmorillonite, 3 parts of SD-202, 12 parts of phenolic resin, 40 parts of water.

[0037] A preparation method for epoxy resin anticorrosion paint, comprising the following steps:

[0038] (1) Dissolve sodium polyacrylate, sodium silicate, and silane coupling agent in water, stir and mix evenly, heat to 50°C, add nano-CeO 2 After ultrasonic dispersion for 4 hours, add water-based epoxy resin emulsion, stir and disperse at a speed of 700rpm for 2 hours to obtain a mixed solution;

[0039] (2) Add tri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an epoxy resin anticorrosive coating comprising the following components in parts by weight: 100 parts of a waterborne epoxy emulsion, 20-30 parts of nano CeO2, 12-19 parts ofzinc phosphate, 15-18 parts of cellulose acetate butyrate, 4-8 parts of sodium polyacrylate, 3-5 parts of sodium silicate, 1-2 parts of a silane coupling agent, 3-6 parts of a curing agent, 2-5 partsof an antisettling agent, 1-2 parts of a plasticizer, 6-8 parts of an antifouling agent, 7-9 parts of a filler, 1-3 parts of a defoaming agent, 12-25 parts of phenolic resin, and 30-40 parts of water.The invention also discloses a preparation method of the epoxy resin anticorrosive coating. The epoxy resin anticorrosive coating has excellent anticorrosive performance, good film forming property and high adhesion force, and can provide effective anticorrosive protection for metals.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an epoxy resin anticorrosion coating and a preparation method thereof. Background technique [0002] The phenomenon of self-damage or deterioration caused by the chemical reaction or electrochemical reaction between metal and its surrounding environment is called corrosion, and the phenomenon of metal damage caused by physical, biological and mechanical factors is also collectively called corrosion. The mechanism of metal corrosion is mainly four types: physical corrosion, chemical corrosion, electrochemical corrosion and microbial corrosion. According to relevant statistics, the annual economic loss caused by metal corrosion in the world is about 6 times the sum of economic losses caused by natural disasters such as earthquakes, floods, and typhoons, which is a great economic waste. Metal corrosion not only brings huge economic losses to people, but also indirectly causes many accidents...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D101/14C09D161/06C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2003/2213C08K2003/328C08K2201/011C08L2205/035C09D5/08C09D163/00C09D7/61C09D7/63C09D7/65C08L1/14C08L33/02C08L61/06C08K13/02C08K3/22C08K3/32C08K3/34C08K5/54C08K3/346
Inventor 王海燕
Owner DONGGUAN JIAQIAN NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap