Underwear bra pad containing chitin sponge and preparation method thereof

A chitin and underwear technology, applied in underwear, baby underwear, bras and other directions, can solve problems such as poor bra performance, achieve a strong sense of modernity, promote cell metabolism, and prevent cell aging.

Inactive Publication Date: 2018-08-17
杨彪
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Most of the sponge production adopts a one-step box-type foaming method. Various raw materials are quickly added to the forming box under high-speed stirring, and chain growth, foaming, cross-linking, and curing reactions are completed in the forming box, thereby completing sponge production. However, the performance of bras with sponges as underwear pads is generally poor, and the uniqueness of existing underwear mold cups is a breeding ground for bacteria, so chitin sponge is very suitable for underwear mold cups

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In the embodiment of the present invention, a kind of underwear chest pad containing chitin sponge, its raw material comprises the following components by weight: 100 parts of toluene diisocyanate, 10 parts of diisocyanate, 0.5 part of polymerization catalyst, 0.5 part of flame retardant, 0.5 parts of foaming agent, 10 parts of chitin powder, 120 parts of polyether polyol, several parts of water.

[0024] The polymerization catalyst is stannous octoate.

[0025] The polyether polyol is polyether propylene glycol.

[0026] A kind of preparation method of the underwear breast pad containing chitin sponge, its concrete steps are as follows:

[0027] (1) fully mixing toluene diisocyanate, diisocyanate, polymerization catalyst, flame retardant, blowing agent, chitin powder, polyether polyol and water to obtain a solution mixture;

[0028] (2) The solution mixture is stirred at high speed for 30-45 seconds, the mixing speed is 900r / min, and the temperature control equipment...

Embodiment 2

[0032] In the embodiment of the present invention, a kind of underwear chest pad containing chitin sponge, its raw material comprises the following components by weight: 110 parts of toluene diisocyanate, 20 parts of diisocyanate, 0.6 part of polymerization catalyst, 5 parts of flame retardant, 5 parts of foaming agent, 20 parts of chitin powder, 130 parts of polyether polyol, several parts of water.

[0033] The polymerization catalyst is stannous octoate.

[0034] The polyether polyol is polyether propylene glycol.

[0035] A kind of preparation method of the underwear breast pad containing chitin sponge, its concrete steps are as follows:

[0036] (1) fully mixing toluene diisocyanate, diisocyanate, polymerization catalyst, flame retardant, blowing agent, chitin powder, polyether polyol and water to obtain a solution mixture;

[0037] (2) The solution mixture is stirred at high speed for 30-45 seconds, the mixing speed is 1000r / min, and the temperature control equipment i...

Embodiment 3

[0041] In the embodiment of the present invention, a kind of underwear chest pad containing chitin sponge, its raw material comprises the following components by weight: 120 parts of toluene diisocyanate, 30 parts of diisocyanate, 0.7 parts of polymerization catalyst, 8 parts of flame retardant, 8 parts of foaming agent, 30 parts of chitin powder, 150 parts of polyether polyol, several parts of water.

[0042] The polymerization catalyst is stannous octoate.

[0043] The polyether polyol is polyether propylene glycol.

[0044] A kind of preparation method of the underwear breast pad containing chitin sponge, its concrete steps are as follows:

[0045] (1) fully mixing toluene diisocyanate, diisocyanate, polymerization catalyst, flame retardant, blowing agent, chitin powder, polyether polyol and water to obtain a solution mixture;

[0046] (2) The solution mixture is stirred at high speed for 30-45 seconds, the mixing speed is 800r / min, and the temperature control equipment i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an underwear chest pad containing a chitin sponge and a preparation method thereof. The raw material comprises the following components by weight: 100 to 150 parts of toluene diisocyanate, 10 to 30 parts of diisocyanate, 0.5-0.8 part of a polymerization catalyst, 0.5 to 8 parts of a flame retardant, 0.5 to 8 parts of a foaming agent, 10 to 30 parts of chitin powder, 120 to150 parts of polyether polyol, and several parts of water. The chitin powder is added to sponge production, so that the sponge contains chitin, the chitin has no repulsive force on cells, has the effect of repairing the cells, and can alleviate allergic skin. At the same time, the chitin has anti-oxidation ability, can activate the cells, prevents cell aging, and promotes cell metabolism, the chitin has a natural bacteriostatic effect and a very-high broad spectrum antibacterial rate, more than 90% of common bacteria cannot survive on chitin fiber, the uniqueness of underwear mold cups is thatthe underwear mold cups are hotbeds for easy breeding of bacteria, and the chitin sponge is very suitable for the underwear mold cups, and thus providing a safety line for female chests.

Description

technical field [0001] The invention relates to the field of underwear brass pads, in particular to an underwear brass pad containing chitin sponge and a preparation method thereof. Background technique [0002] Sponge is a kind of polyurethane foam, which belongs to soft polyurethane foam. Because of the porous honeycomb structure, it has excellent softness, elasticity, water absorption and water resistance, and is widely used in sofas, mattresses, underwear, clothing, flexible packaging and other industries. [0003] Chitin also contains high-efficiency moisturizing ingredients, and its β-glucan can also effectively moisturize the skin. At room temperature, every 100 grams of chitin powder can absorb 200-225 grams of 40wt% sodium hydroxide solution, of which water absorption is About 100 grams. The adsorption value of chitin is related to the concentration of alkali solution and the adsorption temperature. At zero temperature, for 20-30wt% sodium hydroxide solution, eve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/76C08G18/72C08G18/48C08G18/64C08G18/24C08J9/04A41B17/00A41C3/14A41C1/06C08G101/00
CPCA41B17/00A41B2400/34A41C1/06A41C3/144C08G18/244C08G18/4081C08G18/4825C08G18/6484C08G18/721C08G18/7614C08G2101/00C08J9/04C08J2375/08C08J2475/04
Inventor 杨彪
Owner 杨彪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products