Corrosion Inhibitor for Galvanized Pipe of Evaporative Condenser and Process of Using It to Clean Condenser
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An evaporative condenser and corrosion inhibitor technology, applied in the field of condenser galvanized pipe cleaning, can solve the problems of galvanized pipe corrosion, alkali resistance, acid resistance, etc., to improve protection, reduce pressure, and improve polarity Effect
Active Publication Date: 2021-06-25
HANGZHOU GUANJIE IND CLEANING WATER TREATMENT TECH
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] However, since zinc is an active metal, it is neither alkali-resistant nor acid-resistant. In turn, whether it is an organic descaling cleaning agent or an inorganic acid cleaning agent, it is easy to cause serious damage to the galvanized pipe during the cleaning process. Corrosion to a great extent
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-9
[0054] Examples 1-9: A corrosion inhibitor for galvanized pipes of evaporative condensers, the components and corresponding qualities are shown in Table 1.
[0055] Each component and its corresponding mass (kg) in table 1 embodiment 1-9
[0056]
Embodiment 10
[0057] Embodiment 10: a kind of technology that adopts corrosion inhibitor to clean condenser, its steps are as follows:
[0058] S1: Prepare a solution of slime stripping agent with a mass concentration of 1% with water, pass it into a galvanized carbon tube, let it stand for 12 hours for cleaning, drain the water and foreign matter in the condenser, and replace it with new water;
[0059] S2: Add 12 kg of corrosion inhibitor for each ton of water in the condenser, turn on the water pump cycle, add the corrosion inhibitor to the circulating water of the condenser, and form a corrosion inhibition solution in the galvanized carbon tube;
[0060] S3: After the corrosion inhibitor solution circulates evenly in the galvanized carbon tube, the water pump continues to operate, and the fan is turned on, and scale cleaning agent is added to the corrosion inhibitor solution of the condenser at a rate of 5kg / min;
[0061] S4: When the zinc layer is exposed, immediately stop adding scale...
Embodiment 11
[0064] Embodiment 11: a kind of technology that adopts corrosion inhibitor to clean condenser, its steps are as follows:
[0065] S1: Prepare a solution of slime stripping agent with a mass concentration of 3% with water, pass it into a galvanized carbon tube, let it stand for 12 hours for cleaning, drain the water and foreign matter in the condenser, and replace it with new water;
[0066] S2: Add 11 kg of corrosion inhibitor for every ton of water in the condenser, turn on the water pump circulation, add the corrosion inhibitor to the circulating water of the condenser, and form a corrosion inhibition solution in the galvanized carbon tube;
[0067] S3: After the corrosion inhibitor solution circulates evenly in the galvanized carbon tube, the water pump continues to operate, and the fan is turned on, and scale cleaning agent is added to the corrosion inhibitor solution of the condenser at a rate of 4kg / min;
[0068] S4: When the zinc layer is exposed, immediately stop addin...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a corrosion inhibitor for galvanized pipes of evaporative condensers and a process for cleaning condensers using the same, which belongs to the field of cleaning galvanized pipes of condensers and solves the problem that the galvanized layer is easily damaged when cleaning condensers in the prior art. corrosion problem. The corrosion inhibitor is composed of the following components by weight: 1-5 parts of aldehyde compound, 0.5-2 part of cationic surfactant, 0.1-2 part of ammonium salt, 0.1-2 part of dispersant, alkyl glycoside and co-surfactant ; The number of carbon atoms of the aldehyde compound is one of 3, 4, and 5, and the cationic surfactant is a nitrogen-containing organic amine derivative; the ammonium salt is composed of ammonium ions and acid radical ions; alkyl glycosides, cationic surfactants, The mass ratio of co-surfactant is (2‑5):5:1. The corrosion inhibitor in the present invention realizes the corrosion inhibition effect on the galvanized pipe through the combined use of cationic surfactants, ammonium salts and aldehyde compounds.
Description
technical field [0001] The invention relates to the field of cleaning galvanized pipes of condensers, in particular to a corrosion inhibitor for galvanized pipes of evaporative condensers and a process for cleaning condensers using the same. Background technique [0002] The evaporative condenser is the necessary equipment for the cold storage. It relies on circulating water to cool the liquid ammonia. It is composed of a fan, a condensing plate, a heat exchanger, a box and other components, and the condensing plate is a galvanized carbon steel pipe. After one to two years of operation, the inner wall of the galvanized pipe of the condenser will form a carbonate hard scale package, the serious scale layer reaches more than ten millimeters, and there is biological slime attached. Scaling will lead to a significant drop in the heat transfer effect of the galvanized tube in the condenser, an increase in the pressure of liquid ammonia, and an increase in the temperature of the c...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G1/04C23G3/04
Inventor 黄冠土
Owner HANGZHOU GUANJIE IND CLEANING WATER TREATMENT TECH