Method of separating feldspar and quartz from granite materials

A granite and stone technology, applied in chemical instruments and methods, magnetic separation, solid separation, etc., can solve problems such as failure to achieve separation and purification, waste of resources, environmental hazards, etc., to improve identification and resolution, improve effect, Guaranteed effect of purity

Active Publication Date: 2018-12-18
内蒙古华宸再生资源科技有限公司
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Different types of granite are mainly feldspar and quartz mineral rocks. Thousands of granite stone processing enterprises in China will produce a large amount of waste and mined blocks during the mining and processing process. The tailings and blocks are Existence, causing serious pollution to the environment, although the chemical composition of these granite wastes is mainly potassium, albite, quartz, black mica, but due to the K in the granite waste 2 O, Na 2 O grade is low, and the harmful component Fe 2 o 3 、TiO 2 Therefore, it cannot be directly used in ceramic glazes and blanks instead of feldspar, and a small amount of granite ore with good quality can only be added to low-end ceramic blanks, making a large amount of granite waste unreasonable. processing, resulting in a waste of resources
At present, the existing domestic granite separation feldspar and quartz purification technology is mainly flotation process, but there are a large number of harmful chemicals and harmful substances in the flotation process, causing great harm to the environment, and from the separation results From the point of view, the grades of K and Na have been improved by 1-2 percentage points, and the effect of separation and purification cannot be achieved at all. Therefore, there is an urgent need for a method that can improve the grades of K and Na and is environmentally friendly. Feldspar and Quartz Method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of separating feldspar and quartz from granite materials
  • Method of separating feldspar and quartz from granite materials
  • Method of separating feldspar and quartz from granite materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Take the granite in Ulanqab City, Inner Mongolia (such as figure 1 (shown) is the separation object, separate the feldspar and quartz from the granite, and send samples of the granite to Wuhan University of Technology, Foshan Youbo Ceramics Testing Center, Tangshan Ceramics Testing Center, Shenyang Longji Magnetoelectric Co., Ltd. Laboratory, Changsha Hong Shun Mining Co., Ltd. and other testing, comprehensive analysis is as follows, in terms of mass percentage, the granite contains Al 2 o 3 : 14.6%-17.86%, SiO 2 : 73.08%-78.02%, Fe 2 o 3 : 0.90%-1.47%, CaO: 0.78%-1.22%, MgO: 0.05%-0.10%, K 2 O: 4.72%-5.24%, Na 2 O: 3.45%-3.55%, TiO 2 : 0.02%-1.22%. The granite is calcined at 1200°C (such as figure 2 Shown) after milling, its whiteness is 4.9-11.3. The feldspar and quartz in the yellow granite are separated by the following method:

[0033] (1) Ore crushing: crushing the granite rock into material blocks with a particle size less than or equal to 400mm;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method of separating feldspar and quartz from granite materials, and belongs to the technical field of separation and mineral beneficiation. The method comprises the steps of an ore breakage working procedure, an ore grinding working procedure, a screening working procedure, a photoelectric color sorting working procedure, a powder milling working procedure and a magnetic separation working procedure. The feldspar, the quartz and magnetic materials in granite are thoroughly separated by use of the physical technology, no any waste gas or waste water or other substances which pollute the environment are generated in the process of operation, and the damage caused by the floatation technology in the prior art to the environment is effectively avoided. In addition,the feldspar which is separated and purified by use of the method and the quartz which is separated and purified by use of the method can be applied to the ceramic industry instead of natural feldsparand natural quartz, the source of raw materials in the method is sufficient, and the method is suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of separation and beneficiation, and in particular relates to a method for separating feldspar and quartz from granite rock. Background technique [0002] Potassium albite feldspar, due to its low melting point between 1100-1300°C, has good chemical stability, and has a melting effect when co-melted with quartz and silicate, and reacts to form low-melting glass substances, which can reduce the firing temperature of ceramic products , to promote the sintering of ceramic products. Before sintering, feldspar acts as a barren raw material in the blank, improving the hydrophobicity of the blank, shortening the drying time of the blank, and reducing the drying shrinkage and deformation of the blank. In the ceramic glaze, after the feldspar glass melt is cooled after melting, the glass substance of the glaze is formed, which increases the transparency of the glaze and improves the gloss and performance of the glaze...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B03C1/30B07C5/342
CPCB03C1/30B07C5/3425
Inventor 陈小平李贵国王玉臣
Owner 内蒙古华宸再生资源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products