A kind of ultra-thin ultra-soft smooth emery cloth and its production process

A technology of smooth surface and abrasive cloth, applied in manufacturing tools, metal processing equipment, grinding/polishing equipment, etc., can solve the problems of poor softness of abrasive cloth, achieve good adhesion and mechanical properties, good anti-blocking performance, and use long life effect

Active Publication Date: 2021-04-23
古德尚新材料科技湖北有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the problem of poor softness of the abrasive cloth in the prior art, the present invention provides an ultra-thin and ultra-soft smooth abrasive cloth and its production process. The abrasive cloth prepared through a reasonable formula design and corresponding process method has a longer service life and a smoother product. , good softness, can be used in high-precision electronics industry, fine grinding of semiconductors, lithium batteries, liquid metal, stainless steel, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Configuration of soft polyurethane waterproof material

[0046] The primer layer is made of soft polyurethane waterproof material, and the polyurethane is made of PU-3541 water-based polyurethane resin from Guangzhou Hengfeng New Material Co., Ltd. The flexible polyurethane waterproof material adopts a toluene solution with a percentage by weight of: polyurethane: curing agent = 10:1, wherein the curing agent is an amine curing agent, specifically the H-1001 curing agent of Guangzhou Hengfeng New Material Co., Ltd.

[0047] The configuration process of epoxy modified phenolic resin

[0048] Put 100KG of phenol, 86KG of formaldehyde, 0.35KG of oxalic acid, and 10KG of water into the reactor for stirring (60-100 rpm), and heat at 60°C (reflux); Heat at ℃ for 2 hours to 135 minutes to condense. After the reaction is terminated, add 100kg of cold water. After standing for 30 minutes, remove the water with a suction pipe to obtain a phenolic resin. The molecular weight of ...

Embodiment 2

[0071] The method that present embodiment prepares emery cloth, material are basically the same as embodiment 1, and difference is:

[0072] The absolute dry weight of the cloth base material is 50-80g / m 2 ;

[0073] The coating amount of primer layer is 7-12g / m 2 ;

[0074] The sand planting particle size is 1500 mesh, and the sand planting amount is 40-60g / m 2 ;

[0075] The coating amount of the compound layer is 30-50g / m 2 ;

[0076] Anti-clogging coating modified water-based zinc stearate coating amount is 10-18g / m 2 ;

[0077] The abrasive cloth prepared in this embodiment is 1500 mesh, and the weight is 160-180g / m 2 , the thickness is 0.14mm.

[0078] Using the same type of stretching equipment as in Example 1, under normal temperature conditions, measure the strength parameters of the emery cloth prepared in this example, the radial breaking strength of the emery cloth is 638N / 5CM, and the transverse breaking strength is 361N / 5CM; 600N The elongation was 16.1...

Embodiment 3

[0081] The method that present embodiment prepares emery cloth, material are basically the same as embodiment 1, and difference is:

[0082] The absolute dry weight of the cloth base material is 50-80g / m 2 ;

[0083] The coating amount of primer layer is 10-15g / m 2 ;

[0084] The particle size of sand planting is 400 mesh, and the amount of sand planting is 70-100g / m 2 ;

[0085] The coating amount of the compound layer is 50-70g / m 2 ;

[0086] Anti-clogging coating modified water-based zinc stearate coating amount is 20-30g / m 2 ;

[0087] The emery cloth prepared in this embodiment is 400 mesh, and the weight is 220-240g / m 2 , the thickness is 0.2mm.

[0088] Using the same type of stretching equipment as in Example 1, under normal temperature conditions, measure the strength parameters of the emery cloth prepared in this example, the radial breaking strength of the emery cloth is 634N / 5CM, and the transverse breaking strength is 400N / 5CM; 600N The elongation was 16...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultra-thin and ultra-soft smooth abrasive cloth and a production process thereof, belonging to the field of coated abrasives. The ultra-thin and ultra-soft smooth emery cloth of the present invention comprises a cloth-based substrate, a primer layer positioned on one side of the cloth-based substrate, an abrasive layer at least partially embedded in the primer layer, and coated on the abrasive The adhesive layer on the layer, the adhesive layer contains epoxy modified phenolic resin; the epoxy modified phenolic resin is prepared from phenolic resin, epoxy resin, sodium oxide and water. The present invention adopts epoxy-modified phenolic resin as the adhesive layer. The epoxy-modified phenolic resin has small shrinkage, good adhesion and mechanical properties, and the abrasive layer in the middle is not easy to fall off, and the service life is longer, and the product is flat and soft. And strength parameters are significantly improved.

Description

technical field [0001] The invention belongs to the field of coated abrasives, and more specifically relates to an ultra-thin and ultra-soft smooth abrasive cloth and a production process thereof. Background technique [0002] Coated molds are abrasive tools that use adhesives to fix abrasives on flexible substrates such as paper, cloth, film or composite substrates. They are also called flexible abrasive tools. They mainly include abrasive cloth (paper) or abrasive belts, which are widely used. Grinding, polishing and sanding of non-metallic materials such as metal materials, wood, ceramics, plastics, leather, rubber and paint putty. Coated abrasives are usually composed of three parts: abrasives, binders and substrates. The manufacturing process generally includes steps such as substrate treatment, primer coating, sand planting, recoating (coating), drying, and cutting. [0003] The prior art with the Chinese patent application publication number CN107344336A discloses a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information