Polyvinyl chloride co-extrusion foaming furniture board and manufacturing method thereof

A polyvinyl chloride and furniture board technology, applied in chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems of uneven plasticizers, increase production difficulty, and complex formula composition, and achieve reduction Product density and production cost, the effect of improving skin toughness and improving scratch resistance

Active Publication Date: 2018-08-10
SHANDONG HUIFENG NEW MATERIAL TECH CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing formula is relatively complicated, and two or three stabilizers are usually used in combination, and the stabilizing effect is not good
The plasticizers added are also good and bad, both solid and liquid, which increases the difficulty of production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The polyvinyl chloride co-extruded foamed furniture board is composed of a core layer and a surface layer, and the core layer is composed of the following raw materials in parts by weight:

[0028] 60 parts of polyvinyl chloride SG8 resin, 45 parts of heavy calcium, 35 parts of recycled materials, 5 parts of foam regulator P90, 2.8 parts of calcium zinc stabilizer, 0.5 parts of internal lubricant SP-60, micronized polyethylene wax N- 0.1 part of 14P, 0.4 part of plasticizer OA9, 0.5 part of exothermic AC foaming agent, 1.0 part of endothermic NS-603 foaming agent, 0.25 part of blue light brightener, 1 part of rutile;

[0029] The surface layer is composed of the following raw materials in parts by weight:

[0030] 60 parts of polyvinyl chloride SG7 type resin, 20 parts of heavy calcium powder, 20 parts of recycled material, 2 parts of foaming regulator P90, 2.8 parts of calcium zinc stabilizer, 0.5 part of internal lubricant sp-60, PTFE modified polyethylene wax 0.2 pa...

Embodiment 2

[0036] The polyvinyl chloride co-extruded foamed furniture board consists of a core layer and a surface layer,

[0037] The core layer is made up of the following raw materials in parts by weight:

[0038] 70 parts of polyvinyl chloride SG8 resin, 52 parts of heavy calcium, 40 parts of recycled materials, 5.5 parts of foam regulator P90, 3 parts of calcium zinc stabilizer, 0.55 parts of internal lubricant SP-60, micronized polyethylene wax N- 0.2 parts of 14P, 0.45 parts of plasticizer OA9, 0.55 parts of exothermic AC foaming agent, 1.1 parts of endothermic NS-603 foaming agent, 0.25 parts of blue light brightener, and 1.1 parts of rutile.

[0039] The surface layer is composed of the following raw materials in parts by weight:

[0040] 70 parts of polyvinyl chloride SG7 resin, 25 parts of heavy calcium powder, 25 parts of recycled materials, 2 parts of foam regulator P90, 2.9 parts of calcium zinc stabilizer, 0.55 parts of internal lubricant sp-60, PTFE modified polyethylene...

Embodiment 3

[0046] The polyvinyl chloride co-extruded foamed furniture board consists of a core layer and a surface layer,

[0047] The core layer is made up of the following raw materials in parts by weight:

[0048] 80 parts of polyvinyl chloride SG8 resin, 60 parts of heavy calcium, 50 parts of recycled materials, 6 parts of foam regulator P90, 3.2 parts of calcium zinc stabilizer, 0.6 parts of internal lubricant SP-60, micronized polyethylene wax N- 0.25 parts of 14P, 0.5 parts of plasticizer OA9, 0.6 parts of exothermic AC foaming agent, 1.3 parts of endothermic NS-603 foaming agent, 0.25 parts of blue light brightener, 1.5 parts of rutile;

[0049] The surface layer is composed of the following raw materials in parts by weight:

[0050] 80 parts of polyvinyl chloride SG7 type resin, 30 parts of heavy calcium powder, 30 parts of recycled material, 2 parts of foam regulator P90, 3.0 parts of calcium zinc stabilizer, 0.6 part of internal lubricant sp-60, PTFE modified polyethylene wax...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyvinyl chloride co-extrusion foaming furniture board and a manufacturing method thereof, belongs to the technical field of polyvinyl chloride boards, and aims at solving the problems of high density, low hardness and toughness, and rough surface of the conventional product. The polyvinyl chloride co-extrusion foaming furniture board comprises a core layer and a surfacelayer, wherein the core layer comprises 60-80 parts of polyvinyl chloride SG8 type resin, 45-60 parts of triple superphosphate, 35-50 parts of recovery material, 5-6 parts of foaming conditioner P, 2.8-3.2 parts of a calcium-zinc stabilizer, 0.5-0.6 parts of an inner lubricating agent SP-60, 0.1-0.25 part of micronized polyethylene wax N-14P, 0.4-0.5 part of a plasticizer OA, a foaming agent anda pigment. The method comprises the following steps: preheating a heat mixing pot; sequentially adding chloroethylene resin, recovery material, calcium powder and the lubricating agent in sequence; heating; sequentially adding the foaming agent, the foaming conditioner and the rest materials; heating; cooling; extruding the materials to obtain the finished product through an extruder. The method is carried out to manufacture the furniture board.

Description

technical field [0001] The invention relates to a polyvinyl chloride co-extruded foamed furniture board and a preparation method thereof, belonging to the technical field of polyvinyl chloride boards. Background technique [0002] In recent years, the country has vigorously advocated the development of energy-saving and low-consumption products. Plastic formwork is an energy-saving and environmentally friendly product. Therefore, the promotion and application of plastic formwork is a way to save resources and save energy. important measures. Among them, the polyvinyl chloride foam material has the processing properties of sawing, nailing, planing, and sticking, and is waterproof, fireproof, insect-proof, alkali-resistant, anti-corrosion, sound-proof, and has good stability and weather resistance. And other characteristics, has been well developed, widely used in furniture boards, building boards, advertising boards and so on. [0003] For low-density and thinner polyvinyl ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08L27/18C08L23/28C08K3/26C08K5/103C08J9/10B32B27/06B32B27/18B32B27/30
CPCB32B27/08B32B27/18B32B27/304C08J9/0023C08J9/0061C08J9/0066C08J9/0095C08J9/103C08J2203/04C08J2327/06C08J2423/06C08J2423/28C08J2427/06C08J2427/18
Inventor 段培彩林立东高炳坤丁峰刘娜
Owner SHANDONG HUIFENG NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap