A waste polyethylene, impact strength technology, applied in the direction of chemical modification of natural resin, etc., can solve the problems of unsatisfactory market demand, poor impact strength, etc., and achieve the effect of improving bonding effect, improving wear resistance, and reducing holes

Inactive Publication Date: 2018-11-20
JIESHOU HUAYUAN PLASTIC PROD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To sum up, the regeneration of waste polyethylene has important social and economic significance, but the existing waste polyethylene reuse production and processing products have poor impact strength and cannot meet market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A modified waste polyethylene with good impact strength, made of the following components in parts by weight: oxidized sodium alginate modified rosin resin 25, inorganic filler 18, polyethylene terephthalate 3, lubricant 0.3, plasticizer 1.0, coupling agent 1.6, waste polyethylene 88.

[0019] Further, the preparation method of the oxidized sodium alginate modified rosin resin is:

[0020] Using rosin resin as the matrix, oxidized sodium alginate as the modifier, and peroxide as the catalyst, reacted at 172°C for 2 hours according to the mass ratio of rosin resin and oxidized sodium alginate of 80:1.3, then cooled and pulverized, Sieve to get.

[0021] Further, the peroxide is lauroyl peroxide.

[0022] Further, sodium alginate was added to absolute ethanol at a ratio of 50g: 300mL, stirred at a speed of 3000r / min for 40min to obtain a suspension, and then 0.18mol / L sodium periodate of 30% of its mass was added to the suspension Solution, heated to 50°C, stirred at 1...

Embodiment 2

[0030] A modified waste polyethylene with good impact strength, made of the following components in parts by weight: sodium alginate oxidized modified rosin resin 28, inorganic filler 22, polyethylene terephthalate 6, lubricant 0.6, plasticizer 1.3, coupling agent 2.2, waste polyethylene 95.

[0031] Further, the preparation method of the oxidized sodium alginate modified rosin resin is:

[0032] Using rosin resin as the matrix, oxidized sodium alginate as the modifier, and peroxide as the catalyst, react at 175°C for 2 hours according to the mass ratio of rosin resin and oxidized sodium alginate of 80:1.5, then cool and pulverize, Sieve to get.

[0033] Further, the peroxide is lauroyl peroxide.

[0034] Further, sodium alginate was added to absolute ethanol at a ratio of 80g: 300mL, stirred at a speed of 3000r / min for 40min to obtain a suspension, and then 0.18mol / L sodium periodate of 30% of its mass was added to the suspension Solution, heated to 50°C, stirred at 1500r / ...

Embodiment 3

[0042] A modified waste polyethylene with good impact strength, made of the following components in parts by weight: oxidized sodium alginate modified rosin resin 26, inorganic filler 20, polyethylene terephthalate 5, lubricant 0.4, plasticizer 1.2, coupling agent 1.8, waste polyethylene 92.

[0043] Further, the preparation method of the oxidized sodium alginate modified rosin resin is:

[0044] Using rosin resin as the matrix, oxidized sodium alginate as the modifier, and peroxide as the catalyst, react at 173°C for 2 hours according to the mass ratio of rosin resin and oxidized sodium alginate of 80:1.4, then cool and pulverize, Sieve to get.

[0045] Further, the peroxide is lauroyl peroxide.

[0046] Further, sodium alginate was added to absolute ethanol at a ratio of 60g: 300mL, stirred at a speed of 3000r / min for 40min to obtain a suspension, and then 0.18mol / L sodium periodate of 30% of its mass was added to the suspension Solution, heated to 50°C, stirred at 1500r / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modified waste polyethylene having good impact strength. The polyethylene is prepared from, by weight, 25-28 parts of oxidized sodium alginate modified rosin resin, 18-22 parts of an inorganic filling material, 3-6 parts of polydiethylene terephthalate, 0.3-0.6 part of a lubricant, 1.0-1.3 parts of a plasticizer, 1.6-2.2 parts of a coupling agent, and 88-95 parts of wastepolyethylene. The polyethylene has good impact strength and good wear resistance.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a modified waste polyethylene with good impact strength. Background technique [0002] With the rapid development of the plastics industry, polyethylene, as a general-purpose plastic, is widely used in daily necessities, construction, automobile manufacturing and other fields. However, with the expansion of polyethylene application fields and the increase in usage, waste polyethylene is also increasing day by day. Due to the aging and degradation of waste polyethylene, its physical properties are far inferior to that of virgin polyethylene, and its application is also greatly limited, and can only be used to make low-performance products. If it is not applied, it will waste resources and cause great pollution to the environment. The recycling of waste polyethylene is conducive to the sustainable development of the plastics industry. To sum up, the regeneratio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L93/04C08L67/02C08K13/02C08K3/34C08K5/12C09F1/04C08B37/04
CPCC08B37/0084C08L23/06C08L2205/03C08L2205/24C08L2207/20C09F1/04C08L93/04C08L67/02C08K13/02C08K3/34C08K5/12
Inventor 朱同义
Owner JIESHOU HUAYUAN PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap