A kind of preparation method of mullite nanofiber airgel with light weight and thermal insulation

A nanofiber, lightweight thermal insulation technology, applied in ceramic products, other household appliances, household appliances, etc., can solve problems such as improving thermal insulation performance

Active Publication Date: 2021-07-13
TIANJIN UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the macropores produced by the sublimation of freeze-dried ice crystals are not conducive to the improvement of thermal insulation performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of mullite nanofiber airgel with light weight and thermal insulation
  • A kind of preparation method of mullite nanofiber airgel with light weight and thermal insulation
  • A kind of preparation method of mullite nanofiber airgel with light weight and thermal insulation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Cut the mullite nanofiber membrane to 10mm with scissors 2 Size, weigh 0.2g of fiber film and add it to 50ml of ethanol, disperse it with a high-speed disperser at 3000r / min for 5min, take out the suspension above it and dry it to obtain a single fiber.

[0026] (2) Take 5g tetraethyl orthosilicate, 3g ethanol, 2g deionized water, drop 3 drops of 0.1mol / L dilute nitric acid therein, magnetic stirring makes the solution clear and transparent to obtain 50wt% silica sol; weigh 0.08g Put the silica sol into the mold, add 1.92g of water, 0.1g of acrylamide, 0.005g of N-N methylenebisacrylamide, stir well to dissolve it.

[0027] (3) Add 0.05g fiber to the mold, stir to disperse evenly, then add 3 drops of ammonium persulfate aqueous solution, 1 drop of tetramethylethylenediamine aqueous solution, seal and keep warm at 50°C for 20min to make it gel .

[0028] (4) Put the gelled sample into an ultra-low temperature freezer to freeze at -80°C for 24 hours, take it out and...

Embodiment 2

[0030] (1) Cut the mullite nanofiber membrane to 10mm with scissors 2 Size, weigh 0.2g of fiber film and add it to 50ml of ethanol, disperse it with a high-speed disperser at 3000r / min for 5min, take out the suspension above it and dry it to obtain a single fiber.

[0031] (2) Take 5g tetraethyl orthosilicate, 3g ethanol, 2g deionized water, drop 3 drops of 0.1mol / L dilute nitric acid therein, magnetic stirring makes the solution clear and transparent to obtain 50wt% silica sol; weigh 0.08g Put the silica sol into the mold, add 1.92g of water, 0.1g of acrylamide, 0.005g of N-N methylenebisacrylamide, stir well to dissolve it.

[0032] (3) Add 0.05g fiber to the mold, stir to disperse evenly, then add 3 drops of ammonium persulfate aqueous solution, 1 drop of tetramethylethylenediamine aqueous solution, seal and keep warm at 50°C for 20min to make it gel .

[0033] (4) Put the gelled sample into an ultra-low temperature freezer to freeze at -80°C for 24 hours, take it out and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of ultra-low solid content light-weight heat-insulating mullite nanofiber airgel, in which nano-mullite fiber membranes are dispersed to obtain mullite single fibers; silica sol and acrylamide The system gel injection molding premix is ​​mixed with the dispersed mullite single fiber to make a gel; the gel is freeze-dried to obtain an airgel body, and finally calcined at a high temperature to obtain the mullite nanofiber airset Glue products. The product of the invention is light in weight, high in porosity and low in thermal conductivity, and provides a preparation method of the nanofiber airgel which can be used at 1300°C.

Description

technical field [0001] The invention relates to the preparation of lightweight heat-insulating mullite airgel, in particular to a preparation method of light-weight heat-insulating mullite nanofiber airgel, and belongs to the technical field of nanofiber airgel preparation. Background technique [0002] Airgel, which is formed by the aggregation of ultrafine particles to form a porous network structure, has extremely low density and thermal conductivity. important role. However, due to the high activity of nanoparticles, the structure of airgel will collapse at high temperature, and its effective use temperature is generally below 1200 °C. With the development of aircraft and thermal equipment in the direction of light weight, high efficiency and energy saving, especially aerospace fighters with high Mach number, long endurance, and repeated trips to and from the atmosphere have gradually become the focus of military competition in various countries. Ultralight heat-insula...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B35/14C04B35/80C04B35/624
CPCC04B35/803C04B35/14C04B35/624C04B38/0045C04B2235/5228C04B2235/6562C04B2235/6567C04B2235/9607
Inventor 郭安然张莹刘瑞丽刘家臣杜海燕关星宇
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com