Stretchable conductor sheet, stretchable conductor sheet having adhesiveness, and method for forming wiring line formed of stretchable conductor on fabric

一种伸缩性、导体片的技术，应用在绝缘载体上的导电层、粘合剂加热的粘合方法、导电图案形成等方向，能够解决不易对齐位置、衣服丧失柔软性等问题，达到容易操作、确保可见性、准确位置对准的效果

Active Publication Date: 2018-10-23
TOYOBO CO LTD
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In Patent Document 4, a smooth plane filled and cured with resin is made in advance on the plane containing the lines and the gaps between the lines on a part of the electronic cloth or electronic clothing material to improve printability, but excessive filling and curing will lead to clothing Loss of flexibility, insufficient filling and solidification will make it difficult to align the position, and there are situations where it is difficult to take care of both

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stretchable conductor sheet, stretchable conductor sheet having adhesiveness, and method for forming wiring line formed of stretchable conductor on fabric
  • Stretchable conductor sheet, stretchable conductor sheet having adhesiveness, and method for forming wiring line formed of stretchable conductor on fabric
  • Stretchable conductor sheet, stretchable conductor sheet having adhesiveness, and method for forming wiring line formed of stretchable conductor on fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0104] The following examples show the present invention in detail and specifically. In addition, the evaluation results etc. in the Example were measured by the following method.

[0105]

[0106] Based on the composition ratio obtained by NMR analysis of the obtained resin material, it is converted into mass% based on the monomer mass ratio.

[0107]

[0108] The measurement was performed using the SMV-300RT "Mooney Viscometer" manufactured by Shimadzu Corporation.

[0109]

[0110] The measurement was performed using a light scattering particle size distribution measuring device LB-500 manufactured by Horiba Manufacturing Co., Ltd.

[0111]

[0112] For resin materials and paste-like materials, each material is applied to the release sheet in an amount to reach a dry thickness of 100±10μm, dried and cured under predetermined conditions, and then stamped into ISO 527 together with the release sheet -Dumbbell shape specified in 2-1A, as a sample piece. For sheet-like materials, the...

manufacture example 1

[0126]

[0127] Add to the stainless steel reaction vessel equipped with a mixer and a water cooling jacket:

[0128]

[0129] Keep the temperature of the water bath at 15°C under nitrogen flow and stir gently. Then, an aqueous solution of 0.3 parts by mass of potassium persulfate dissolved in 19.7 parts by mass of deionized water was dropped over 30 minutes, and after the reaction was continued for another 20 hours, 0.5 parts by mass of hydroquinone dissolved in 19.5 parts by mass of deionized water was added. In the aqueous solution, the polymerization is stopped.

[0130] Then, in order to distill off the unreacted monomer, first, the pressure in the reaction vessel is reduced, steam is further introduced, and the unreacted monomer is recovered to obtain a synthetic rubber latex (L1) composed of NBR.

[0131] Add salt and dilute sulfuric acid to the obtained latex, perform coagulation / filtration, and repeat the re-dispersion and filtration of the resin in the deionized water in 5...

manufacture example 2

[0133] Except that 40 parts by mass of styrene and 60 parts by mass of butadiene were used instead of acrylonitrile and butadiene of Production Example 1, the same operations were performed to obtain synthetic rubber resin R02. Synthetic rubber resin R02 has a nitrile group content of 0% by mass, a Mooney viscosity of 67, and an elastic modulus of 51 MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

To provide a stretchable conductor sheet which is useful as a material for electrical wiring lines and electrodes for wearable electronic devices, said material having excellent durability in terms ofwashing and durability in terms of perspiration. A fabric provided with an electrode and an electrical wiring line, which are formed from a stretchable conductor sheet, is obtained by: providing a film having mold releasability with a first stretchable conductor layer which is formed from a paste material that uses carbon-based particles as a conductive filler, while using a flexible resin as a binder resin; subsequently forming a second stretchable conductor layer, while using metal-based particles as a conductive filler; laminating a hot melt adhesive layer thereon; superposing the resulting laminate on a fabric after removing unnecessary parts from the laminate by means of partial slits; and subjecting the resulting fabric to hot pressing. Since the carbon-based particles adsorb a contamination substance of the metal-based particles, oxidation degradation and sulfuration degradation of the metal-based particles is reduced, thereby improving the durability.

Description

Technical field [0001] The present invention relates to a sheet-like stretchable conductor sheet that can be laminated on a stretchable base material, and a method for forming electrical wiring used in clothing-type electronic devices and the like using these. Background technique [0002] In recent years, wearable electronic devices have been developed that aim to enable electronic devices with input and output, computing, and communication functions to be used in close proximity or in close contact with the body. As wearable electronic devices, there are known accessory-type devices such as watches, glasses, and earphones, and textile-integrated clothing-type electronic devices in which electronic functions are assembled on clothing. [0003] Electronic equipment requires electrical wiring for power supply or signal transmission. Especially for textile-integrated wearable electronic devices with stretchable clothes, the electrical wiring is also required to be stretchable. Gene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/22C09J7/30C09J201/00H01B1/24H05K1/09H05K3/12H05K3/20C09J7/29C09J7/35
CPCC09J201/00H01B1/22H01B1/24C09J2400/266C09J2301/41C09J7/29C09J2301/304C09J2203/358C08K3/04C09J2421/006C09J5/06C08K2201/001C08K2003/0806H05K3/025H05K1/0283H05K2201/0314H05K2201/0323H05K2203/0156H05K3/281H05K2201/0133H05K2201/0108C09J7/35C09J7/405C09J2301/408C09J9/02C09J2203/326H01B5/14H05K3/20B32B27/12
Inventor 权义哲石丸园子入江达彦米仓弘伦森本翔太
Owner TOYOBO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap