Chinese maifanite mineral dry powder and modification process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A Chinese medical stone and medical stone technology, which is applied in the fields of adding substances to water/sewage treatment, water pollutants, water/sludge/sewage treatment, etc., can solve the problem of inconspicuous functions of medical stone
Inactive Publication Date: 2019-09-10
韩宝音代来
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, it has been proved by experiments that the release of trace elements from medical stones under normal conditions is negligible. The medical stone industry has been developed for 30 years, and users of medical stone products increasingly feel that the functions of medical stones are not obvious, so the medical stone industry has not been big. development of
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] The present embodiment provides a modification process of Chinese medical stone mineral dry powder, comprising the following steps:
[0029] (1) Wash the Chinese medical stone with clear water, then pulverize it to 3000-3100 mesh through a pulverizer to obtain Chinese medical stone powder;
[0030] (2) calcining the Chinese medical stone micro-powder obtained in step (1) at 700° C. for 3 hours, until it is completely red, and then the activated Chinese medical stone micro-powder is obtained;
[0031] (3) Mix the activated Chinese medical stone powder obtained in step (2) with the liquid at a weight ratio of 1:0.5, then extract for 26 hours at an extraction temperature of 25°C and a stirring speed of 60r / min, and obtain Chinese wheat rice stone extract;
[0032] (4) The Chinese medical stone extract obtained in step (3) is fully evaporated to dryness at 400° C. to obtain Chinese medical stone mineral dry powder.
Embodiment 2
[0034] The present embodiment provides a modification process of Chinese medical stone mineral dry powder, comprising the following steps:
[0035] (1) Wash the Chinese medical stone with clear water, then pulverize it to 3400-3500 mesh through a pulverizer to obtain Chinese medical stone powder;
[0036] (2) calcining the Chinese medical stone micro-powder obtained in step (1) at 750° C. for 2 hours, until it is completely red, and then the activated Chinese medical stone micro-powder is obtained;
[0037] (3) Mix the activated Chinese medical stone powder obtained in step (2) with the liquid at a weight ratio of 1:2, then extract for 24 hours at an extraction temperature of 90°C and a stirring speed of 40r / min, and obtain Chinese wheat rice stone extract;
[0038] (4) fully evaporating the Chinese medical stone extract obtained in step (3) to dryness at 1000° C. to obtain Chinese medical stone mineral dry powder.
Embodiment 3
[0040] The present embodiment provides a modification process of Chinese medical stone mineral dry powder, comprising the following steps:
[0041] (1) Wash the Chinese medical stone with clear water, then pulverize it to 3200-3300 mesh through a pulverizer to obtain Chinese medical stone powder;
[0042] (2) calcining the Chinese medical stone micro-powder obtained in step (1) at 725°C for 2.5 hours, until it was completely red, and then the activated Chinese medical stone micro-powder was obtained;
[0043] (3) Mix the activated Chinese medical stone powder obtained in step (2) with the liquid at a weight ratio of 1:1, then extract for 25 hours at an extraction temperature of 55°C and a stirring speed of 50 r / min, and obtain Chinese wheat rice stone extract;
[0044] (4) Fully evaporate the Chinese medical stone extract solution obtained in step (3) to dryness at 700° C. to obtain Chinese medical stone mineral dry powder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to Chinese maifanite mineral dry powder and a modification process thereof. The modification process comprises the following steps: (1) washing Chinese maifanite, and pulverizingthe washed Chinese maifanite so as to obtain Chinese maifanite micro-powder; (2) performing high-temperature calcination on the Chinese maifanite micro-powder obtained in the step (1) so as to obtainactivated Chinese maifanite micro-powder after completion of the calcination; (3) mixing the activated Chinese maifanite micro-powder obtained in the step (2) with a liquid, and then performing extraction and stirring so as to obtain Chinese maifanite extract; and (4) evaporating the Chinese maifanite extract obtained in the step (3) to dryness so as to obtain the Chinese maifanite mineral dry powder. In the modification process, high-temperature calcination and liquid boiling are performed, and therefore the degree of migration of mineral elements in the Chinese maifanite to water is enhanced, so that the elements are more easily dissolved in the water; and it is confirmed after tests that after the Chinese maifanite mineral dry powder is soaked in boiled water, not only the soaked dry powder is rich in a variety of elements required by the human body, but also the distilled water can be adjusted to weak alkalinity, so that the human health is facilitate, and safety and no harm are achieved.
Description
technical field [0001] The invention belongs to the field of medical stone processing, and in particular relates to Chinese medical stone mineral dry powder and a modification process thereof. Background technique [0002] Chinese medical stone is a kind of medical stone, and the medical stone produced in Pingdingshan, Naiman Banner, Inner Mongolia is called "Chinese medical stone". In 1985, the People's Government of Naiman Banner, Tongliao City, Inner Mongolia entrusted 12 scientific research units in 14 provinces, municipalities and autonomous regions, and 98 experts conducted a systematic study on the medical stone of Naiman Banner. The research results confirmed that the medical stone of Naiman Banner is non-toxic and harmless. , containing 59 kinds of minerals and trace elements. Among them, there are more than 17 kinds of essential life elements for human body. Contains all 11 constant elements and all 17 rare earth elements. It is the most ideal natural mineral an...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More