Production method of Fumantianxia gourd bottle Jun porcelain artware
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and technology of gourd bottle, applied in decorative arts, manufacturing tools, clay products, etc., can solve the problems of easy cracking, low treasure rate, etc., and achieve the effects of high yield, uniform glaze color distribution, and beautiful handicrafts.
Inactive Publication Date: 2018-09-07
禹州市晋家钧窑有限公司
View PDF5 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
A large number of gourd vases are fired, and the shape of the utensils also changes. The key to gourd vase Jun porcelain is the enamel. The color change of the enamel after glaze firing determines the value of Jun porcelain. Very easy to crack, resulting in low treasure rate
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] Such as figure 1 Shown, a kind of making method of Fumantianxia gourd vase Jun porcelain handicraft, comprises the following steps:
[0022] Step 1. Select pottery clay; the pottery clay includes the following components: 50 parts of kaolin, 5 parts of alkaline earth, 3 parts of quartz stone, 8 parts of sandstone, 8 parts of lead powder, 8 parts of mullite, and 1 part of iron ore;
[0023] Step 2, practice mud; first coarsely crush the clay into sand or powder, then grind it, add water and mix it into a mud ball;
[0024] Step 3, drawing the billet; drawing the mud ball into a green body, the green body is gourd-shaped;
[0025] Step 4, mold making; carve the models of the dragon head, small ring, lion head and big ring respectively, and make plaster molds for the carved models;
[0026] Step 5, grouting molding; the pottery clay in step 1 is first roughly crushed into sand or powder, and then ground to a fineness of 230 mesh, mixed with water and ball milled to make ...
Embodiment 2
[0033] A method for making Fumantianxia gourd vase Jun porcelain handicraft, comprising the following steps:
[0034] Step 1. Select pottery clay; the pottery clay includes the following components: 65 parts of kaolin, 10 parts of alkaline earth, 5 parts of quartz stone, 12 parts of sandstone, 10 parts of lead powder, 10 parts of mullite, and 2 parts of iron ore;
[0035] Step 2, practice mud; first coarsely crush the clay into sand or powder, then grind it, add water and mix it into a mud ball;
[0036] Step 3, drawing the billet; drawing the mud ball into a green body, the green body is gourd-shaped;
[0037] Step 4, mold making; carve the models of the dragon head, small ring, lion head and big ring respectively, and make plaster molds for the carved models;
[0038] Step 5, grouting molding; the pottery clay in step 1 is first roughly crushed into sand or powder, and then ground to a fineness of 250 mesh, mixed with water and ball milled to make a slurry; then the slurry ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a production method of Fumantianxia gourdbottle Jun porcelain artware. The production method comprises the following steps: (1) selecting argil; (2) refining mud; (3) drawinga blank: drawing a mud pie into a gourd-shaped blank body; (4) preparing a mold: respectively carving models of a dragon head, a small round ring, a lion head and a big round ring, and respectively producing plaster molds by virtue of the carved models; (5) carrying out slip casting; (6) drying: drying the trimmed blank body at room temperature, wherein the water content of the dried blank body isless than 3%; (7) carrying out biscuiting; (8) carrying out glazing; and (9) sintering: after glazing in the step (8), carrying out edulcoration on the surface of the biscuited blank body, applying aground coat to the surface of the biscuited blank body, carrying out glazing, and drying, wherein the bottom of the biscuited blank body is not glazed. The production method has the beneficial effects that the blank-glaze combination performance is good, the yield of Jun porcelain finished products is high, and the creativity and art effect of the product of the invention can be well embodied.
Description
technical field [0001] The invention relates to the field of Jun porcelain crafts, in particular to a method for making a Fumantianxia gourdvase Jun porcelain handicraft. Background technique [0002] Jun Porcelain is known as the first of my country's "Five Famous Porcelains". It is a specialty of Yuzhou City, Henan Province. , out of the kiln and other unique features, which cannot be achieved and compared with other ceramic handicrafts. Since the Tang Dynasty, the bottle shaped like a gourd has been loved by the people because of its homonym "Fulu", and has become a traditional shape. The name "Daji bottle" means good luck. A large number of gourd vases are fired, and the shape of the utensils also changes. The key to gourd vase Jun porcelain is the enamel. The color change of the enamel after glaze firing determines the value of Jun porcelain. It is very easy to crack, resulting in a low treasure rate. Contents of the invention [0003] In view of this, the present...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More