A method for preparing high-purity praseodymium oxide and neodymium oxide by single fractionation of praseodymium and neodymium concentrates

A technology of enrichment and praseodymium oxide, applied in the direction of improving process efficiency, can solve the problems of difficulty in obtaining high-purity neodymium and high-purity praseodymium, low separation coefficient of praseodymium-neodymium, difficult control of praseodymium-neodymium, etc., and achieve the reduction of blank organic phase. , The product quality is stable and the unit consumption is small.

Active Publication Date: 2022-03-18
中稀(常州)稀土新材料有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the problem that the separation coefficient of praseodymium and neodymium is low at present, if the content of praseodymium and neodymium fluctuates, it is difficult to control and it is difficult to obtain high-purity neodymium and high-purity praseodymium. Then extract and separate high-purity praseodymium oxide and high-purity neodymium oxide from the enrichment of praseodymium and neodymium with stable content. By controlling the source of raw materials, the separation of praseodymium and neodymium is better controlled, and the purity of praseodymium and neodymium obtained is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Dissolve the light rare earth whose main components are lanthanum, cerium, praseodymium and neodymium in hydrochloric acid, remove the insoluble particles, the remaining solution mainly contains rare earth chloride solution, add sodium carbonate to the feed solution to pH 12, and form rare earth Precipitation, after solid-liquid separation, a large amount of non-rare earth impurities are discharged from the mother liquor, and the precipitate is mixed with hydrochloric acid to keep the pH at 3 to 4 to obtain a rare earth chloride solution, in which the rare earth concentration is La 15.0g / L and Ce 40.0g / L , Pr 10.0g / L, Nd 28.0g / L.

[0039] (2) With octanol, naphthenic acid, sulfonated kerosene mass ratio 1:1:2 mixture is organic phase, saponification, saponification value 0.52, feed liquid and organic phase after saponification are added in the first extraction tank, organic phase, The volume flow ratio of the enriched material liquid of lanthanum, cerium, praseodymi...

Embodiment 2

[0045] (1) Dissolving the light rare earth whose main components are lanthanum, cerium, praseodymium and neodymium in hydrochloric acid to remove insoluble particles, the remaining solution mainly contains rare earth ion chloride solution, and sodium carbonate is added to the feed solution to pH 12 to form rare earth Precipitation, after solid-liquid separation, a large amount of non-rare earth impurities are discharged from the mother liquor, the precipitate is mixed with hydrochloric acid, and the pH is kept at 3 to 4 to obtain a rare earth chloride solution, in which the rare earth concentration La 24.0g / L, Ce 27.0g / L , Pr 20.0g / L, Nd45.0g / L.

[0046] (2) With octanol, naphthenic acid, sulfonated kerosene mass ratio 0.8:1:1.8 mixture is organic phase, saponification value 0.52, feed liquid and organic phase are added in the first extraction tank, organic phase, lanthanum cerium praseodymium neodymium The volume flow ratio of the enriched material liquid is 3.8:1, the water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of rare earth separation, in particular to a method for preparing high-purity praseodymium oxide and neodymium oxide by single separation of praseodymium and neodymium concentrates. In the present invention, light rare earths such as lanthanum, cerium, praseodymium and neodymium are dissolved in hydrochloric acid, and after impurities are removed, the material liquid is mixed with the organic phase and added to the extraction tank, and the water phase is passed into the extraction tank in the opposite direction, and the extraction reaction is carried out to obtain Pr, Nd rare earth organic phase, obtain praseodymium and neodymium organic phase enrichment, add qualified praseodymium and neodymium products, adjust the content of praseodymium and neodymium, and stabilize the mass ratio of praseodymium; use the adjusted praseodymium and neodymium enrichment as raw material, mix and add with organic phase Single separation is carried out in the extraction tank, and high-purity praseodymium oxide and neodymium oxide are obtained after single separation. The method of the invention can ensure that the praseodymium and neodymium obtained by single fractionation have high purity and few impurities. Moreover, it is conducive to the production of large quantities of praseodymium and neodymium products, and the product quality is very stable.

Description

technical field [0001] The invention relates to the technical field of rare earth separation, in particular to a method for preparing high-purity praseodymium oxide and neodymium oxide by single separation of praseodymium and neodymium concentrates. Background technique [0002] Rare earth is the abbreviation of a group of metals, which includes lanthanum, cerium, praseodymium, neodymium, giant, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium of the lanthanide elements in the third subgroup of the periodic table of chemical elements , lutetium, and scandium and yttrium with similar properties. [0003] Rare earth is playing an increasingly important role in the technological progress and development of traditional industries. Its application in many fields can generate economic and social benefits dozens or even hundreds of times its own value. In recent years, the application fields of rare earths have become more and more extensive...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C22B3/26C22B3/10C22B59/00
CPCC22B3/10C22B59/00C22B3/26Y02P10/20
Inventor姚栋伟罗中武周健朱亚清贺国伟黄俊军施碧峰蒋宏徐敏蒋逸波刘惠芬蒋超超施建兴刘玉平陈春琴周红燕蒋网生陈永强孙鹏蒋雪薇周亚珠邓文俊牛卫芳张琳邰艳婷王阳任苏蕾邹建东杨迎
Owner中稀(常州)稀土新材料有限公司