Waterproofing and low-voltage aluminum electrolytic capacitor working electrolyte
A technology of aluminum electrolytic capacitors and electrolytes, applied in electrolytic capacitors, capacitors, circuits, etc., can solve problems such as oxide film performance damage, achieve low production costs, simple formulas, and realize the effects of industrialized production
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] Example 1 Electrolyte formula and its preparation
[0034]
[0035] Preparation process: According to the components in the above table, first, heat the main solvent and auxiliary solvent to 60°C and mix, add the solute adipic acid and ammonium formate, then add the waterproof mixture and other additives, and stir for 15 minutes under the constant temperature of 110°C. , Cool to room temperature to obtain electrolyte.
Example Embodiment
[0036] Example 2 Electrolyte formula and its preparation
[0037]
[0038] Preparation process: According to the components in the above table, first, heat the main solvent and auxiliary solvent to 60°C and mix, add the solute adipic acid and ammonium formate, then add the waterproof mixture and other additives, and stir for 15 minutes under the constant temperature of 110°C. , Cool to room temperature to obtain electrolyte.
Example Embodiment
[0039] Example 3 Performance Test
[0040] Working electrolyte parameters are shown in Table 1.
[0041] Table 1 Test parameters of working electrolyte
[0042] Performance parameter
[0043] The electrical characteristics of the electrolytic capacitor obtained using the electrolyte of Example 1 of the present invention at a working voltage of 6.3V to 35V are shown in Table 2. The electrical characteristics of the electrolytic capacitor obtained using the electrolyte of Example 2 of the present invention at a working voltage of 50V to 100V are shown in Table 2. The characteristics are shown in Table 3.
[0044] Table 2 Electrical characteristics under 6.3V~35V working voltage (take 6.3V 1500μf specification as an example)
[0045]
[0046] Table 3: Electrical characteristics under 50V~100V working voltage (take 100V 330μf specification as an example)
[0047]
[0048] From the test results of the performance parameters of the electrolyte in Table 1, it can be seen that the electrolyt...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap