A kind of preparation method of lightweight polypropylene material

A polypropylene material and lightweight technology, applied in the field of polypropylene materials, can solve the problems of difficulty in meeting the production requirements of polypropylene foam materials, low decomposition starting temperature, wide decomposition temperature range, etc., so as to reduce the decomposition temperature range and improve the Compatibility, the effect of improving the effect

Active Publication Date: 2021-06-01
SUZHOU RUNJIA ENGINEER PLASTIC
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the decomposition initiation temperature of sodium bicarbonate is low (begins to decompose at about 60°C), the decomposition temperature range is wide, and a large amount of volatilization occurs before the softening temperature of polypropylene, which is difficult to meet the production requirements of polypropylene foam materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The invention provides a kind of preparation method of lightweight polypropylene material, comprises the following steps:

[0023] (1) Weigh 12 parts by mass of sodium bicarbonate and 28 parts by mass of citric acid; mix the two and infiltrate them in 100 parts by mass of ethanol, then mix them evenly with ultrasonic waves, spin dry them by spin coating, and dry them in vacuum for 0.5h , to remove the organic solvent to obtain a microcellular foaming agent for polypropylene; citric acid can increase the thermal decomposition initiation temperature of sodium bicarbonate, and citric acid itself also has a foaming effect, which is conducive to improving the microcellular foaming agent for polypropylene The foaming effect of the agent;

[0024] (2) Weigh 75 parts by mass of silicone oil (molecular weight 1-100,000), add 25 parts by mass of the microcellular foaming agent for polypropylene prepared in step (1), and then ultrasonicate and stir at a speed of 100rpm, The mixin...

Embodiment 2

[0031] The invention provides a kind of preparation method of lightweight polypropylene material, comprises the following steps:

[0032] (1) Weigh 15 parts by mass of sodium bicarbonate and 21 parts by mass of citric acid; mix the two and infiltrate them in 100 parts by mass of ethanol, then mix them evenly with ultrasonic waves, spin dry them by spin coating, and dry them in vacuum for 0.2h , remove the organic solvent to obtain the microcellular foaming agent for polypropylene;

[0033] (2) Weigh 80 parts by mass of silicone oil (molecular weight 1-100,000), add 20 parts by mass of the microcellular foaming agent for polypropylene prepared in step (1), and then ultrasonicate and stir at a speed of 150rpm, The mixing time is 12 hours; vacuum drying for 100 minutes after vacuum filtration to obtain a microporous foaming agent for silicone-coated polypropylene;

[0034] (3) Weigh 2 parts by mass of the microcellular foaming agent for silicone-coated polypropylene prepared in ...

Embodiment 3

[0040] The invention provides a kind of preparation method of lightweight polypropylene material, comprises the following steps:

[0041] (1) Weigh 9 parts by mass of sodium bicarbonate and 35 parts by mass of citric acid; mix the two and infiltrate them in 100 parts by mass of ethanol, then mix them evenly with ultrasonic waves, spin dry them by spin coating, and dry them in vacuum for 1 hour. Remove the organic solvent to obtain a microcellular foaming agent for polypropylene;

[0042] (2) Weigh 70 parts by mass of silicone oil (molecular weight 1-100,000), add 30 parts by mass of the microcellular foaming agent for polypropylene prepared in step (1), and then ultrasonicate and stir at a speed of 80rpm, The mixing time is 24 hours; vacuum drying for 50 minutes after vacuum filtration to obtain a microporous foaming agent for silicone-coated polypropylene;

[0043] (3) Weigh 4.5 parts by mass of the microcellular foaming agent for silicone-coated polypropylene prepared in st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
phase transition temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a lightweight polypropylene material, comprising the following steps: (1) uniformly mixing sodium bicarbonate and citric acid to obtain a microporous foaming agent for polypropylene; (3) Microcellular foaming agent for silicone-coated polypropylene, polypropylene, filler, antioxidant, heat stabilizer, microcapsule red The thucitol is mixed evenly to obtain the finished product. The present invention improves the thermal decomposition starting temperature of sodium bicarbonate by adding citric acid and microcapsule erythritol, narrows the decomposition temperature range, and improves the foaming effect; wherein the thiritol material is an excellent medium-temperature phase It is a change material with a phase transition temperature of 119-124°C. When the temperature rises above the phase change temperature, erythritol undergoes a phase change, absorbing heat to slow down / prevent the temperature rise, thereby delaying the thermal decomposition of sodium bicarbonate as a foaming agent and improving the foaming effect.

Description

technical field [0001] The invention relates to the field of polypropylene materials, in particular to a preparation method of lightweight polypropylene materials. Background technique [0002] Lightweight, energy saving and environmental protection, as well as high-efficiency and low-cost production have always been the goals that the automotive industry continues to pursue. Because polypropylene is a material with high cost performance, its application in automotive plastic parts has been continuously expanded, and it has been widely used in bumpers, automotive dashboards, door panels, and central passages. , decorative pillars, trunks and other major automotive plastic parts. [0003] However, since polypropylene materials began to replace expensive engineering plastics or bulky metal materials, after decades of technological development, this alternative work can be said to be gradually approaching the extreme to some extent, short-term From the perspective of material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/08C08L23/12C08K9/10C08K3/34C08K5/053
CPCC08J9/0023C08J9/009C08J9/08C08J2203/02C08J2323/12
Inventor 汪理文李庆贵刘正军牛国增沈安平翁永华
Owner SUZHOU RUNJIA ENGINEER PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com