Graphite-like phase carbon nitride coated [alpha]-Fe2O3 material, and preparation and application thereof

A graphite phase carbon nitride and coating technology, which is applied in the direction of electrochemical generators, active material electrodes, electrical components, etc., can solve the problems of low initial Coulombic efficiency, volume expansion during charging and discharging, and difficulty in meeting future needs. Achieve the effects of thin and uniform coating layer, enhanced electrical conductivity, and stable cycle performance

Active Publication Date: 2019-11-08
HEFEI GUOXUAN HIGH TECH POWER ENERGY
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional graphite is used as the negative electrode of lithium batteries, and its research and development is close to its theoretical specific capacity of 372mAh/g, which is difficult to meet future needs
Among them, the transition metal oxide fer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphite-like phase carbon nitride coated [alpha]-Fe2O3 material, and preparation and application thereof
  • Graphite-like phase carbon nitride coated [alpha]-Fe2O3 material, and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] A kind of graphite-like phase carbon nitride coated α-Fe 2 O 3 The preparation method of the material includes the following steps: add 0.01 mol of ferric nitrate to 200 ml of deionized water to dissolve, then add 0.05 mol of urea, magnetically stir for 1 h, and ultrasonic for 0.5 h to disperse uniformly to obtain a precursor solution; take the precursor solution in a tube furnace In an air atmosphere, heat up to 200°C at a rate of 3°C / min, sinter for 2 hours, then heat up to 400°C at a rate of 3°C / min, sinter for 2 hours, and then take out and wash with deionized water alternately 3 times to medium Performance, vacuum drying at 80℃ for 24h to obtain graphite-like phase carbon nitride coated α-Fe 2 O 3 material.

Example Embodiment

[0032] Example 2

[0033] A kind of graphite-like phase carbon nitride coated α-Fe 2 O 3 The preparation method of the material includes the following steps: add 0.01 mol of ferric nitrate to 200 ml of deionized water to dissolve, then add 0.05 mol of urea, magnetically stir for 1 h, and ultrasonic for 0.5 h to disperse uniformly to obtain a precursor solution; take the precursor solution in a tube furnace In an air atmosphere, heat up to 300°C at a rate of 3°C / min, sinter for 2h, then heat up to 600°C at a rate of 3°C / min, sinter for 2h, and then take out and wash with deionized water alternately 3 times to medium Performance, vacuum drying at 80℃ for 24h to obtain graphite-like phase carbon nitride coated α-Fe 2 O 3 material.

Example Embodiment

[0034] Example 3

[0035] A kind of graphite-like phase carbon nitride coated α-Fe 2 O 3 The preparation method of the material includes the following steps: adding 0.01 mol of ferric nitrate to 200 ml of deionized water to dissolve, then adding 0.1 mol of urea, magnetic stirring for 1 h, and ultrasonic for 0.5 h to disperse uniformly to obtain a precursor solution; taking the precursor solution in a tube furnace In an air atmosphere, heat up to 200°C at a rate of 3°C / min, sinter for 2 hours, then heat up to 600°C at a rate of 3°C / min, sinter for 2 hours, and then take out and wash with deionized water alternately 3 times to medium Performance, vacuum drying at 80℃ for 24h to obtain graphite-like phase carbon nitride coated α-Fe 2 O 3 material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a graphite-like phase carbon nitride coated [alpha]-Fe2O3 material, comprising the steps of: uniformly stirring and mixing an iron salt and a graphite-like phase carbon nitride precursor in water, dispersing ultrasonically the mixture to obtain a precursor solution; sintering the precursor solution, washing the sintered precursor solution with waterto neutrality, and drying the product to obtain a graphite-like phase carbon nitride-coated [alpha]-Fe2O3 material. The invention also discloses a graphite-like phase carbon nitride coated [alpha]-Fe2O3 material, which is prepared by using the preparation method. The invention also discloses the application of the graphite-like phase carbon nitride coated [alpha]-Fe2O3 material in preparing battery electrodes, supercapacitors and electric vehicles. The method realizes the uniform coating of graphite phase carbon nitride. The graphite phase carbon nitride on the surface of [alpha]-Fe2O3 effectively improves the conductivity and the stability of [alpha]-Fe2O3. The graphite phase carbon nitride and the [alpha]-Fe2O3 have a synergistic effect.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a graphite phase carbon nitride coated α-Fe 2 o 3 Materials and their preparation methods and applications. Background technique [0002] With the rapid development of the global economy, the human demand for energy is getting higher and higher, while the non-renewability of traditional fossil fuel energy and the pollution caused by fossil fuel combustion are becoming more and more prominent. The development of new energy technologies has gradually become a human priority. Focus on focus and research hotspots. In recent decades, with the commercial success of lithium-ion batteries, research on lithium-based high-performance chemical power sources has intensified. [0003] With the development of new energy electric vehicles and the promotion of national policies, the market demand for high energy density lithium-ion batteries is also increasing. Traditional graphi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/36H01M4/485H01M4/62H01M10/0525
CPCH01M4/362H01M4/485H01M4/625H01M10/0525H01M2004/027Y02E60/10
Inventor 辛昱林少雄辛利君王辉
Owner HEFEI GUOXUAN HIGH TECH POWER ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap