A kind of anti-slip and anti-fouling anti-slip and anti-fouling ceramic tile with ceramic polishing anti-slip wax and preparation method thereof
A technology for ceramic polishing and ceramic tiles, which is used in grinding/polishing equipment, surface-polished machine tools, ceramic molding machines, etc., and can solve the problems of uneven glaze surface, easy to hide dirt, drop, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0051] The preparation method of the anti-slip and anti-fouling full-glazed porcelain tile with delicate surface comprises the following steps:
[0052] 1. The powder is pressed into shape and dried.
[0053] 2. Apply glaze. The specific gravity of the top glaze is 1.42, and the application amount is 650g / m 2 .
[0054] 3. Print the pattern with inkjet, and dry the green body after printing the inkjet pattern.
[0055] 4. Prepare the protective glaze according to the ratio, and then print the protective glaze. The chemical composition of the protective glaze is: SiO 2 : 51.1%, Al 2 o 3 : 12.5%, Fe 2 o 3 : 0.4%, TiO 2 : 0.2%, CaO: 9.8%, MgO: 3.9%, K 2 O: 2.2%, Na 2 O: 4.5%, BaO: 3.1%, ZnO: 3.6%, loss on ignition: 8.6%. The protective glaze is applied by screen printing, the specific gravity is 1.33, and the amount of glaze applied is 60g / m 2 .
[0056] 5. Apply glaze on the green body after applying protective glaze. The chemical composition of the glaze is: SiO ...
Embodiment 2
[0065] It is basically the same as Embodiment 1, the difference is:
[0066] In step 5, the chemical composition of the glaze is: SiO 2 : 53.4%, Al 2 o 3 : 11%, Fe 2 o 3 : 0.1%, TiO 2 : 0.2%, CaO: 7.6%, MgO: 2.6%, K 2 O: 4%, Na 2 O: 2.6%, BaO: 6.6%, ZnO: 5.9%, loss on ignition: 6%. Drenching glaze: the specific gravity is 1.88, and the amount of glaze application is 550g / m 2 .
[0067] In step 8, the raw material composition of the water-based antifouling wax is: 60% of nano silicon dioxide particles, 1% of antifreeze solvent, 0.5% of surfactant, 1.5% of alkaline corrosion agent, 0.5% of organic silane coupling agent, water 36.5%. The raw material composition of the oily antifouling wax is: nano silicon dioxide particles: 38%, antifreeze solvent 1%, surfactant 1%, organosilane coupling agent 1%, dimethyl silicone oil 17%, hydrogen silicone oil 42%. Grind 20 discs with water-based anti-fouling wax water, the application time is 28 seconds, and the application amount...
Embodiment 3
[0072] It is basically the same as Embodiment 1, the difference is:
[0073] In step 5, the chemical composition of the glaze is: SiO 2 : 57.0%, Al 2 o 3 : 11.8%, Fe 2 o 3 : 0.15%, TiO 2 : 0.2%, CaO: 5.6%, MgO: 3.2%, K 2 O: 3.1%, Na 2 O: 3.3%, BaO: 4%, ZnO: 4%, loss on ignition: 7.6%. Drenching glaze: the specific gravity is 1.85, and the amount of glaze application is 600g / m 2 .
[0074] In step 8, the raw material composition of the water-based antifouling wax is: 50% of nano silicon dioxide particles, 0.7% of antifreeze solvent, 2% of surfactant, 0.6% of alkaline corrosion agent, 0.7% of organic silane coupling agent, water 46%. The raw material composition of the oily antifouling wax is: nano silicon dioxide particles: 30%, antifreeze solvent 0.8%, surfactant 0.5%, organosilane coupling agent 0.7%, dimethyl silicone oil 15%, hydrogen silicone oil 53%. Apply 24 discs of water-based anti-fouling wax water, the application time is 35 seconds, and the application a...
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |