A kind of copper red matt kiln changing glaze and preparation method thereof

A technology of bottom glaze and surface glaze, which is applied in the field of ceramic glaze, can solve the problems of high difficulty in making kiln-changing glaze and poor kiln-changing effect, and achieve the effect of beautiful and generous products, delicate glazed surface and smooth glazed surface

Active Publication Date: 2021-11-23
福建省德化县哈维陶瓷有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a copper red matt kiln-changing glaze and its preparation method, which solves the problems of high difficulty in making kiln-changing glaze and poor kiln-changing effect in the prior art, and the prepared kiln-changing glaze Excellent performance, thermal stability, water absorption and lead, cadmium dissolution of the product can meet the relevant standards of daily ceramic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of copper red matt kiln changing glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A copper-red matt kiln-changing glaze, the copper-red matt kiln-changing glaze is composed of a bottom glaze and a top glaze, the bottom glaze is applied on a ceramic body, and the top glaze is applied on the bottom glaze:

[0040] The bottom glaze includes the following components by weight: 25 parts of refined potassium feldspar, 1.8 parts of animal ashes, 12 parts of refined quartz, 9 parts of lime, 4 parts of talc, 4 parts of refined cordierite, 8 parts of silicon carbonate, copper oxide 1.5 parts, 4 parts of tin oxide, 4 parts of zinc oxide, 5 parts of aluminum oxide, 12 parts of barium carbonate, 15 parts of boron;

[0041] The surface glaze includes the following components by weight: 15 parts of refined potassium feldspar, 8 parts of refined quartz, 4 parts of talc, 8 parts of zirconium phosphate, 4 parts of titanium oxide, 4 parts of tin oxide, 35 parts of frit, and refined dolomite 6 parts of stone, 6 parts of zinc oxide, 1.5 parts of copper oxide;

[0042] T...

Embodiment 2

[0053] A copper-red matt kiln-changing glaze, the copper-red matt kiln-changing glaze is composed of a bottom glaze and a top glaze, the bottom glaze is applied on a ceramic body, and the top glaze is applied on the bottom glaze:

[0054] The bottom glaze includes the following components by weight: 35 parts of refined potassium feldspar, 2.2 parts of animal ashes, 18 parts of refined quartz, 11 parts of lime, 6 parts of talc, 6 parts of refined cordierite, 12 parts of silicon carbonate, copper oxide 2.5 parts, 6 parts of tin oxide, 6 parts of zinc oxide, 8 parts of aluminum oxide, 18 parts of barium carbonate, 25 parts of boron;

[0055] The surface glaze includes the following components by weight: 25 parts of refined potassium feldspar, 12 parts of refined quartz, 6 parts of talc, 12 parts of zirconium phosphate, 8 parts of titanium oxide, 6 parts of tin oxide, 45 parts of frit, and refined dolomite 10 parts of stone, 10 parts of zinc oxide, 2.5 parts of copper oxide;

[0...

Embodiment 3

[0067] A copper-red matt kiln-changing glaze, the copper-red matt kiln-changing glaze is composed of a bottom glaze and a top glaze, the bottom glaze is applied on a ceramic body, and the top glaze is applied on the bottom glaze:

[0068] The bottom glaze includes the following components by weight: 28 parts of refined potassium feldspar, 1.9 parts of animal ashes, 14 parts of refined quartz, 9 parts of lime, 4.5 parts of talc, 4.5 parts of refined cordierite, 9 parts of silicon carbonate, copper oxide 1.8 parts, 4.5 parts of tin oxide, 4.5 parts of zinc oxide, 6 parts of aluminum oxide, 14 parts of barium carbonate, 18 parts of boron;

[0069] The surface glaze includes the following components by weight: 18 parts of refined potassium feldspar, 9 parts of refined quartz, 4.5 parts of talc, 9 parts of zirconium phosphate, 5 parts of titanium oxide, 4.5 parts of tin oxide, 38 parts of frit, and refined dolomite 7 parts of stone, 7 parts of zinc oxide, 1.8 parts of copper oxide;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of ceramic glazes, in particular to a copper red matt kiln-changing glaze and a preparation method thereof. The copper-red matt kiln glaze is composed of a bottom glaze and a top glaze. The bottom glaze includes refined potassium feldspar, animal bone ash, refined quartz, lime, talc, refined cordierite, silicon carbonate, copper oxide, tin oxide, zinc oxide, Alumina, barium carbonate, and boron; topcoats include refined potassium feldspar, refined quartz, talc, zirconium phosphate, titanium oxide, tin oxide, frit, refined dolomite, zinc oxide, and copper oxide. The preparation method comprises: preparing the bottom glaze slurry; preparing the top glaze slurry; preparing the bottom glaze; and preparing the top glaze. The invention solves the problems of high difficulty in making kiln-transformed glaze and poor kiln-transformed effect in the prior art, and the prepared kiln-transformed glaze has excellent performance, and the thermal stability, water absorption rate and dissolution of lead and cadmium of the product can meet the requirements of daily-use ceramic products. related standards.

Description

technical field [0001] The invention relates to the technical field of ceramic glazes, in particular to a copper red matt kiln-changing glaze and a preparation method thereof. Background technique [0002] Porcelain is made of porcelain stone, kaolin, quartz stone, mullite, etc., and the surface is covered with glass glaze or painted objects. Porcelain is formed by firing at a high temperature (about 1280°C-1400°C) in a kiln, and the glaze color on the surface of the porcelain will undergo various chemical changes due to different temperatures. Sintered porcelain bodies generally contain less than 3% iron and are impermeable. Because of their relatively low cost and wear-resistant and impermeable properties, they are widely used by people all over the world. [0003] When firing porcelain, anyone who finds that the shape or glaze color is not the expected shape or glaze color after opening the kiln, so that the handed down porcelain sometimes has a special situation, can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C03C8/00
Inventor 曾昭育
Owner 福建省德化县哈维陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap