High-transmittance polyester thin film and preparation method thereof
A technology of high-transparency polyester and transparent polyester, which is applied in the field of polyester film, can solve the problems of high continuity requirements, long time, and impact on the recycling and granulation of polyester chips, so as to improve sustainability and binding force Effects of preventing and improving light transmittance reduction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0046] The present invention also provides a method for preparing a high permeability polyester film. The method comprises weighing the raw materials used in the core layer and the surface layer according to the formula, and then extruding them through a single screw or twin screw after drying and mixing devices. The machine is melted and mixed, the main extrusion and auxiliary extrusion are co-cast and extruded at the die head, the cast sheet is cooled, and the polyester film is obtained after longitudinal stretching, transverse stretching, and heat setting treatment.
[0047] It should be noted that the "longitudinal direction" of the aforementioned "longitudinal stretch" refers to the direction along which the polyester film moves, and the "lateral direction" of the "lateral stretch" refers to the direction along the width of the polyester film.
[0048] Further, in a specific production process, the longitudinal stretch ratio is 3.6 to 3.85, the transverse stretch ratio is 3.7 t...
Example Embodiment
[0053] Example 1
[0054] A polyester film includes a core layer and surface layers arranged on both sides of the core layer.
[0055] The surface layer includes 95% polyethylene terephthalate, 0.15% silica particles (with a particle size of 0.8μm), antioxidant 168 0.25%, antioxidant 1010 0.50%, and ultraviolet absorber UV-329 0.65%, antistatic agent (plastic antistatic agent 0006 produced by Zhongteng Chemical Co., Ltd.) 1.45%, dispersant (PEG, molecular weight 20000) 2%; the percentages are mass percentages;
[0056] The silica particles and the compatibilizer ABS-g-MAH (grafting rate≥0.5%) are ultrasonically dispersed in acetone, the acetone is recovered, and dried to obtain silica particles coated with the compatibilizer. Among them, the mass ratio of silica particles, compatibilizer ABS-g-MAH (grafting rate≥0.5%) and acetone is 1:0.07:19;
[0057] The preparation method of the polyester film includes:
[0058] The raw materials used in the core layer and the surface layer are wei...
Example Embodiment
[0062] Example 2
[0063] As in the polyester film provided in Example 1, in the modification treatment of silica particles, the mass ratio of silica particles, compatibilizer ABS-g-MAH (grafting rate ≥0.5%) and acetone is changed to 1:0.07:18, the rest remain unchanged, the preparation of polyester film is carried out, and the obtained polyester film is recorded as A2.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap