Coloration process of brass zipper

A zipper and brass technology, applied in the coating process of metal materials, etc., can solve the problems of poor color fastness to washing and corrosion resistance, unfavorable large-scale application, light color of the color film layer, etc., and achieve the coloring process Simple and easy to implement, high promotion and application value, low cost effect

Inactive Publication Date: 2019-01-01
道晟拉链科技(太仓)有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the implementation process of this coloring process, the process of depositing pure copper needs to be completed under boiling conditions, which has high energy consumption and cost, and the color of the obtained color film layer is relatively light and the bonding force is not high. At the same time, its color fastness to washing The degree and corrosion resistance are not good, so it is not conducive to large-scale application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coloration process of brass zipper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The specific processing method is as follows:

[0021] a) Chemical degreasing treatment, first, according to the mass concentration, mix 50g / L sodium hydroxide, 50g / L sodium phosphate, 20g / L sodium carbonate, 8g / L anhydrous sodium sulfate, and prepare the degreasing Oil solution; then fully wash the brass zipper with deionized water, then immerse the brass zipper in degreasing solution, degrease at 60°C for 5 minutes; finally wash in hot water at 70°C for 5 minutes.

[0022] b) Chemical polishing treatment, firstly mix 650mL / L hydrogen peroxide, 30g / L sulfuric acid, 140g / L ethylene glycol, 2g / L OP-10 emulsifier according to the volume concentration and mass concentration, Prepare a polishing solution; then immerse the degreasing brass zipper in the polishing solution, and polish it at 20°C for 2 minutes.

[0023] c) Activation treatment, first fully wash the polished brass zipper with deionized water, then activate it with 10% sulfuric acid solution at 25°C for 20s, an...

Embodiment 2

[0027] The specific processing method is as follows:

[0028] a) Chemical degreasing treatment, first, according to the mass concentration, mix 50g / L sodium hydroxide, 50g / L sodium phosphate, 20g / L sodium carbonate, 8g / L anhydrous sodium sulfate, and prepare the degreasing Oil solution; then fully wash the brass zipper with deionized water, then immerse the brass zipper in degreasing solution, degrease at 65°C for 4 minutes; finally wash with hot water at 75°C for 4 minutes.

[0029] b) Chemical polishing treatment, firstly mix 650mL / L hydrogen peroxide, 30g / L sulfuric acid, 140g / L ethylene glycol, 2g / L OP-10 emulsifier according to the volume concentration and mass concentration, Prepare a polishing solution; then immerse the degreased brass zipper in the polishing solution, and polish it at 25°C for 1.5 minutes.

[0030] c) Activation treatment, first fully wash the polished brass zipper with deionized water, then activate it with 10% sulfuric acid solution at 25°C for 20s,...

Embodiment 3

[0034] The specific processing method is as follows:

[0035] a) Chemical degreasing treatment, first, according to the mass concentration, mix 50g / L sodium hydroxide, 50g / L sodium phosphate, 20g / L sodium carbonate, 8g / L anhydrous sodium sulfate, and prepare the degreasing Oil solution; then fully wash the brass zipper with deionized water, then immerse the brass zipper in degreasing solution, degrease at 70°C for 3 minutes; finally wash in hot water at 80°C for 3 minutes.

[0036] b) Chemical polishing treatment, firstly mix 650mL / L hydrogen peroxide, 30g / L sulfuric acid, 140g / L ethylene glycol, 2g / L OP-10 emulsifier according to the volume concentration and mass concentration, Prepare a polishing solution; then immerse the degreased brass zipper in the polishing solution, and polish it at 30°C for 1 min.

[0037] c) Activation treatment, first fully wash the polished brass zipper with deionized water, then activate it with 10% sulfuric acid solution at 25°C for 20s, and fin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a coloration process of a brass zipper. The coloration process comprises the following steps of a) chemical deoiling treatment; b) chemical polishing treatment; c) activation treatment; d) chemical coloration treatment; and e) post treatment. The invention discloses the coloration process of the brass zipper; the coloration process is simple, feasible, low in energy consumption and low in cost; through optimizing the constitution of a coloration solution and a process condition, not only is the higher bonding force of a colored film ensured, but also the better color fastness to washing and the corrosion resistance of the colored film are ensured; and the coloration process has higher popularization and application value.

Description

technical field [0001] The invention relates to a coloring process, in particular to a brass zipper coloring process, and belongs to the technical field of zippers. Background technique [0002] Zipper is an important livelihood product, widely used in clothing, bags, shoes and other daily necessities. Among them, brass zippers have the unique texture and nobleness of metal, and are often used in various high-end products to improve the decoration and competitiveness of the products. In order to improve the service life of the brass zipper and increase the aesthetics, it is usually necessary to carry out necessary surface coloring treatment on the brass zipper. Brass is a kind of copper metal. Among the current copper metal coloring formulas, the commonly used coloring formulas mainly include copper-ammonia salt system and sulfide system. [0003] At present, the surface coloring process of brass zippers is usually divided into two steps: first deposit a layer of pure copp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/63C23C22/78C23G1/20C23F3/06
CPCC23C22/63C23C22/78C23F3/06C23G1/20
Inventor 杨志锋
Owner 道晟拉链科技(太仓)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap